Modified hydroxyapatite-based environment-friendly PVC composite heat stabilizer

A composite heat stabilizer and hydroxyapatite technology, which is applied in the field of material processing aids, can solve problems such as easy precipitation, and achieve the effects of improving dispersion, good synergy, and improving thermal stability

Inactive Publication Date: 2018-04-20
SHAOYANG UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the amount of unmodified zinc-containing hydroxyapatite in the PVC composite heat fixer should not exceed 50%, otherwise it is easy to precipitate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified hydroxyapatite-based environment-friendly PVC composite heat stabilizer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The composite thermal stabilizer of this embodiment contains the following components by mass fraction: modified hydroxyapatite: 70%, zinc stearate: 15%, dibenzoylmethane: 5%, antioxidant 1010: 2% , Polyethylene wax: 8%.

Embodiment 2

[0023] The composite thermal stabilizer of this embodiment contains the following components by mass fraction: modified hydroxyapatite: 60%, zinc stearate: 20%, stearoylbenzoylmethane: 5%, antioxidant 1010: 3%, solid paraffin: 12%.

Embodiment 3

[0025] The composite thermal stabilizer of this example contains the following components in mass fraction: modified hydroxyapatite: 80%, zinc stearate: 10%, dibenzoylmethane: 4%, antioxidant 689: 1% , Polyethylene wax: 5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a modified hydroxyapatite-based environment-friendly PVC composite heat stabilizer. The composite heat stabilizer is prepared from the following components in mass fraction: 60-80% of modified hydroxyapatite, 10-20% of zinc stearate, 3-5% of a beta-diketone-type compound, 1-3% of an antioxidant and 5-12% of a lubricating agent, wherein the beta-diketone-type compound is stearyl benzoylmethane, dibenzoylmethane, calcium acetylacetonate or zinc acetylacetonate, and the modified hydroxyapatite is prepared by adopting polyethylene glycol and calcium stearate as a compositemodifying agent and performing surface modification on hydroxyapatite. All components of the composite heat stabilizer provided by the invention have good synergistic effects, can obviously improve the heat stability of PVC, and have the advantages of being nontoxic, environmentally friendly and lower in cost.

Description

technical field [0001] The invention relates to a PVC heat stabilizer, in particular to a modified hydroxyapatite-based environment-friendly PVC composite heat stabilizer, which belongs to the field of material processing aids. Background technique [0002] PVC is easy to decompose at processing temperature, resulting in darkening of product color and changes in structure and properties. Therefore, during the processing of PVC, heat stabilizers must be added to prevent or reduce its decomposition. At present, commonly used heat stabilizers include lead salts, organotins, metal soaps and composite heat stabilizers. Lead salt heat stabilizer is the earliest developed PVC heat stabilizer with good heat stability. However, due to the strong toxicity of lead salt compounds, which pose a hazard to human and environmental safety, countries around the world are gradually restricting the use of lead salt heat stabilizers. Organotin heat stabilizers have good thermal stability and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K13/06C08K9/10C08K9/04C08K3/32C08K5/098C08K5/07C08K5/00C08L91/06C08L23/06C08L27/06
CPCC08K3/32C08K5/0091C08K5/07C08K5/098C08K9/04C08K9/10C08K13/06C08K2003/325C08L23/06C08L27/06C08L91/06C08L2201/08
Inventor 周喜张超
Owner SHAOYANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com