Online thermal composite quick infiltration guide material

A technology of thermal compounding and diversion layer, which is applied in the field of composite diversion materials and on-line thermal compound rapid permeation diversion materials, which can solve the problems of waste of raw materials, increase of raw material costs, and influence on product quality, so as to achieve a dry surface and not easy to separate Layer, good effect of anti-back seepage effect

Inactive Publication Date: 2017-09-29
FITESA CHINA AIRLAID
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the addition of polymer water-absorbing materials to the composite dust-free paper, in order to ensure the bonding strength between the bottom liner and its adjacent layers, it is necessary to add powdery or granular bonding materials at the same time, and it is necessary during the production process. Higher pressure, although it increases the bonding effect, will affect the bulkiness, rebound performance and diversion effect of the material, and also increase the cost of raw materials; another disadvantage is that the powdery bonding material increases the control complexity of the production process During the forming process, a small amount of powdery bonding material will penetrate through the backing material due to vacuum (when the vacuum degree fluctuates greatly, there will also be a phenomenon of powdery bonding material passing through), which will affect the pores of non-woven materials. which in turn affects the quality of the entire product
In addition, in the production and use of sanitary napkins, the size of the diversion composite dust-free paper needs to be the same as the surface area of ​​the sanitary napkin, and the core area of ​​the absorbent layer of the general sanitary napkin is smaller than the surface layer, so the composite dust-free paper is used Paper will result in the waste of some raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Online thermal composite quick infiltration guide material
  • Online thermal composite quick infiltration guide material
  • Online thermal composite quick infiltration guide material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0102] The total weight of the composite quick-seepage diversion material of the present embodiment is about 50g / m 2 , designed as a two-layer structure with a thickness of about 1.0mm. The specific raw materials and structure are as follows: the cellulose fiber is Weyerhauser NB416, and the fiber length is about 2-5mm. The bicomponent composite fiber is composed of a core layer and a skin layer, the core layer is polypropylene (PET), the skin layer is polyethylene (PE), the fiber length is about 3-10mm, and the fineness is about 1.5-3.0 decitex. The non-woven fabric adopts 20gsm hot-air non-woven fabric. In this embodiment, the emulsion is sprayed on the outer surface of the fiber layer, which is a Vinnapas 192 product from Wacker Company.

[0103] The composite quick-seepage diversion material structure includes two layers, wherein the weight of the quick-seepage diversion layer accounts for about 40.00% of the total weight of the product, the weight of the fiber layer accou...

Embodiment 2

[0113] The total weight of the composite rapid seepage diversion material of the present embodiment is about 85g / m 2 , designed as a three-layer structure with a thickness of about 1.75mm. The specific raw materials and structure are as follows: the cellulose fiber is Weyerhauser NB416, and the fiber length is about 2-5mm. The bicomponent composite fiber is composed of a core layer and a skin layer, the core layer is polypropylene (PET), the skin layer is polyethylene (PE), the fiber length is about 3-6mm, and the fineness is about 1.7-3.0 decitex. The non-woven fabric adopts 35gsm hot-air non-woven fabric. In this embodiment, latex is sprayed on the third layer, which is Vinnapas 192 product from Wacker Company.

[0114] The structure of the composite quick-seepage diversion material includes three layers, the weight of the quick-seepage diversion layer accounts for about 41.20% of the total weight of the product, the weight of the first fiber layer accounts for about 26.34% ...

Embodiment 3

[0126] The total weight of the composite rapid permeation diversion material of the present embodiment is about 140g / m 2 , designed as a four-layer structure with a thickness of about 3.10mm. The specific raw materials and structure are as follows: the cellulose fibers are Weyerhauser NB405 and NB416, and the fiber length is about 2-5mm. The bicomponent composite fiber is composed of a core layer and a skin layer, the core layer is polypropylene (PET), the skin layer is polyethylene (PE), the fiber length is about 3-6mm, and the fineness is about 1.7-3.0 decitex. The non-woven fabric adopts 55gsm hot-air non-woven fabric. In this embodiment, latex is sprayed on the outer surface of the third fiber layer, which is the Vinnapas 192 product from Wacker Company.

[0127] The structure of the composite quick-seepage diversion material includes four layers, the weight of the quick-seepage diversion layer accounts for about 39.29% of the total weight of the product, the weight of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides an online thermal composite quick infiltration guide material. The online thermal composite quick infiltration guide material comprises a quick infiltration guide layer and a dust-free paper layer which are communicated with each other by virtue of liquid; the quick infiltration guide layer is prepared from a porous nonwoven material and accounts for 8 to 85 percent of the total weight of the composite quick infiltration guide material; the dust-free paper layer comprises at least one fiber layer, the fiber layer is prepared from cellulose fibers and dual-component composite fibers, and the dust-free paper layer accounts for 15 to 92 percent of composite guide material dust-free paper; the cellulose fibers in the fiber layer account for 5 to 95 percent of the total weight of the fiber layer, and the dual-component composite fibers account for 5 to 95 percent of the total weight of the fiber layer; and when the layer number of the fiber layers is two or more, the two adjacent fiber layers are communicated with each other by virtue of liquid. A sanitary towel product prepared from the composite quick infiltration guide material is loose, soft, good in resilience, low in production cost, good in overall performance, simple and novel in structure, not only capable of quickly guiding, infiltrating, dispersing and temporarily storing the liquid, but also excellent in back-permeability resistance.

Description

technical field [0001] The invention relates to a fluffy and soft, good resilience, low production cost, good overall performance, simple and novel on-line thermal compound rapid permeation diversion material, which has the functions of rapid liquid diversion, rapid permeation, diffusion and temporary storage of liquid, and has A composite diversion material with excellent back seepage resistance performance, including the structure, production process and application of the composite rapid seepage diversion material. Background technique [0002] Dust-free paper (also known as puffed core material) is produced from wood pulp fibers with a length of several millimeters as the main raw material through air-laid and different consolidation methods. This technology can produce a variety of materials with different thicknesses, softness, and hygroscopicity. Its products are mainly used in disposable sanitary products such as diapers, feminine hygiene products, and adult incontin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/04B32B9/02B32B3/24B32B27/12B32B27/36B32B27/30B32B27/32B32B37/10B32B37/12B32B38/16B32B38/06
CPCB32B3/266B32B5/02B32B9/047B32B27/12B32B37/1009B32B37/12B32B38/06B32B38/164B32B2307/726B32B2262/06B32B2262/0276B32B2262/0253B32B2262/0223B32B2255/02B32B2255/26B32B2555/02B32B2553/00D04H1/732B32B3/26B32B2262/062B32B7/12B32B2262/14B32B3/06B32B2307/72B32B2262/067B32B3/08B32B2307/54B32B2262/12B32B2262/023B32B7/04B32B5/26B32B3/30B32B2307/718B32B2262/0284B32B5/022B32B2250/20B32B7/022B32B2262/0261B32B2307/732B32B2255/28A61F13/537A61F13/15658B32B5/12B32B5/08B32B7/05B32B2250/02B32B2307/728D04H1/425D04H1/4291D04H1/435D04H1/5412A61F13/472A61F13/49D04H1/559D06N3/0011D06N3/0013D06N3/0036D06N3/0038D06N2201/042D06N2209/126D06N2211/24B32B37/06B32B2310/0454B32B2323/10B32B2323/04B32B2367/00B32B2037/243B32B2319/00B32B2309/10
Inventor 任继春王娟冯勋旺屈义俭马克·纽曼
Owner FITESA CHINA AIRLAID
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products