Preparation method of superstrong synthetic quartz stone and prepared superstrong synthetic quartz stone

A technology for synthesizing quartz and quartz stone, which is applied in the field of decorative building materials, can solve the problems of natural resource destruction, consumption of a large amount of natural quartz stone, and high cost of quartz stone, and achieves the effects of reducing the preparation cost, having bright colors and good mechanical properties.

Inactive Publication Date: 2018-03-13
石家庄多邦晶岗石有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, quartz stone still has some defects and deficiencies, for example, the cost of quartz stone is relatively high, and a large amount of natural quartz stone is required to be prepared as a raw material, which will also cause certain damage to natural resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of superstrong synthetic quartz stone and prepared superstrong synthetic quartz stone
  • Preparation method of superstrong synthetic quartz stone and prepared superstrong synthetic quartz stone
  • Preparation method of superstrong synthetic quartz stone and prepared superstrong synthetic quartz stone

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Prepare super strong synthetic quartz stone as follows:

[0064] (1) Waste treatment, decontamination, cleaning and draining the marble waste, breaking the waste larger than 200mm into small pieces, and all the waste reaches an irregular shape with a specification of 20-200mm;

[0065] (2) Lay the waste material, lay the waste material on the surface of the self-adhesive, and paste it to form a plate;

[0066] (3) Clean up the assembly platform and the mould, clean up and assemble the mould, and then lay kraft paper on the bottom of the mould;

[0067] (4) Prepare materials. Prepare various raw materials such as quartz stone particles, quartz stone fine powder, cullet, unsaturated polyester resin, color paste, curing agent, accelerator, coupling agent, etc. according to the formula ratio. deployment;

[0068] (5) Stir, pour the prepared raw materials into the mixing tank in order and stir until they are evenly stirred;

[0069] (6) Forming, spread the waste materials...

Embodiment 2

[0078] Super strong synthetic quartz stone was prepared according to the method of Example 1, wherein, in Example 2, the waste used was vitrified brick waste.

Embodiment 3

[0080] Super strong synthetic quartz stone was prepared according to the method of Example 1, wherein, in Example 3, the waste used was granite waste.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of superstrong synthetic quartz stone and the prepared superstrong synthetic quartz stone. The preparation method comprises the following steps: laying waste inorganic silicon material fragments on the surface of an adhesive sticker, and pasting the material to form a plate; stirring and blending the raw materials comprising quartz stone particles, quartz stone fine powder, broken glass, unsaturated resin, a color paste, a curing agent, an accelerator and a coupling agent, so as to obtain a wet material; according to the way that the plate is arranged downwards and the adhesive sticker is arranged upwards, putting the plate adhered onto the adhesive sticker into a mold, and then removing the adhesive sticker; then, adding the wet material into the mold to obtain a formed part; carrying out vacuum treatment on the formed part, carrying out vibration and compression treatment, and then carrying out curing, demolding and maintenance treatment toobtain the superstrong synthetic quartz stone. The preparation method has the advantages that waste raw materials are used, the cost is reduced and the method is environmentally friendly, and the prepared superstrong synthetic quartz stone has the advantages of low cost, excellent mechanical property, high quality and various designs and colors.

Description

technical field [0001] The invention relates to the field of decorative building materials, in particular to a method for preparing a super-strong synthetic quartz stone and the produced super-strong synthetic quartz stone. Background technique [0002] At present, commercially available stone is mainly divided into two categories: natural stone and artificial stone. Natural stone materials include granite (various varieties), marble, etc., and artificial stone materials include granite, quartz stone (also known as crystal granite), microcrystalline stone, etc. [0003] Quartz stone is a new type of material that is made of natural quartz stone (granule and fine powder), resin and pigment, and processed by special equipment. Quartz stone has the characteristics of many varieties, good decorative effect, high hardness, good wear resistance, strong stain resistance, corrosion resistance, environmental protection, no radiation, high temperature resistance without deformation, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/02C04B111/82
CPCC04B26/02C04B2111/00017C04B2111/82C04B2201/50C04B14/06C04B14/22C04B18/16C04B18/165C04B18/0427C04B2103/54C04B2103/0068
Inventor 周彤苗李万庆李令顺
Owner 石家庄多邦晶岗石有限公司