Graphene/manganese tetroxide composite nano lubricating additive and its synthesis method

A technology of manganese tetroxide and lubricating additives, applied in the field of materials, can solve the problems of reducing the lubricating properties of graphene, the destruction of carbon atoms in the layer, and the performance degradation, etc., to achieve excellent and stable lubricating properties, saving load processes, and low production costs. Effect

Active Publication Date: 2020-06-19
TSINGHUA UNIV +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although chemically modified graphene has good solubility, the introduction of foreign atoms or functional groups is likely to destroy its structure, which significantly reduces its intrinsic performance.
For example, the irregular folds and bends on the edges of graphite sheets, and the destruction and loss of carbon atoms in the layers will reduce the lubricating properties of graphene.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene/manganese tetroxide composite nano lubricating additive and its synthesis method
  • Graphene/manganese tetroxide composite nano lubricating additive and its synthesis method
  • Graphene/manganese tetroxide composite nano lubricating additive and its synthesis method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] (1) In an ice bath environment, mix 300g concentrated sulfuric acid and 35g potassium permanganate fully, then slowly add 10g graphite powder, after mixing evenly, raise the temperature to 50°C, and react for 1h to obtain graphite oxide and / or graphite oxide Mixture of alkenes;

[0058](2) Add 80 mL of 30% hydrogen peroxide to reduce the unreacted oxidant in the mixed solution, add 1 L of deionized water to dilute, and then maintain ultrasonic vibration for 1 hour to obtain the graphene oxide mixed solution;

[0059] (3) Under the action of magnetic stirring, slowly add potassium hydroxide solution (20wt%) directly to the graphene oxide mixed solution, adjust the mixed solution to be alkaline, and make its pH=9;

[0060] (4) filter out the solid precipitate in step (3) gained alkaline solution;

[0061] (5) Put the filtered solid precipitate into a blast drying oven, heat up to 170° C., and keep warm for 5 hours to obtain a graphene / manganese tetraoxide composite produ...

Embodiment 2

[0070] (1) In an ice bath environment, fully mix 300g concentrated sulfuric acid and 30g potassium permanganate, then slowly add 10g graphite powder, after mixing evenly, raise the temperature to 50°C for 1h to obtain graphite oxide and / or graphene oxide the mixture;

[0071] (2) Add 80 mL of 30% hydrogen peroxide to reduce the unreacted oxidant in the mixed solution, add 5 L of deionized water to dilute, and then maintain ultrasonic vibration for 1 hour to obtain the graphene oxide mixed solution;

[0072] (3) Under the action of magnetic stirring, slowly add potassium hydroxide solid directly to the graphene oxide mixed solution, adjust the mixed solution to be alkaline, and make its pH=11;

[0073] (4) filter out the solid precipitate in step (3) gained alkaline solution;

[0074] (5) Put the filtered solid precipitate into a blast drying oven, heat up to 170° C., and keep warm for 5 hours to obtain a graphene / manganese tetraoxide composite product;

[0075] (6) Use 3L of...

Embodiment 3

[0078] (1) In an ice-bath environment, fully mix 300g of concentrated sulfuric acid and 35g of potassium permanganate, then slowly add 10g of graphite powder, after mixing evenly, heat up to 45°C and react for 1h to obtain graphite oxide and / or graphene oxide the mixture;

[0079] (2) Add 80 mL of 30% hydrogen peroxide to reduce the unreacted oxidant in the mixed solution, add 1 L of deionized water to dilute, and then maintain ultrasonic vibration for 1 hour to obtain the graphene oxide mixed solution;

[0080] (3) Under the action of magnetic stirring, slowly add potassium hydroxide solid directly to the graphene oxide mixed solution, adjust the mixed solution to be alkaline, and make its pH=11;

[0081] (4) filter out the solid precipitate in step (3) gained alkaline solution;

[0082] (5) Put the filtered solid precipitate into a blast drying oven, heat up to 100° C., and keep warm for 5 hours to obtain a graphene / manganese tetraoxide composite product;

[0083] (6) Use ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
volumeaaaaaaaaaa
diameteraaaaaaaaaa
breaking strengthaaaaaaaaaa
Login to View More

Abstract

Provided are a graphene / trimanganese tetraoxide composite nano lubricating additive and a synthesis method thereof. Graphite is mixed with concentrated sulfuric acid and potassium permanganate for oxidation reaction, hydrogen peroxide is added to reduce unreacted potassium permanganate, water is added for dilution, ultrasonic treatment is carried out after the dilution, pH is adjusted to be alkaline, evaporation or filtration is carried out to obtain a solid product, reduction treatment is carried out at high temperature, and the product is washed and ball milled to obtain the composite nano lubricating additive.

Description

technical field [0001] The invention belongs to the field of materials, and in particular relates to a graphene / trimanganese tetraoxide composite nano-lubricating additive and a synthesis method thereof. Background technique [0002] With the development of industrial modernization, mechanical equipment is developing towards high speed and heavy load, which poses a higher challenge to the friction reduction and wear resistance of the friction pairs of parts. In order to reduce the friction energy consumption of mechanical equipment and improve the operation stability, the use of lubricating oil has played a great role. Today, the development of lubricating oil and additives has changed from the initial requirements of adapting to mechanical operation to the requirements of environmental protection and energy saving. However, traditional anti-wear additives contain groups such as sulfur and phosphorus, which easily cause metal corrosion and environmental pollution. Graphene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M125/10C10M177/00C10N30/04C10N30/06
CPCC10M125/10C10M177/00C10M2201/041C10M2201/062C10N2030/04C10N2030/06C10N2020/055C10N2020/06
Inventor 何永勇赵军李英儒毛俊元雒建斌
Owner TSINGHUA UNIV