Antirust paint used for electrical equipment

A technology for power equipment and anti-rust paint, applied in the field of anti-rust paint, can solve problems such as power equipment damage, danger, and influence on the operation of power equipment in the casing, and achieve the effect of enhancing rust resistance and oxygen resistance

Inactive Publication Date: 2017-10-20
安徽新智电力科技有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When the metal casing of the power equipment is affected by chemical corrosion such as water, acid, salt and other environmental conditions, the metal casing of the power equipment will corrode and produce rust stains, which will seriously affect the operation of the power equipment in the casing, not only causing damage to the power equipment damage, waste of power resources, and may also cause danger

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antirust paint used for electrical equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An antirust paint for electric equipment, made of the following components by weight: 20 parts of modified alkyd resin, 8 parts of polyurethane modified acrylic emulsion, 10 parts of polyether modified siloxane, petroleum sulfonate 5 parts, xylene 4 parts, oily wax 7 parts, polyphosphate 8 parts, chlorinated polyvinyl chloride 2 parts, C5 hydrogenated petroleum resin 5 parts, silicon dioxide 1 part, rust inhibitor 4 parts.

[0021] The antirust agent is made of the following components by weight: 5 parts of dicyclohexylamine, 3 parts of soda ash, 2 parts of ceramic micropowder, 1 part of nano-zinc oxide, 2 parts of nano-calcium carbonate, 3 parts of ascorbyl palmitate .

[0022] The preparation method of the above-mentioned antirust paint for electric equipment is as follows:

[0023] a. Mix the modified alkyd resin, polyether modified siloxane, and petroleum sulfonate, heat to a molten state, and carry out stirring reaction, and the stirring time is 20 minutes;

[00...

Embodiment 2

[0029] An antirust paint for electric equipment, made of the following components by weight: 30 parts of modified alkyd resin, 15 parts of polyurethane modified acrylic emulsion, 15 parts of polyether modified siloxane, petroleum sulfonate 10 parts, xylene 8 parts, oily wax 15 parts, polyphosphate 12 parts, chlorinated polyvinyl chloride 4 parts, C5 hydrogenated petroleum resin 10 parts, silicon dioxide 3 parts, rust inhibitor 6 parts.

[0030] The antirust agent is made of the following components by weight: 10 parts of dicyclohexylamine, 6 parts of soda ash, 4 parts of ceramic micropowder, 2 parts of nano-zinc oxide, 3 parts of nano-calcium carbonate, 5 parts of ascorbyl palmitate .

[0031] The preparation method of the above-mentioned antirust paint for electric equipment is as follows:

[0032] a. Mix the modified alkyd resin, polyether modified siloxane, and petroleum sulfonate, heat to a molten state, and carry out stirring reaction, and the stirring time is 30 minutes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antirust paint used for electrical equipment. The antirust paint used for electrical equipment is prepared from, by weight, 20 to 30 parts of modified alkyd resin, 8 to 15 parts of polyurethane modified acrylic emulsion, 10 to 15 parts of polyether modified siloxane, 5 to 10 parts of a petroleum sulfonate, 4 to 8 parts of xylene, 7 to 15 parts of an oily wax, 8 to 12 parts of a polyphosphate, 2 to 4 parts of chlorinated polyvinyl chloride, 5 to 10 parts of C5 hydrogenated petroleum resin, 1 to 3 parts of silicon dioxide, and 4 to 6 parts of an antirust agent. The beneficial effects are that: modified alkyd resin, polyurethane modified acrylic emulsion, and polyether modified siloxane are taken as main raw materials, xylene, the oily wax, the polyphosphate, C5 hydrogenated petroleum resin, silicon dioxide, and the antirust agent are added as modifying agents, so that oxidation resistance, stability, and antirust properties are improved.

Description

technical field [0001] The invention relates to the technical field of chemical coatings, in particular to an antirust paint used for electric equipment. Background technique [0002] Power equipment mainly includes two categories: power generation equipment and power supply equipment. Power generation equipment is mainly power plant boilers, steam turbines, gas turbines, water turbines, generators, transformers, etc. Power supply equipment is mainly transmission lines of various voltage levels, transformers, contactors and more. [0003] When the metal shell of the power equipment is affected by chemical corrosion such as water, acid, salt and other environmental conditions, the metal shell of the power equipment will corrode and produce rust stains, which will seriously affect the operation of the power equipment in the shell, not only causing damage to the power equipment The damage and waste of power resources may also cause danger. Contents of the invention [0004]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D175/14C09D183/12C09D5/08C09D7/12
CPCC08K2003/2296C08K2003/265C08K2003/321C08K2201/011C08L2201/08C08L2203/20C08L2205/035C09D5/08C09D167/08C08L75/14C08L83/12C08L91/06C08L27/24C08L57/02C08K13/02C08K3/32C08K3/36C08K3/26C08K3/22
Inventor 王凯
Owner 安徽新智电力科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap