Deodorization toilet lid and production method thereof

A deodorant toilet and urea-formaldehyde resin technology, applied in the field of deodorant toilet cover and its production, can solve the problems of accelerated toilet air circulation, poor air circulation, toilet full of odor, etc., to improve the degree of adhesion, reduce brittleness, The effect of increasing the melting and boiling point

Inactive Publication Date: 2017-11-07
ZHEJIANG HENGYUAN SANITARY WARE
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, after this toilet lid is frequently used in the toilet, the air circulation in the toilet is poor, causing the toilet to be full of foul smell
It is cumbersome and inconvenient to artificially add air fresheners and accelerate the air circulation in the toilet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036]A deodorant toilet cover, comprising the following components in parts by weight: 42 parts of urea-formaldehyde resin; 7 parts of ammonium chloride powder; 1.4 parts of aminopropyltriethoxysilane; 3.3 parts of anhydrous calcium chloride; 2.4 parts of ethyl ester; 1 part of white carbon black; 2.5 parts of white carbon; 2.7 parts of polyvinyl alcohol.

[0037] A method for making a deodorizing toilet cover, comprising the following steps:

[0038] (1) Prepare 42 parts of urea-formaldehyde resin in parts by weight, and grind the urea-formaldehyde resin into particles. And at 42 degrees Celsius, 2.7 parts of polyvinyl alcohol were added for modification; 7 parts of ammonium chloride powder, 1.4 parts of aminopropyltriethoxysilane, 1 part of white carbon black, and 3.3 parts of anhydrous calcium chloride were configured in parts by weight. 2.4 parts, 2.4 parts of diethyl oxalate and 2.5 parts of white carbon, after grinding into powder, add to polyvinyl alcohol modified ure...

Embodiment 2

[0042] A deodorant toilet cover, comprising the following components in parts by weight: 48 parts of urea-formaldehyde resin; 9.2 parts of ammonium chloride powder; 1.8 parts of aminopropyltriethoxysilane; 3.6 parts of anhydrous calcium chloride; 2.5 parts of ethyl ester; 1.4 parts of white carbon black; 3.2 parts of white carbon; 3 parts of polyvinyl alcohol.

[0043] A method for making a deodorizing toilet cover, comprising the following steps:

[0044] (1) Prepare 48 parts of urea-formaldehyde resin in parts by weight, and grind the urea-formaldehyde resin into granules. And add 3 parts of polyvinyl alcohol at 45 degrees Celsius for modification; configure 8.2 parts of ammonium chloride powder, 1.5 parts of aminopropyltriethoxysilane, 1.4 parts of white carbon black, and 3.6 parts of anhydrous calcium chloride by weight. 2.5 parts, 2.5 parts of diethyl oxalate and 3.2 parts of white carbon, after grinding into powder, add to polyvinyl alcohol modified urea-formaldehyde re...

Embodiment 3

[0048] A deodorant toilet cover, comprising the following components in parts by weight: 51 parts of urea-formaldehyde resin; 8.2 parts of ammonium chloride powder; 1.5 parts of aminopropyltriethoxysilane; 3.9 parts of anhydrous calcium chloride; 2.8 parts of ethyl ester; 1.7 parts of white carbon black; 3.6 parts of white carbon; 3.2 parts of polyvinyl alcohol.

[0049] A method for making a deodorizing toilet cover, comprising the following steps:

[0050] (1) Prepare 51 parts of urea-formaldehyde resin in parts by weight, and grind the urea-formaldehyde resin into particles. And add 3 parts of polyvinyl alcohol to modify at 48 degrees Celsius; configure 8.2 parts of ammonium chloride powder, 1.5 parts of aminopropyltriethoxysilane, 1.4 parts of white carbon black, and 3.6 parts of anhydrous calcium chloride by weight. 2.8 parts, 2.8 parts of diethyl oxalate and 3.2 parts of white carbon, after being ground into powder, add to polyvinyl alcohol modified urea-formaldehyde re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a deodorization toilet lid and a production method thereof. The deodorization toilet lid is characterized by containing the following components in parts by weight: 40-60 parts of urea resin, 6-14 parts of a curing agent, 1.2-3.5 parts of a coupling agent, 3-4.3 parts of a water absorbent, 2-3.6 parts of an accelerant, 1-2.3 parts of a reinforcing agent and 2.4-4.4 parts of white charcoal. The deodorization toilet lid has the beneficial effects that the automatic deodorization can be realized, and the air quality in a toilet is improved.

Description

technical field [0001] The invention relates to a toilet cover and a manufacturing method thereof, in particular to a deodorizing toilet cover and a manufacturing method thereof. Background technique [0002] As a common sanitary ware in daily life, the toilet seat is mainly used in the toilet type flush toilet. Generally, after people frequently use the toilet, the odor in the toilet is more difficult to get rid of, thus making the whole toilet full of odor. [0003] The Chinese patent with the publication number CN102627865A discloses a manufacturing method of a wood-plastic environmental protection toilet cover, which comprises the following raw materials mixed in parts by weight: 30-55 parts of polypropylene powder, 1-3 parts of coupling agent, lubricant 1~5 copies etc. By adding the above materials in a granulator, granulate to make wood-plastic granules, and then injection molded by an injection molding machine. This wood-plastic environmentally friendly toilet cove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/24C08L29/04C08K13/04C08K5/544C08K5/098C08K3/16C08K3/36C08K7/24C08K3/28C08J9/30
CPCC08J9/30C08J2361/24C08J2429/04C08L61/24C08L2201/08C08L2312/00C08L29/04C08K13/04C08K5/544C08K5/098C08K3/16C08K3/36C08K7/24C08K3/28
Inventor 许肖峰
Owner ZHEJIANG HENGYUAN SANITARY WARE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com