Modified diatomite-based multifunctional building board

A technology for building board and diatomite, applied in the field of building materials, can solve problems such as poor mechanical properties, and achieve the effects of enhancing mechanical properties, enhancing strength, and enhancing adsorption properties

Inactive Publication Date: 2018-04-20
CHANGZHOU DINGRI ENVIRONMENTAL PROTECTION TECH
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem mainly solved by the present invention is: Aiming at the problem of poor mechanical properties of traditional diatomite building boards, a modified diatomite-based multifunctional building board is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024]Add polyvinyl alcohol and water into the No. 4 beaker at a mass ratio of 1:100, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, and then move the No. , under the condition of rotating speed of 500r / min, heat and stir to dissolve for 50min to obtain the polyvinyl alcohol liquid; place the coconut shell fiber in an oven and dry it until the water content is 10% to obtain the dry coconut shell fiber, and mix the dry coconut shell fiber with Ethyl orthosilicate was placed in a No. 1 beaker at a mass ratio of 1:50, and stirred and mixed for 50 minutes at a rotating speed of 600r / min to obtain a dry coconut fiber mixture, and then filter the dry coconut fiber mixture to obtain To pretreat coconut shell fibers, place the pretreated coconut shell fibers in a carbonization furnace, and fill the furnace with nitrogen gas at a rate of 70mL / min, and keep warm for 3 hours at a temperature of 550°C to obtain carbonized coconut shell fibers for one t...

example 2

[0026] Add polyvinyl alcohol and water into the No. 4 beaker at a mass ratio of 1:100, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, and then move the No. , under the condition of rotating speed of 500r / min, heat and stir to dissolve for 50min to obtain the polyvinyl alcohol liquid; place the coconut shell fiber in an oven and dry it until the water content is 10% to obtain the dry coconut shell fiber, and mix the dry coconut shell fiber with Ethyl orthosilicate was placed in a No. 1 beaker at a mass ratio of 1:50, and stirred and mixed for 50 minutes at a rotating speed of 600r / min to obtain a dry coconut fiber mixture, and then filter the dry coconut fiber mixture to obtain To pretreat coconut shell fibers, place the pretreated coconut shell fibers in a carbonization furnace, and fill the furnace with nitrogen gas at a rate of 70mL / min, and keep warm for 3 hours at a temperature of 550°C to obtain carbonized coconut shell fibers for one ...

example 3

[0028] Add polyvinyl alcohol and water into the No. 4 beaker at a mass ratio of 1:100, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, and then move the No. , under the condition of rotating speed of 500r / min, heat and stir to dissolve for 50min to obtain the polyvinyl alcohol liquid; place the coconut shell fiber in an oven and dry it until the water content is 10% to obtain the dry coconut shell fiber, and mix the dry coconut shell fiber with Ethyl orthosilicate was placed in a No. 1 beaker at a mass ratio of 1:50, and stirred and mixed for 50 minutes at a rotating speed of 600r / min to obtain a dry coconut fiber mixture, and then filter the dry coconut fiber mixture to obtain To pretreat coconut shell fibers, place the pretreated coconut shell fibers in a carbonization furnace, and fill the furnace with nitrogen gas at a rate of 70mL / min, and keep warm for 3 hours at a temperature of 550°C to obtain carbonized coconut shell fibers for one ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses modified diatomite-based multifunctional building board, and belongs to the technical field of building materials. The modified diatomite-based multifunctional building board is prepared by the following steps: calcining diatomite to obtain primary treated diatomite; mixing the primary treated diatomite with an agar liquid, performing nitrogen charging and thermal insulation reaction, so that secondary treated diatomite is obtained; mixing the secondary treated diatomite with a casein solution to obtain tertiary treated diatomite; mixing the tertiary treated diatomite with a ferric chloride solution, and performing vacuum concentration, so that quaternary treated diatomite is obtained; performing ball milling on the quaternary treated diatomite with paraffin wax, soas to obtain modified diatomite; and mixing the modified diatomite, silane coupling agent, sepiolite, modified carbonized coconut shell fiber, phenolic resin, polyvinyl alcohol solution, curing agentand water to obtain a mixed slurry, and then injecting the mixed slurry into a mold, putting the mold into a hot press, and performing hot press molding, so that the modified diatomite-based multifunctional building board is obtained. The modified diatomite-based multifunctional building board has a good bending strength, and has a certain purifying effect on formaldehyde.

Description

technical field [0001] The invention discloses a modified diatomite-based multifunctional building plate, which belongs to the technical field of building materials. Background technique [0002] With the increasing level of modern social economy and technology, the majority of urban and rural residents pay more and more attention to the safety and comfort of the indoor living environment. Dry and wet conditions, formaldehyde pollution, PM2.5, air-conditioning diseases, etc. have long become public concerns. A hot topic, environment-regulating porous materials with strong adsorption media such as diatomaceous earth and activated carbon as functional components have therefore become one of the research hotspots. [0003] Diatomite is a soft rock formed by transporting, depositing and mineralizing under the action of natural factors after the death of extremely abundant single-celled diatoms in ancient times. The properties are also relatively stable, and traditionally mainly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/12C04B38/02C04B20/04C04B20/12C04B14/38C04B14/08
CPCC04B14/386C04B20/04C04B20/12C04B26/122C04B2111/00025C04B14/08C04B24/42C04B14/042C04B24/2623C04B24/121C04B24/125C04B38/02C04B20/1055C04B20/1029C04B20/107C04B20/1044C04B20/1022
Inventor 吴展牙殷磊张淼
Owner CHANGZHOU DINGRI ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com