Seamless silk embroidery wall cloth and preparing method thereof

A silk and embroidery technology, applied in the directions of non-polymer adhesive additives, adhesive additives, non-polymer organic compound adhesives, etc. And other issues

Inactive Publication Date: 2018-01-16
ANHUI YINTU DECORATION MATERIALS CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wall cloth is a very common material in the existing interior decoration. It is mainly set on the wall by glue and splicing. Although the quality of the existing wall cloth is relatively good, there are still shortcomings: it is easy to change color Resistance to scrubbing, moisture absorption and mildew, especially its poor anti-mold effect
Due to the above-mentioned defects, the promotion of decoration in decoration has been greatly limited, and it has brought great industry obstacles for the wallpaper industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Seamless silk embroidery wall cloth and preparing method thereof
  • Seamless silk embroidery wall cloth and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The present invention also provides a method for preparing the above-mentioned seamless silk embroidered wall covering, the preparation method comprising:

[0021] 1) Apply the adhesive to the surface of the cotton cloth layer, and then perform preliminary drying;

[0022] 2) laying the silk on the surface of the adhesive, and then performing secondary drying to obtain the primary product;

[0023] 3) The initial product is subjected to compaction treatment, and the surface of the silk layer is embroidered to prepare a seamless silk embroidery wall covering.

[0024] In step 1) of the above-mentioned preparation method, the specific conditions of preliminary drying can be selected within a wide range of conditions, but in order to make the prepared wall covering have a more excellent mechanical anti-fungal effect, preferably, in step 1), The preliminary drying at least satisfies the following conditions: the drying temperature is 50-70°C, and the drying time is 0.5-1h....

preparation example 1

[0029] 1) Stir polyvinyl alcohol, urea, methyl methacrylate, polyacrylamide, alkylphenol polyoxyethylene ether, ethylene glycol and water for 1 h to prepare mixture I;

[0030] 2) Add starch, nano-silicon oxide (average particle size of 20nm), and nano-diatomaceous earth (average particle size of 20nm) to the mixture I and stir for 30min to prepare mixture II;

[0031] 3) Thickener (methyl cellulose) and defoamer (polyoxyethylene polyoxypropylene pentaerythritol ether) were added to the mixture II and stirred for 30 minutes to obtain adhesive A1; wherein, polyvinyl alcohol, The weight ratio of starch, urea, methyl methacrylate, polyacrylamide, nano silicon oxide, nano diatomaceous earth, alkylphenol polyoxyethylene ether, ethylene glycol, water, thickener and defoamer is 100: 30:9:38:48:20:8:8:250:70:3:2.

preparation example 2

[0033] 1) Stir polyvinyl alcohol, urea, methyl methacrylate, polyacrylamide, alkylphenol polyoxyethylene ether, ethylene glycol and water for 1 h to prepare mixture I;

[0034] 2) Add starch, nano-silicon oxide (average particle size of 15nm), and nano-diatomaceous earth (average particle size of 15nm) to the mixture I and stir for 30min to prepare mixture II;

[0035] 3) Thickener (hydroxyethyl cellulose) and defoamer (polyoxyethylene polyoxypropanol amine ether) were added to the mixture II and stirred for 30 minutes to obtain adhesive A2; wherein, polyethylene The weight ratio of alcohol, starch, urea, methyl methacrylate, polyacrylamide, nano silicon oxide, nano diatomaceous earth, alkylphenol polyoxyethylene ether, ethylene glycol, water, thickener and defoamer is 100:25:8:35:45:15:5:7:200:50:2:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses seamless silk embroidery wall cloth and a preparing method thereof. The seamless silk embroidery wall cloth includes a cotton cloth layer and a bonding layer which are compounded in sequence from top to bottom. Silk is implanted in the surface of the bonding layer, and an embroidery layer is arranged on the surface of the silk layer. The bonding layer is formed by drying abonding agent, and the bonding agent is composed of polyving alcohol, starch, urea, methyl methacrylate, polyacrylamide, nano silicon dioxide, nano kieselguhr, alkylphenol ethoxylates, ethylene glycol, water, a thickening agent and an antifoaming agent. The length of the silk ranges from 12 cm to 20 cm. The seamless silk embroidery wall cloth prepared through the preparing method has good mechanical performance and a good antifungal effect.

Description

technical field [0001] The invention relates to a wall covering, in particular to a seamless silk embroidery wall covering and a preparation method thereof. Background technique [0002] Wall cloth is a very common material in the existing interior decoration. It is mainly set on the wall by glue and splicing. Although the quality of the existing wall cloth is relatively good, there are still shortcomings: it is easy to change color It is resistant to scrubbing, moisture absorption and mildew, especially its anti-mold effect is poor. Due to the above-mentioned defects, the promotion of decoration in decoration has been greatly limited, which has brought great industry obstacles for the wallpaper industry. Contents of the invention [0003] The object of the present invention is to provide a seamless silk embroidered wall covering and a preparation method thereof. The seamless silk embroidered wall covering prepared by the preparation method has excellent mechanical proper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04F13/00C09J4/02C09J4/06C09J11/04C09J11/06C09J11/08
Inventor 凌清明周玉斌吴中建莫秀斌
Owner ANHUI YINTU DECORATION MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More