Production method of fiber cement board

A fiber cement board and a production method technology, applied in the field of building materials, can solve the problems of cement fiber board not easy to demould, asbestos carcinogenic risk, health hazards of production personnel, etc., and achieve easy demoulding, simple and convenient operation, and high yield. Effect

Inactive Publication Date: 2018-03-13
张克勤
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most of the adhesives used in the production process of cement fiberboard are resins or isocyanates, etc., which are prone to produce harmful gases. Most of the fibers are asbestos fibers. hazards, and the existing cement fiberboard production methods have problems such as difficult demoulding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of production method of fiber cement board, comprises the following steps:

[0016] (1) According to the size of the fiber cement board, make the abrasive mold of the same size and the bottom surface is a water-permeable sheet, and apply a release agent in the mould;

[0017] (2) 50 parts of magnesium oxychloride cement, 5 parts of wood fiber, 10 parts of fly ash, 8 parts of quartz sand, 3 parts of diatomaceous earth, 0.5 part of modifying agent, 0.5 part of sodium lignosulfonate will be formed by weight Put it in a container and mix it with water, stir to make cement slurry;

[0018] (3) Pour the cement slurry of step (2) into the grinding tool of step (1), at 0.5-1kg / cm 2 Rolling and leveling under pressure, removing moisture, curing at 10-50°C and then releasing the mold.

Embodiment 2

[0020] A kind of production method of fiber cement board, comprises the following steps:

[0021] (1) According to the size of the fiber cement board, make the abrasive mold of the same size and the bottom surface is a water-permeable sheet, and apply a release agent in the mould;

[0022] (2) 60 parts of magnesium oxysulfide cements, 8 parts of wood fibers, 12 parts of fly ash, 9 parts of quartz sand, 5 parts of diatomaceous earth, 0.8 parts of modifiers, 0.6 parts of calcium lignosulfonate are formed by weight parts Put it in a container and mix it with water, stir to make cement slurry;

[0023] (3) Pour the cement slurry of step (2) into the grinding tool of step (1), at 0.5-1kg / cm 2 Rolling and leveling under pressure, removing moisture, curing at 10-50°C and then releasing the mold.

Embodiment 3

[0025] A kind of production method of fiber cement board, comprises the following steps:

[0026] (1) According to the size of the fiber cement board, make the abrasive mold of the same size and the bottom surface is a water-permeable sheet, and apply a release agent in the mould;

[0027] (2) 80 parts of magnesium phosphate cement, 10 parts of glass fiber, 15 parts of fly ash, 12 parts of quartz sand, 10 parts of diatomite, 1 part of modifier, 1 part of naphthalenesulfonate formaldehyde condensate, 1 part of magnesium phosphate cement, 10 parts of glass fiber, 10 parts of diatomaceous earth, 1 part of weight parts put into a container and mix with water, and stir to prepare cement slurry;

[0028] (3) Pour the cement slurry of step (2) into the grinding tool of step (1), at 0.5-1kg / cm 2 Rolling and leveling under pressure, removing moisture, curing at 10-50°C and then releasing the mold.

[0029] Adopting the production method of the present invention to produce fiber cemen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method of a fiber cement board, which comprises the following steps: (1) according to the size of the fiber cement board, an abrasive mold with the same size and a water-permeable thin plate is made on the bottom surface, and a release agent is applied in the mould; (2) put the composition raw material of fiber cement board into the container and mix with water, stir and modulate into cement slurry; (3) pour the cement slurry of step (2) into the grinding tool of step (1), at 0.5- Rolling and leveling under 1kg / cm2 pressure, removing moisture, curing at 10-50°C and then releasing the mold. The fiber cement board produced by the production method of the present invention is simple and convenient to operate, the board body is easily demolded, the board body is not easy to be damaged, and the yield is high.

Description

technical field [0001] The invention relates to a production method of a fiber cement board, which belongs to the technical field of building materials. Background technique [0002] At present, most of the adhesives used in the production process of cement fiberboard are resins or isocyanates, etc., which are prone to produce harmful gases. Most of the fibers are asbestos fibers. harm, and the existing production methods of cement fiber boards have problems such as difficult demoulding. Contents of the invention [0003] In view of this, the present invention provides a production method of fiber cement board to overcome the above-mentioned deficiencies mentioned in the prior art. [0004] For solving above technical problem, technical scheme of the present invention has adopted a kind of production method of fiber cement board, and it comprises the following steps: [0005] (1) According to the size of the fiber cement board, make the abrasive mold of the same size and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/30C04B28/32C04B28/34
CPCC04B28/30C04B28/32C04B28/344C04B16/02C04B18/08C04B14/06C04B14/08C04B2103/0068C04B24/18C04B24/226
Inventor 张克勤
Owner 张克勤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap