Ground brick and preparation method thereof

A technology of floor tiles and raw materials, applied in clay products, other household appliances, applications, etc., to achieve the effect of reducing the degree of urban heat island effect, high activity and good fire resistance

Inactive Publication Date: 2017-10-27
合肥永泰新型建材有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In order to solve the deficiencies of the existing floor tiles in flame retardancy, utilization of industrial waste and treatment of automobile exhaust, the purpose of the present invention is to provide a floor tile and a preparation method thereof. The advantages of high strength, good flame retardancy, full utilization of industrial waste and effective treatment of automobile exhaust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A floor tile comprising the following raw materials in parts by weight: 60 parts of clay, 32 parts of shale, 18 parts of fly ash, 29 parts of rice straw, 15 parts of emulsified asphalt, and 19 parts of quartz glass fiber , 12 parts of steel slag, 12 parts of bauxite, 10 parts of nano silicon dioxide, 5 parts of nano titanium dioxide, 9 parts of attapulgite and 18 parts of water.

[0045] Bauxite is added to the raw materials. Bauxite has good fire resistance and can improve the fire resistance of floor tiles.

[0046] Nano silicon dioxide is added to the raw material, because it has conventional SiO 2The special optical properties that it does not have, it has extremely strong ultraviolet absorption and heat radiation absorption characteristics, and its absorption rate of ultraviolet light within a wavelength of 400nm is as high as 70%, so adding it to the aggregate of floor tiles can achieve anti-ultraviolet The purpose of radiation and thermal aging can reduce the de...

Embodiment 2

[0064] A ground tile, comprising the following raw materials in parts by weight: 50 parts of clay, 21 parts of shale, 12 parts of fly ash, 23 parts of rice straw, 12 parts of emulsified asphalt, 16 parts of quartz glass fiber, 9 parts of steel slag, aluminum alum 8 parts of soil, 7 parts of nano silicon dioxide, 3 parts of nano titanium dioxide, 6 parts of attapulgite and 15 parts of water.

[0065] Bauxite is added to the raw materials. Bauxite has good fire resistance and can improve the fire resistance of floor tiles.

[0066] Nano silicon dioxide is added to the raw material, because it has conventional SiO 2 The special optical properties that it does not have, it has extremely strong ultraviolet absorption and heat radiation absorption characteristics, and its absorption rate of ultraviolet light within a wavelength of 400nm is as high as 70%, so adding it to the aggregate of floor tiles can achieve anti-ultraviolet The purpose of radiation and thermal aging can reduce ...

Embodiment 3

[0084] A ground tile, comprising the following raw materials in parts by weight: 70 parts of clay, 43 parts of shale, 24 parts of fly ash, 35 parts of rice straw, 18 parts of emulsified asphalt, 22 parts of quartz glass fiber, 15 parts of steel slag, aluminum alum 16 parts of soil, 13 parts of nano silicon dioxide, 7 parts of nano titanium dioxide, 12 parts of attapulgite and 21 parts of water.

[0085] Bauxite is added to the raw materials. Bauxite has good fire resistance and can improve the fire resistance of floor tiles.

[0086] Nano silicon dioxide is added to the raw material, because it has conventional SiO 2 The special optical properties that it does not have, it has extremely strong ultraviolet absorption and heat radiation absorption characteristics, and its absorption rate of ultraviolet light within a wavelength of 400nm is as high as 70%, so adding it to the aggregate of floor tiles can achieve anti-ultraviolet The purpose of radiation and thermal aging can red...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides a ground brick and a preparation method thereof, and relates to the technical field of bricks. The ground brick is prepared from the following raw materials in parts by weight: 50-70 parts of clay, 21-43 parts of shale, 12-24 parts of coal ash, 23-35 parts of rice straws, 12-18 parts of emulsified asphalt, 16-22 parts of quartz glass fibers, 9-15 parts of steel slag, 8-16 parts of bauxite, 7-13 parts of nano silicon dioxide, 3-7 parts of nano titanium dioxide, 6-12 parts of attapulgite and 15-21 parts of water. A preparation method for the ground brick comprises the following steps: (1) weighing raw materials; (2) adding the raw materials into a pulverizer; (3) mixing the raw materials; (4) forming the raw materials; (5) drying the raw materials; and (6) firing the raw materials. The ground brick solves the problems that an existing ground brick has defects in aspect of flame resistance, industrial waste utilization and vehicle tail gas treatment.

Description

technical field [0001] The invention belongs to the technical field of bricks, and in particular relates to a ground brick and a preparation method thereof. Background technique [0002] As a common and widely used building material, floor tiles have a large demand and consume a huge amount of material resources. Today, as non-renewable resources are increasingly depleted, energy conservation and environmental protection have become the theme of the times, and finding other alternative material resources has become a problems that urgently need to be resolved. [0003] Industrial waste materials are an important part of urban waste. At present, industrial waste is mainly treated by traditional open-air stacking and deep excavation. Although this method has a large amount of processing, is convenient and simple, and has low processing costs, it actually occupies a large amount of land. resources, resulting in irreversible environmental pollution. [0004] Automobile exhaust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/36C04B33/13C04B33/135C04B33/138C04B33/32
CPCC04B33/13C04B33/1305C04B33/1352C04B33/138C04B33/32C04B33/36C04B2235/3217C04B2235/3232C04B2235/3418C04B2235/3427C04B2235/422C04B2235/661C04B2235/96Y02P40/60
Inventor 伍志远
Owner 合肥永泰新型建材有限公司