Copper molybdate adsorbing material and preparation method thereof

An adsorption material, copper molybdate technology, applied in chemical instruments and methods, adsorbed water/sewage treatment, molybdenum compounds, etc. Effect

Inactive Publication Date: 2018-03-30
长沙埃比林环保科技有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is still a certain distance between the general and practical application of common adsorbents for xanthate wastewater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Mix copper sulfate and deionized water at a ratio of 3:8.2, and then shake rapidly in a shaker for 9 minutes to obtain a primary solution. Potassium molybdate and deionized water were mixed according to the ratio of 2:9, and then oscillated rapidly in a shaker for 9 minutes to obtain a secondary solution. The primary solution and the secondary solution were mixed at a ratio of 1:1, and then shaken rapidly in a shaker for 3 hours to obtain a mixed solution. The mixed solution was aged at room temperature for 16 hours, the aged solution was filtered, washed 3 times with deionized water, and then dried for a period of time at a drying temperature of 90°C and a drying time of 4 hours to obtain a primary solid Product: Put the primary solid product into a roasting furnace for roasting at a roasting temperature of 500° C. and a roasting time of 3.5 hours to obtain a copper molybdate adsorption material. The copper molybdate adsorption material, CuO content is 61 ~ 64wt%, MoO...

Embodiment 2

[0027] Mix copper sulfate and deionized water according to the ratio of 3.2:8.6, and then oscillate rapidly in a shaker for 10 minutes to obtain a primary solution. Potassium molybdate and deionized water were mixed according to the ratio of 2.5:9.5, and then oscillated rapidly in a shaker for 10 minutes to obtain a secondary solution. The primary solution was mixed with the secondary solution at a ratio of 1:1, and then shaken rapidly in a shaker for 3.5 hours to obtain a mixed solution. The mixed solution was aged at room temperature for 17 hours, the aged solution was filtered, washed 4 times with deionized water, and then dried for a period of time at a drying temperature of 95°C and a drying time of 5 hours to obtain a primary solid Product: put the primary solid product into a roasting furnace for roasting at a roasting temperature of 700° C. and a roasting time of 4 hours to obtain a copper molybdate adsorption material. The copper molybdate adsorption material, CuO co...

Embodiment 3

[0029] Mix copper sulfate and deionized water according to the ratio of 3.4:9.3, and then oscillate rapidly in a shaker for 10 minutes to obtain a primary solution. Potassium molybdate and deionized water were mixed according to the ratio of 3:10, and then oscillated rapidly in a shaker for 10 minutes to obtain a secondary solution. The primary solution and the secondary solution were mixed according to a ratio of 1:1, and then shaken rapidly in a shaker for 4 hours to obtain a mixed solution. The mixed solution was aged at room temperature for 18 hours, the aged solution was filtered, washed 5 times with deionized water, and then dried for a period of time at a drying temperature of 100°C for 5 hours to obtain a primary solid Product: put the primary solid product into a roasting furnace for roasting at a roasting temperature of 800° C. and a roasting time of 4.5 hours, and then obtain a copper molybdate adsorption material. The copper molybdate adsorption material, CuO cont...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a copper molybdate adsorbing material. The content of CuO is 61-64wt%, the content of MoO3 is 22-25wst%, and the average particle diameter of copper molybdate particles is 300-350nm. A preparation method comprises the following steps: mixing copper sulfate and deionized water, and then quickly vibrating the mixture for a period of time in a vibrator to obtain a primary solution; mixing potassium molybdate and the deionized water, and then quickly vibrating the mixture for a period of time in the vibrator to obtain a secondary solution; mixing the primary solution and the secondary solution, and then quickly vibrating the mixture for a period of time in the vibrator to obtain a mixed solution; aging, filtering and washing the mixed solution, and then performing drying for a period of time to obtain a primary solid product; and roasting the primary solid product in a roasting furnace to obtain the copper molybdate adsorbing material. The copper molybdate adsorbing material provided by the invention has small copper molybdate impurity content, high purity and good particle size uniformity and has good adsorption capacity to xanthate.

Description

technical field [0001] The invention relates to the environmental protection field of mineral processing wastewater treatment, in particular to a copper molybdate adsorption material and a preparation method thereof. Background technique [0002] Since my country's reform and opening up, with the introduction of foreign technology and the maturation of the domestic market environment, in the past 30 years, the industry has developed rapidly. The rapid development of industry has promoted economic take-off, but it cannot be ignored that for a long time, the heavy industrialization of my country's industrial structure has led to high consumption of resources and energy, and high pollution to the environment. The hazards of air pollution and industrial wastewater have seriously affected people's health. Pollution has become the biggest livelihood issue, and it is imperative to adjust the industrial structure and strictly reduce energy conservation and emission reduction. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/02B01J20/28B01J20/30C01G39/00C02F1/28C02F103/10
CPCB01J20/0218B01J20/0237B01J20/28004B01J20/28016C01G39/00C01P2004/60C02F1/281C02F2103/10
Inventor 不公告发明人
Owner 长沙埃比林环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com