A technology of automotive lamps and crafts, which is applied in metal material coating technology, household appliances, sputtering coating, etc., can solve the problems of uneven film thickness and low reflectivity of the film, and achieve stable reflectivity and good protection , the effect of long-term use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0035] Example 1:
[0036] A coating process for automotive lamps includes the following steps:
[0037] (1) Dry
[0038] The polyethylene terephthalate and silica particles are dried in a dryer, the temperature of the dryer is 80°C, the drying time is 8 hours, and the polyethylene terephthalate The mass fractions of and silica particles are 40% and 60% respectively;
[0039] (2) Mixed
[0040] Centrifugal mixing the dried polyethylene terephthalate, silicon dioxide particles and dimethyl silicone oil emulsifier in a centrifuge to form a mixture, and the centrifugal mixing time is 15 minutes;
[0041] (3) Reaction
[0042] Put the mixed material after mixing into the polymerization reactor to make it react, and the reaction time is 20 min;
[0043] (4) Extrusion
[0044] Feed the reacted materials to the extrusion feeder for feeding, and then to the twin-screw extruder for extrusion and granulation to obtain mixed particles;
[0045] (5) Calendering
[0046] Fully mix the mixed particles and...
Example Embodiment
[0059] Example 2:
[0060] A coating process for automotive lamps includes the following steps:
[0061] (1) Dry
[0062] The polyethylene terephthalate and silica particles are dried in a dryer, the temperature of the dryer is 90°C, the drying time is 10 hours, and the polyethylene terephthalate The mass fractions of and silica particles are 60% and 40% respectively;
[0063] (2) Mixed
[0064] Centrifugal mixing the dried polyethylene terephthalate, silica particles and dimethyl silicone oil emulsifier in a centrifuge to form a mixture, and the centrifugal mixing time is 20 min;
[0065] (3) Reaction
[0066] Put the mixed material after mixing into the polymerization reactor to make it react, and the reaction time is 30 min;
[0067] (4) Extrusion
[0068] Feed the reacted materials to the extrusion feeder for feeding, and then to the twin-screw extruder for extrusion and granulation to obtain mixed particles;
[0069] (5) Calendering
[0070] Fully mix the mixed particles and PET, and th...
Example Embodiment
[0083] Example 3:
[0084] A coating process for automotive lamps includes the following steps:
[0085] (1) Dry
[0086] The polyethylene terephthalate and silica particles are dried in a dryer, the temperature of the dryer is 100°C, the drying time is 12h, and the polyethylene terephthalate The mass fractions of and silica particles are 80% and 20% respectively;
[0087] (2) Mixed
[0088] Centrifugal mixing the dried polyethylene terephthalate, silica particles and dimethyl silicone oil emulsifier in a centrifuge to form a mixture, and the centrifugal mixing time is 25 min;
[0089] (3) Reaction
[0090] Put the mixed material after mixing into the polymerization reactor to make it react, and the reaction time is 40 min;
[0091] (4) Extrusion
[0092] Feed the reacted materials to the extrusion feeder for feeding, and then to the twin-screw extruder for extrusion and granulation to obtain mixed particles;
[0093] (5) Calendering
[0094] The mixed particles and PET are fully mixed, and ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap