Moisture-absorption and sweat-discharge fiber spunlaced nonwoven fabric and preparation method thereof

A technology of moisture-absorbing and sweat-wicking fibers and non-woven fabrics, which is applied in non-woven fabrics, textiles, and papermaking, and can solve the problems of poor netting effect of pure polyester fibers, high quality resistance of polyester fibers, and low wet breaking strength. Achieve strong inhibition and disinfection effects, good hygroscopicity, and good moisture permeability

Inactive Publication Date: 2017-12-01
ZHONGYUAN ENGINEERING COLLEGE
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wet breaking strength is small, and the shrinkage deformation of the fabric made of pure viscose fiber is large
The strength of viscose fiber is lower than that of cotton fiber, it is not washable, its elongation at break is higher than that of cotton fiber, it has poor wear resistance, it is easy to deform under small load, it has poor dimensional stability, low stiffness and poor elasticity
[0013] Polyester fiber has the advantages of high strength, good recovery, and good heat setting, but the mass specific resistance of polyester fiber is large, and the electrostatic phenomenon is prominent, which makes it difficult to form a net in the process of carding pure polyester fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Using the above technological process, equipment and technical measures, etc., the white bamboo charcoal fiber spunlace nonwoven face towel base fabric has been developed, wherein it is made of the raw materials with the following weight ratio: the weight content of Coolmax moisture-absorbing and sweat-wicking fiber accounts for 10%, the weight content of pearl fiber accounts for 15%, the weight content of mint fiber accounts for 15%, the weight content of antibacterial viscose fiber accounts for 20%, the weight content of viscose fiber accounts for 10%, and the weight content of antibacterial polyester fiber accounts for 5% %, the weight content of polyester fiber accounts for 25%, and the performance index of spunlace nonwoven face towel base fabric is: the actual weight is 40.2g / m 2 , average thickness 0.29mm; longitudinal strength 36.7N, transverse strength 41.8N, longitudinal and transverse strength ratio 0.88:1; longitudinal elongation at break 25.40%, transverse e...

Embodiment 2

[0056] Using the above technological process, equipment and technical measures, etc., the white bamboo charcoal fiber spunlace nonwoven face towel base fabric has been developed, wherein it is made of the raw materials with the following weight ratio: the weight content of Coolmax moisture-absorbing and sweat-wicking fiber accounts for 20%, the weight content of pearl fiber accounts for 10%, the weight content of mint fiber accounts for 10%, the weight content of antibacterial viscose fiber accounts for 30%, the weight content of viscose fiber accounts for 10%, and the weight content of polyester fiber accounts for 20% , the performance index of the spunlace nonwoven face towel base fabric is: the actual weight is 45g / m 2 , average thickness 0.30mm; longitudinal strength 46.6N, transverse strength 49.3N, longitudinal and transverse strength ratio 0.95:1; longitudinal elongation at break 27.3%, transverse elongation at break 37.2%, longitudinal and transverse elongation at break...

Embodiment 3

[0059]Using the above technological process, equipment and technical measures, etc., the white bamboo charcoal fiber spunlace nonwoven face towel base fabric has been developed, wherein it is made of the following raw materials in the weight ratio: the weight content of Coolplus moisture-absorbing and sweat-wicking fiber accounts for 10%, the weight content of pearl fiber accounts for 10%, the weight content of antibacterial viscose fiber accounts for 10%, the weight content of viscose fiber accounts for 50%, the weight content of antibacterial polyester fiber accounts for 10%, and the weight content of polyester fiber accounts for 10% %, the performance index of the spunlace nonwoven face towel base fabric is: actual weight 50.8g / m 2 , average thickness 0.37mm; longitudinal strength 43.7N, transverse strength 49.3N, longitudinal and transverse strength ratio 0.89:1; longitudinal elongation at break 25.3%, transverse elongation at break 37.8%, longitudinal and transverse elonga...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tear loadaaaaaaaaaa
tear loadaaaaaaaaaa
Login to View More

Abstract

The invention relates to an antibacterial health-care spunlaced faric, in particular to a preparation method and application of a moisture-absorption and sweat-discharge fiber spunlaced nonwoven fabric. The moisture-absorption and sweat-discharge fiber spunlaced nonwoven fabric is prepared from, by weight, 10-70% of moisture-absorption and sweat-discharge fiber (including Coolmax, Coolplus, Cooldry and Topocool), 0-50% of pearl fiber, 0-50% of mint fiber, 0-60% of antibacterial viscose fiber (or viscose fiber) and 0-60% of antibacterial polyester fiber or polyester fiber. The moisture-absorption and sweat-discharge fiber spunlaced nonwoven fabric has the advantages that the developed moisture-absorption and sweat-discharge fiber spunlaced nonwoven face towel base fabric has the effects of disinfection, cleaning, maintenance, moisturizing nourishing and the like and also has the effects of corrosion prevention, inflammation diminishing, hygiene, health care and the like.

Description

technical field [0001] The present invention relates to a health-care spunlace cloth for medical textiles, in particular to a spunlace fabric using moisture-absorbing and sweat-wicking fibers (including Coolmax, Coolplus, Cooldry, Topocool), pearl fibers, mint fibers, antibacterial viscose fibers (or viscose Polyester fiber), antibacterial polyester fiber (or polyester fiber) and the moisture-absorbing and sweat-wicking fiber spunlace non-woven face towel base cloth processed by mixing and its preparation method and application. Background technique [0002] The spunlace method uses multiple fine water jets generated by high pressure to spray the fiber web. After the water jet passes through the fiber net, it is entrusted with the rebound of the net curtain and penetrates the fiber net again. Therefore, the fibers in the fiber net are displaced, interspersed, entangled and entangled under the hydraulic action of high-speed water jets interspersed in different directions, thu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/492
CPCD04H1/4382D04H1/492
Inventor 赵博
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com