A kind of titanium-doped indium sulfide spangle microsphere and its preparation method and application

A technology doped with indium zinc sulfide and titanium, which is applied in the field of catalysis, can solve problems such as photocorrosion and affecting the rate of hydrogen production, and achieve the effect of improving photocorrosion, improving the ability of photocatalytic hydrogen production, and the preparation process is simple and controllable

Active Publication Date: 2018-11-06
INT ACAD OF OPTOELECTRONICS AT ZHAOQING SOUTH CHINA NORMAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, sulfides have photocorrosion phenomenon in the photocatalytic reaction, which in turn affects the rate of hydrogen production by photocatalyst photolysis of water.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of titanium-doped indium sulfide spangle microsphere and its preparation method and application
  • A kind of titanium-doped indium sulfide spangle microsphere and its preparation method and application
  • A kind of titanium-doped indium sulfide spangle microsphere and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Weigh 1mmol of zinc chloride, 2mmol of indium chloride, and 5mmol of thioacetamide, add 80mL of deionized water and stir evenly, transfer to a polytetrafluoroethylene tank, put it into a high-pressure reactor, and put it in a blast drying oven at 80°C Thermal reaction for 12 hours; after the hydrothermal treatment, pour off the supernatant, take the orange-yellow precipitate at the bottom, wash it three times with deionized water, and then dry it in a blast drying oven at 60°C for 8 hours to obtain indium sulfide spangles with a flower-like structure shaped microspheres.

[0033] Take 10mL of titanium sulfate solution with a concentration of 0.1g / L, add 1g of indium zinc sulfide powder, and heat on a heating platform at 30°C for 3 hours while stirring; centrifuge the mixed solution, remove the lower layer of precipitate, wash it with water three times, and place it in a blast drying oven Dry at a temperature of 60° C. to obtain 0.1% titanium-doped indium sulfide spangle...

Embodiment 2

[0035] Weigh 1mmol of zinc chloride, 2mmol of indium chloride, and 5mmol of thioacetamide, add 80mL of deionized water and stir evenly, transfer to a polytetrafluoroethylene tank, put it into a high-pressure reactor, and put it in a blast drying oven at 80°C Thermal reaction for 10 hours; after the hydrothermal treatment, pour off the supernatant, take the orange-yellow precipitate at the bottom, wash it three times with deionized water, and dry it in a blast drying oven at 60°C for 8 hours to obtain indium sulfide spangles with a flower-like structure shaped microspheres.

[0036] Take 10mL of titanium sulfate solution with a concentration of 0.15g / L, add 1g of indium zinc sulfide powder, and heat it on a heating platform at 80°C for 1 hour while stirring; centrifuge the mixed solution, remove the lower layer and wash it with water for three times, then place it in a blast drying oven Dry at a temperature of 60° C. to obtain 0.15% titanium-doped indium sulfide spangle microsp...

Embodiment 3

[0038] Weigh 1mmol of zinc nitrate, 2mmol of indium chloride, and 5mmol of thioacetamide, add 80mL of deionized water and stir evenly, transfer to a polytetrafluoroethylene tank, put it into a high-pressure reactor, and heat it in a blast drying oven at 80°C React for 12 hours; after the hydrothermal treatment, pour off the supernatant, take the orange-yellow precipitate at the bottom, wash it three times with deionized water, and dry it in a blast drying oven at 60°C for 10 hours to obtain a flower-like indium sulfide spangle Microspheres.

[0039] Take 10mL of titanium sulfate solution with a concentration of 0.2g / L, add 1g of indium zinc sulfide powder, and heat it on a heating platform at 150°C for 0.25 hours while stirring; centrifuge the mixed solution, remove the lower layer and wash it with water for three times, then place it in a blast drying oven Dry at a temperature of 60° C. to obtain 0.2% titanium-doped indium sulfide spangle microsphere composite photocatalyst. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a titanium-doped indium sulfide spangle microsphere and its preparation method and application, the preparation method of the titanium-doped indium sulfide spangle microsphere is as follows: placing the indium sulfide spangle microsphere In a titanium salt solution, heat and stir at 30-150°C for 0.25-3 hours; then centrifuge the mixed solution, remove the lower layer of precipitate, wash and dry to obtain the titanium-doped indium sulfide spangle-shaped microspheres; the indium sulfide The mass ratio of the spangle microspheres to the titanium salt is 100:0.01-10. In the invention, the indium sulfide spangle microspheres are placed in a titanium salt solution, and the indium sulfide spangle microspheres are doped with titanium ions by a dipping method, thereby further improving the photocatalytic activity of the indium zinc sulfide. The titanium-doped indium sulfide spangle microspheres prepared by the invention have stable morphology, large specific surface area, and higher photocatalytic hydrogen production activity, and can be used for photocatalytic decomposition of water to produce hydrogen.

Description

technical field [0001] The invention relates to the technical field of catalysis, in particular to a titanium-doped indium sulfide spangle microsphere and a preparation method and application thereof. Background technique [0002] With the development of human science and technology and the growth of living standards, energy problems have gradually become the main problems facing human society. In addition to the energy crisis caused by the yearly increase in energy consumption, the greenhouse effect caused by the burning of fossil fuels also needs to be resolved urgently. For the continuation and stability of human sustainable development, it is imminent to develop a clean and environmentally friendly new energy source. Solar energy, wind energy, hydrogen energy, nuclear energy, and biological energy are all objects of research and development by scientific researchers in recent years. Among them, hydrogen energy is environmentally friendly, non-toxic, has high combustion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/04B01J35/08C01B3/04
CPCC01B3/042B01J27/04B01J35/51B01J35/39Y02E60/36
Inventor 王新马歌陈志鸿苑明哲周国富
Owner INT ACAD OF OPTOELECTRONICS AT ZHAOQING SOUTH CHINA NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com