A kind of etching process of magnesium alloy etching plate
A magnesium alloy plate and magnesium alloy technology are applied in the field of etching process of magnesium alloy etching plate, which can solve the problems of unstable performance of magnesium alloy etching plate, poor etching edge slope, lack of mature etching process, etc. Clear surface, low density effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] This embodiment relates to an etching process for a magnesium alloy etching plate, including preparing the plate, attaching a film, exposing, developing, etching and drying. When making a letterpress, the process parameters of the etching include:
[0040] (1) Rotational speed: the rotational speed of the etching machine blade is 420-430rpm;
[0041] (2) Etching solution temperature: when publishing, the temperature of the etching solution was 33-34°C; when publishing, the temperature of the etching solution was 38-39°C;
[0042] (3) Etching time
[0043] When using the newly prepared etching solution, when the etching time is 5 minutes, the etching depth on the magnesium alloy plate is 0.7-0.8mm; if you want to etch to other depths, you need to prolong the etching time proportionally. When using a non-freshly prepared etching solution, gradually extend the etching time of the next magnesium alloy plate according to the etching depth of the previous magnesium alloy pla...
Embodiment 2
[0051] This embodiment relates to an etching process for a magnesium alloy etching plate, including preparing the plate, attaching a film, exposing, developing, etching and drying. When making a gravure, the etching process parameters include:
[0052] (1) Rotational speed: the rotational speed of the etching machine blade is 370-380rpm;
[0053] (2) Etching solution temperature: when publishing, the temperature of the etching solution was 35-36°C; when publishing, the temperature of the etching solution was 38-39°C;
[0054] (3) Etching time
[0055]When using the newly prepared etching solution, when the etching time is 5 minutes, the etching depth on the magnesium alloy plate is 0.7-0.8mm; if you want to etch to other depths, you need to prolong the etching time proportionally. When using a non-freshly prepared etching solution, gradually extend the etching time of the next magnesium alloy plate according to the etching depth of the previous magnesium alloy plate. If the e...