Preparation method of weatherproof preservative plywood

A plywood, weather resistance technology, applied in the direction of manufacturing tools, wood treatment, pressure impregnation, etc., can solve the problems that affect the service life of anti-corrosion plywood, poor anti-microbial attack performance, easy to rot, insects, mildew, etc., to achieve anti-corrosion effect Effective and long-lasting, significant economic benefits, and avoid over-aging effects

Inactive Publication Date: 2017-12-08
含山县茂盛胶合板厂
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Plywood is an important type of wood-based panels. Due to the characteristics of small deformation, large format, inconvenient construction, not easy to warp, and high tensile strength of transverse grains, plywood is widely used in furniture, carriages, shipbuilding, military industry, packaging and other industrial sectors. It has been widely used. my country's timber industry is in the process of transition from natural forest timber to plantation forest timber. Plantation forest fast-growing small timber will be the main timber raw material in the future, but plantation forest fast-growing timber is prone to decay and insects. , mildew, so wood protection will play a role in prolonging the life of wood, reducing the waste of wood due to decay and insects, and can also improve the quality of wood products and increase the functions of wood products in related industries. Plywood can solve the problem of wood resources. Insufficient problem, but the corrosion resistance of existing plywood is poor, therefore, how to carry out anticorrosion treatment to plywood scientifically and environmentally friendly is a technical problem that needs to be solved now
[0003] With the infiltration of technical research, the treated plywood can basically meet the anti-corrosion requirements, but the anti-microbial attack performance is poor, and the preservative used to treat the plywood is easy to lose during use, which affects the service life of the anti-corrosion plywood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A method for preparing weather-resistant anti-corrosion plywood, comprising rotary cutting of wood segments, veneer drying, veneer cutting, veneer anti-corrosion treatment, anti-corrosion veneer drying, anti-corrosion veneer gluing, billet formation, cold pressing, curing, and hot pressing , trimming and sanding, the veneer anti-corrosion treatment method is vacuum dipping in an anti-corrosion solution, the anti-corrosion solution contains the following raw materials in parts by weight: 10 parts of ultrafine iron powder, 4 parts of aluminum octadecanoate, hydrogenated castor 3 parts of sesame oil, 1 part of hard water softener, 2.4 parts of ammonium polyphosphate, 0.6 parts of sodium selenate;

[0020] The conditions of the vacuum impregnation are as follows: keep at a negative pressure of 0.14MPa for 1.5 hours, then return to normal pressure and keep for 30 minutes, and then pressurize to 1MPa and keep for 1 hour;

[0021] The method for drying the anti-corrosion venee...

Embodiment 2

[0028] A method for preparing weather-resistant anti-corrosion plywood, comprising rotary cutting of wood segments, veneer drying, veneer cutting, veneer anti-corrosion treatment, anti-corrosion veneer drying, anti-corrosion veneer gluing, billet formation, cold pressing, curing, and hot pressing , trimming and sanding, the veneer anti-corrosion treatment method is vacuum dipping in an anti-corrosion solution, and the anti-corrosion solution contains the following raw materials in parts by weight: 7 parts of ultrafine iron powder, 5 parts of aluminum octadecanoate, hydrogenated castor 2 parts of sesame oil, 1.2 parts of hard water softener, 2.2 parts of ammonium polyphosphate, 0.8 parts of sodium selenate;

[0029] The conditions of the vacuum impregnation are as follows: keep under the condition of negative pressure 0.12MPa for 2 hours, then return to normal pressure and keep for 30 minutes, and then pressurize to 0.8MPa, keep for 0.5 hours;

[0030] The method for drying the...

Embodiment 3

[0037]A method for preparing weather-resistant anti-corrosion plywood, comprising rotary cutting of wood segments, veneer drying, veneer cutting, veneer anti-corrosion treatment, anti-corrosion veneer drying, anti-corrosion veneer gluing, billet formation, cold pressing, curing, and hot pressing , trimming and sanding, the veneer anti-corrosion treatment method is vacuum dipping in an anti-corrosion solution, and the anti-corrosion solution contains the following raw materials in parts by weight: 12 parts of ultrafine iron powder, 3 parts of aluminum octadecanoate, hydrogenated castor 4 parts of sesame oil, 0.8 parts of hard water softener, 2.6 parts of ammonium polyphosphate, 0.4 parts of sodium selenate;

[0038] The conditions of the vacuum impregnation are: keep it under the condition of negative pressure 0.15MPa for 0.5 hours, then return to normal pressure and keep it for 30 minutes, and then pressurize to 1.2MPa, keep it for 2 hours;

[0039] The method for drying the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of processing anti-corrosion plywood, and in particular relates to a preparation method of weather-resistant anti-corrosion plywood, including a veneer anti-corrosion treatment method of vacuum immersion in anti-corrosion liquid, a method of drying anti-corrosion veneer by electromagnetic wave drying and an adhesive preparation. Compared with the prior art, the present invention has the following advantages: the antiseptic liquid in the present invention is friendly to the environment and has good resistance to various microorganisms. Through the cooperation of vacuum conditions, the antiseptic liquid has good permeability in the veneer and can Uniform, and then use electromagnetic wave sealing treatment, which can make the ingredients in the antiseptic solution better combined in the veneer, which can effectively reduce the loss of active ingredients and improve the durability of the antiseptic effect; the adhesive can avoid the problem of excessive aging and avoid After hot pressing, the glue is opened, so that the obtained plywood has a stable structure, good weather resistance, effective and long-lasting anti-corrosion effect, and remarkable economic benefits.

Description

technical field [0001] The invention belongs to the technical field of processing anti-corrosion plywood, and in particular relates to a preparation method of weather-resistant anti-corrosion plywood. Background technique [0002] Plywood is an important type of wood-based panels. Due to the characteristics of small deformation, large format, inconvenient construction, not easy to warp, and high tensile strength of transverse grains, plywood is widely used in furniture, carriages, shipbuilding, military industry, packaging and other industrial sectors. It has been widely used. my country's timber industry is in the process of transition from natural forest timber to plantation forest timber. Plantation forest fast-growing small timber will be the main timber raw material in the future, but plantation forest fast-growing timber is prone to decay and insects. , mildew, so wood protection will play a role in prolonging the life of wood, reducing the waste of wood due to decay and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/08B27K3/52B27K5/00B27K5/04
CPCB27K3/08B27K3/52B27K5/003B27K5/0075B27K5/04B27K2240/20
Inventor 刘凯
Owner 含山县茂盛胶合板厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products