Antistatic and wear-resistant rubber material for rubber covered roller

A rubber material and wear-resistant technology, which is used in the field of rubber materials for anti-static and wear-resistant rubber rollers, can solve the problems of poor mechanical properties, anti-static and wear resistance, wear or cracks, and poor rebound. Achieve the effect of shortening vulcanization time, improving surface properties and increasing hardness

Inactive Publication Date: 2017-11-10
薛念念
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Under the high-speed working environment, the mechanical properties of commercially available rubber rollers, especially the antistatic and wear-resistant performances, are not good. Performance degradation Adsorption to paper products or fabrics causing failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic and wear-resistant rubber material for rubber covered roller

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of wear-resistant antistatic rubber roller rubber material, its raw material comprises by weight:

[0027] 50 parts of carboxylated nitrile rubber, 50 parts of EPDM rubber, 25 parts of naphthenic oil, 15 parts of reinforcing agent, 6 parts of modified nano-zinc oxide, 6 parts of plasticizer, 3 parts of vulcanizing agent, and 1 part of accelerator , 5 parts of additives;

[0028] Wherein, in the EPDM rubber, the weight percent content of the propylene unit is 40%, the weight percent content of the ethylene unit is 54%, and the weight percent content of the ethylidene norbornene unit is 6%.

Embodiment 2

[0030] A kind of wear-resistant antistatic rubber roller rubber material, its raw material comprises by weight:

[0031] 70 parts of carboxylated nitrile rubber, 30 parts of EPDM rubber, 5 parts of naphthenic oil, 30 parts of reinforcing agent, 3 parts of modified nano zinc oxide, 10 parts of plasticizer, 2 parts of vulcanizing agent, 3 parts of accelerator , 1 part of auxiliary agent;

[0032] Wherein, in the EPDM rubber, the weight percentage of the propylene unit is 50%, the weight percentage of the ethylene unit is 46%, and the weight percentage of the ethylidene norbornene unit is 4%.

Embodiment 3

[0034] A kind of wear-resistant antistatic rubber roller rubber material, its raw material comprises by weight:

[0035] 60 parts of carboxylated nitrile rubber, 40 parts of EPDM rubber, 13 parts of naphthenic oil, 20 parts of reinforcing agent, 5 parts of modified nano zinc oxide, 8 parts of plasticizer, 2.5 parts of vulcanizing agent, 2 parts of accelerator , 4 parts of additives;

[0036] Wherein, the weight percentage of propylene unit in EPDM rubber is 50%, the weight percentage of ethylene unit is 45%, and the weight percentage of ethylidene norbornene unit is 5%; EPDM rubber The Mooney viscosity (ML100℃1+4) is 75;

[0037] The preparation process of the modified nano-zinc oxide includes: adding sucrose ester to 0.5mol / L zinc nitrate solution to obtain a mixed solution, the amount of sucrose ester added is 0.25g / L; adding the obtained mixed solution dropwise to a concentration of 1.0 In mol / L sodium hydroxide solution, pretreatment for 1.5h, ultrasonic reaction for 10m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a rubber material for wear-resistant and antistatic rubber rollers. The raw materials include, by weight, 50-70 parts of carboxylated nitrile rubber, 30-50 parts of EPDM rubber, and 5-25 parts of naphthenic oil , 15-30 parts of reinforcing agent, 3-6 parts of modified nano-zinc oxide, 6-10 parts of plasticizer, 2-3 parts of vulcanizing agent, 1-3 parts of accelerator, 1-5 parts of auxiliary agent; wherein, The weight percent content of propylene units in the EPDM rubber is 40-50%, the weight percentage content of ethylene units is 45-55%, and the weight percentage content of ethylidene norbornene units is 4-6%. The invention adopts the blending of EPDM rubber obtained by polymerization of ethylene, propylene and ethylidene norbornene with a specific ratio and carboxylated nitrile rubber, which reduces the hardness of EPDM rubber and improves the tensile strength and wear resistance Performance, adding modified nano zinc oxide, improves the wear resistance and antistatic performance of the rubber roller, and at the same time improves the rubber vulcanization activity, shortens the vulcanization time and reduces the production cost.

Description

technical field [0001] The invention relates to the technical field of twist stick rubber materials, in particular to a rubber material for antistatic and wear-resistant rubber rollers. Background technique [0002] Rubber rollers are a main variety of rubber products, widely used in metallurgy, papermaking, fiber textiles, printing and dyeing, wood processing, plastic film processing, office equipment manufacturing and other industries, and are important industrial accessories. Rubber rollers are closely related to industrial continuity and labor saving. Therefore, with the acceleration of industrial modernization, the important role of rubber rollers is becoming increasingly apparent. [0003] With the development of science and technology, people have higher and higher requirements for equipment, and put forward higher requirements for the speed and service life of rubber rollers. Under the high-speed working environment, the mechanical properties of commercially availab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L13/00C08L23/16C08L91/00C08L23/06C08L83/04C08K13/06C08K9/04C08K3/22C08K3/36C08K5/12C08K3/04C08K5/09C08K5/098
CPCC08L13/00C08K2003/2296C08K2201/011C08L23/16C08L2201/04C08L2201/08C08L2205/035C08L91/00C08L23/06C08L83/04C08K13/06C08K9/04C08K3/22C08K3/36C08K5/12C08K3/04C08K5/09C08K5/098
Inventor 薛念念
Owner 薛念念
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com