Ceramic water permeable brick and production method thereof

A production method and a technology for permeable bricks are applied in the field of ceramic permeable bricks and their production, which can solve the problem of low water permeability of permeable bricks, and achieve the effects of high strength, production cost saving and high strength.

Active Publication Date: 2018-03-06
JINGDEZHEN CERAMIC INSTITUTE
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the first technical problem to be solved by the present invention is to overcome the problem of non-uniform internal and external performance of the existing ceramic permeable bricks, thereby providing a permeable brick with uniform performance; the second technical problem to be solved by the present invention is to overcome The problem that the existing permeable bricks have low water permeability, thus providing a permeable brick with high water permeability; further the present invention also provides a production method for the above permeable bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic water permeable brick and production method thereof
  • Ceramic water permeable brick and production method thereof
  • Ceramic water permeable brick and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a ceramic permeable brick, which is made of waste ceramic tiles as the main raw material, and introduces combustible raw materials, plus a binder, and is sintered according to the following formula:

[0038] Formula (by mass percentage):

[0039] Ceramic tile waste tiles 72% (among them, 5-30 meshes accounted for 36%, 30-60 meshes accounted for 36%)

[0040] Clean coal 8%

[0041] The mixture of water glass and pulp waste liquid is 20% (the mass ratio of the two is 1:1).

[0042] The method for producing the above-mentioned ceramic permeable bricks is carried out in the following steps:

[0043] (1) Ingredients: Waste ceramic tiles are sieved according to the particle gradation ratio of the formula, and the clean coal of the formula amount is added, and stirred and mixed evenly. Add the mixture of water glass and pulp waste liquid and stir well.

[0044] (2) Stale: stale the evenly stirred raw materials for 15 hours;

[0045] (3) Forming: p...

Embodiment 2

[0050] This embodiment provides a ceramic permeable brick, which is made of waste ceramic tiles as the main raw material, and introduces combustible raw materials, plus a binder, and is sintered according to the following formula:

[0051] Formula (by mass percentage):

[0052] Ceramic tile waste tiles 68% (among them, 5-30 meshes accounted for 36%, 60-120 meshes accounted for 32%)

[0053] Low quality coal 17%

[0054] The mixture of water glass and pulp waste liquid 15% (plus, the mass ratio of the two is 1:2).

[0055] The method for producing the above-mentioned ceramic permeable bricks is carried out in the following steps:

[0056] (1) Ingredients: Waste ceramic tiles are sieved according to the particle gradation ratio of the formula, and the clean coal of the formula amount is added, and stirred and mixed evenly. Add the mixture of water glass and pulp waste liquid and stir well.

[0057] (2) Stale: stale the evenly stirred raw materials for 12 hours;

[0058] (3)...

Embodiment 3

[0063] This embodiment provides a ceramic permeable brick, which is made of waste ceramic tiles as the main raw material, and introduces combustible raw materials, plus a binder, and is sintered according to the following formula:

[0064] Formula (by mass percentage):

[0065] Ceramic tile waste tiles 34% (among them, 5-30 meshes accounted for 20%, 30-60 meshes accounted for 14%)

[0066] Gangue 51%

[0067] The mixture of water glass and pulp waste liquid 15% (plus, the mass ratio of the two is 1:3).

[0068] The method for producing ceramic permeable bricks is carried out in the following steps:

[0069] (1) Ingredients: Waste ceramic tiles are sieved according to the particle gradation ratio of the formula, and the clean coal of the formula amount is added, and stirred and mixed evenly. Add the mixture of water glass and pulp waste liquid and stir well.

[0070] (2) Stale: stale the evenly stirred raw materials for 18 hours;

[0071] (3) Forming: put the raw material ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of inorganic non-metal materials, and discloses a ceramic water permeable brick and a production method thereof. The ceramic water permeable brick is prepared from an aggregate, a binding agent and a combustible raw material; heat generated during a combustion process of the combustible raw material can be used for heating a green brick from inside to outside, and meanwhile, a kiln is used for heating the green brick from outside to inside, so that the uniformity of inner and outer structures of the green brick is increased under the combined action of insideand outside heating, and the performance of the green brick can be more uniform; in addition, the heat efficiency is increased to a large extent. Residue generated after fuel combustion can be used as the aggregate of the ceramic water permeable brick in situ and can be fully utilized, zero emission of fuel residue is realized, and the production cost of the ceramic water permeable brick is saved; in addition, the volume of the combustible raw material is lessened after combustion, larger pore diameter is formed between residue particles, and meanwhile, certain gaps are formed in the residueper se, so that the properties of high strength and good water permeability are given to the ceramic water permeable brick through the special structure. During roasting of the ceramic water permeablebrick, a gradient temperature rising mode is adopted, the combustible raw material can be fully combusted, meanwhile, the green brick can be prevented from being over-combusted, and the quality of the ceramic water permeable brick is ensured.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a ceramic permeable brick and a production method thereof. Background technique [0002] With the continuous advancement and development of my country's new urbanization construction, urban public places need to be covered with a large number of pavement building materials. Traditional pavement construction materials are mainly stone, cement, ordinary ceramic square bricks, etc. The common characteristics of these materials are impermeable and airtight, and have no water retention function. Rainwater and snow water cannot effectively penetrate into the ground, resulting in reduced groundwater and ground subsidence , the soil moisture content is low, the growth of flowers and trees is inhibited, etc., destroying the ecological environment. At the same time, the impermeable pavement also blocks the exchange of water vapor and heat energy betwe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/13C04B33/32C04B38/06
CPCC04B33/131C04B33/1315C04B33/1324C04B33/32C04B35/6316C04B38/068C04B2235/3201C04B2235/3427C04B2235/6562C04B2235/6567C04B2235/96Y02P40/60
Inventor 苗立锋江伟辉梁健包镇红徐贵荣
Owner JINGDEZHEN CERAMIC INSTITUTE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap