Vehicle-mounted air purifying sheet and preparation method thereof

A technology of purification sheet and air, which is applied in the field of air purification, can solve the problems of electrostatic adsorption force attenuation, low adsorption efficiency, and influence on electrostatic adsorption effect, and achieve the effect of enhancing adsorption capacity, strong inhibition ability, and overcoming poor adsorption effect

Active Publication Date: 2017-09-19
杭州创克洛环境科技有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are also some shortcomings. Since the above two filter materials are not used for air outlets, the requirements for wind resistance are not high, so their wind resistance is relatively high, and they are not suitable for air outlet filters.
On the other hand, during the preparation of electretized non-woven fabrics, the adsorption efficiency of non-woven fabrics after PTFE emulsion impregnation is low, making PTFE emulsions unable to be permanently and firmly adsorbed by non-woven fabrics, thus affecting the electrostatic adsorption effect. Especially after a long time, the electrostatic adsorption force decays seriously
In addition, the above-mentioned non-woven fabrics also lack antibacterial function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A vehicle-mounted air purification sheet, which is composed of an electrostatic adsorption layer and an antibacterial layer, and the electrostatic adsorption layer is an air inlet surface; wherein, the electrostatic adsorption layer is polypropylene non-woven fabric containing nano-electret; the antibacterial layer Polypropylene non-woven fabric compounded with peptide silver. The air resistance of the antibacterial layer is smaller than that of the electrostatic adsorption layer.

[0042] The polypropylene non-woven fabric containing nano electret is made from the following raw materials in mass percentage: 75% polypropylene, 1% hydrophobic cyclodextrin, 5% modified coral powder, 1.5% nano sepiolite, silane 0.5% coupling agent, 17% polytetrafluoroethylene.

[0043] The preparation method of the modified coral powder is as follows: the coral is washed and roughly ground to 80 mesh, then placed in a muffle furnace and heated to 350°C under anaerobic conditions, calcined...

Embodiment 2

[0053] A vehicle-mounted air purification sheet, which is composed of an electrostatic adsorption layer and an antibacterial layer, and the electrostatic adsorption layer is an air inlet surface; wherein, the electrostatic adsorption layer is polypropylene non-woven fabric containing nano-electret; the antibacterial layer It is a polypropylene non-woven fabric compounded with nano-titanium dioxide. The air resistance of the antibacterial layer is smaller than that of the electrostatic adsorption layer.

[0054] The polypropylene non-woven fabric containing nano electret is made from the following raw materials in mass percentage: 80% polypropylene, 1.5% hydrophobic cyclodextrin, 3% modified coral powder, 3% nano sepiolite, silane 1% coupling agent, 11.5% polytetrafluoroethylene.

[0055] The preparation method of the modified coral powder is as follows: the coral is washed and roughly ground to 60 mesh, then placed in a muffle furnace and heated to 300°C under anaerobic condi...

Embodiment 3

[0065] A vehicle-mounted air purification sheet, which is composed of an electrostatic adsorption layer and an antibacterial layer, and the electrostatic adsorption layer is an air inlet surface; wherein, the electrostatic adsorption layer is polypropylene non-woven fabric containing nano-electret; the antibacterial layer It is polypropylene non-woven fabric compounded with quaternary ammonium salt antibacterial agent. The air resistance of the antibacterial layer is smaller than that of the electrostatic adsorption layer.

[0066] The polypropylene non-woven fabric containing nano-electret is made from the following raw materials in mass percentage: 85% polypropylene, 1.5% hydrophobic cyclodextrin, 1% modified coral powder, 1% nano-meersiolite, silane 0.5% coupling agent, 11% polytetrafluoroethylene.

[0067] The preparation method of the modified coral powder is as follows: the coral is washed and roughly ground to 100 mesh, then placed in a muffle furnace and heated to 400...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wind resistanceaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of air purification, and discloses a vehicle-mounted air purifying sheet and a preparation method thereof. The vehicle-mounted air purifying sheet is prepared by compounding an electrostatic adsorption layer and an antibacterial layer, wherein the electrostatic adsorption layer is an air inlet face; the electrostatic adsorption layer is a polypropylene non-woven fabric containing a nanometer electret; the antibacterial layer is a polypropylene non-woven fabric compounded with antibacterial substances. The vehicle-mounted air purifying sheet has a large loading capacity and high fastness for an electrostatic adsorption agent, has a good electrostatic adsorption effect on particles such as PM2.5, pollen, dust, soot and dust mites, and has high air permeability and small wind resistance; moreover, the vehicle-mounted air purifying sheet has antibacterial and noise reduction functions.

Description

technical field [0001] The invention relates to the field of air purification, in particular to a vehicle-mounted air purification sheet and a preparation method thereof. Background technique [0002] In recent years, the urban environment has been seriously polluted, especially air pollution. According to the survey data of relevant departments, the main source of urban air PM2.5 pollution is vehicle exhaust pollution. Therefore, for drivers and passengers in vehicles running on the road, the threat of air pollution is more serious due to being on the road where the pollution sources are most concentrated. The fresh air system and air conditioning system of the vehicle will exchange the air inside the vehicle with the air outside the vehicle. Although these systems of the vehicle also have filtering devices, the filtering efficiency is not ideal. Therefore it is necessary to purify the air at the air outlet in the vehicle again. [0003] Generally, the requirements for t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D39/08B03C3/017B03C3/40
CPCB01D39/08B01D2239/0435B01D2239/0442B01D2239/0622B01D2239/0668B03C3/017B03C3/40Y02A50/2351
Inventor 徐江宁
Owner 杭州创克洛环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com