Method for preparing ceramic-imitating building and ornamental material

A building decoration material and imitation porcelain technology, applied in biocide-containing paints, antifouling/underwater coatings, coatings, etc., can solve the problems of complicated preparation process, weak bonding, brittle and easy to crack decorative paper, etc. Achieve the effects of simple preparation process, excellent waterproof and mildew-proof effect, and excellent adhesive firmness

Active Publication Date: 2018-05-08
龙元明筑科技有限责任公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] It can be seen that among the building material veneer materials in the prior art, the decorative paper has the problems of being brittle and easy to crack, not firm, not waterproof, and prone to mildew, and the coating and stone materials also have the problems of weak bonding, easy falling off, and weather resistance Poor and other problems, while the preparation process is complex, high cost, causing some pollution to the environment, but the current research and application of architectural decorative film is less

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing ceramic-imitating building and ornamental material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Grind acrylonitrile-butadiene-styrene and muscovite in a vertical grinder at a mass ratio of 100:5, so that muscovite is attached to the surface of fine particles of acrylonitrile-butadiene-styrene copolymer, Obtain a modified acrylonitrile-butadiene-styrene copolymer powder with a particle size of 50-200nm;

[0027] (2) Mix the obtained acrylonitrile-butadiene-styrene copolymer modified powder, acrylic resin, ceramic powder and water, add to the disperser, then add emulsifier alkylphenol polyoxyethylene ether, antioxidant Dialkyl dithiophosphate zinc, coloring agent is lithopone, open forced stirring, spindle speed 800r / min, dispersing time is 15min; get pasty material after fully mixing; Wherein acrylic resin 37 weight parts, ceramic powder 6 weight Part, 5 parts by weight of acrylonitrile-butadiene-styrene copolymer modified powder, 40 parts by weight of water, 0.1 part by weight of emulsifier, 0.1 part by weight of antioxidant, 0.05 part by weight of coloring ag...

Embodiment 2

[0031] (1) Grind acrylonitrile-butadiene-styrene and muscovite in a vertical grinder at a mass ratio of 100:6, so that muscovite is attached to the surface of fine particles of acrylonitrile-butadiene-styrene copolymer, Obtain a modified acrylonitrile-butadiene-styrene copolymer powder with a particle size of 50-200nm;

[0032] (2) Mix the obtained acrylonitrile-butadiene-styrene copolymer modified powder, acrylic resin, ceramic powder, and water, add it to the disperser, and then add emulsifier diglycerin polypropylene glycol ether, antioxidant sulfurized hydrocarbon Copper borate salt and coloring agent are lead chrome yellow, start the forced stirring, the spindle speed is 800r / min, and the dispersion time is 20min; after fully mixing, a paste material is obtained; wherein 40 parts by weight of acrylic resin, 6 parts by weight of ceramic powder, acrylonitrile- 8 parts by weight of butadiene-styrene copolymer modified powder, 40 parts by weight of water, 0.2 parts by weight ...

Embodiment 3

[0036](1) Grind acrylonitrile-butadiene-styrene and muscovite in a disc grinder with a mass ratio of 100:10, so that muscovite is attached to the surface of fine particles of acrylonitrile-butadiene-styrene copolymer, Obtain a modified acrylonitrile-butadiene-styrene copolymer powder with a particle size of 50-200nm;

[0037] (2) Mix the obtained acrylonitrile-butadiene-styrene copolymer modified powder, acrylic resin, ceramic powder and water, add to the disperser, then add emulsifier fatty alcohol polyoxyethylene ether, antioxidant sub Triphenyl phosphate, colorant iron oxide red, start forced stirring, spindle speed 1000r / min, disperse time 30min; get paste material after fully mixing; wherein 41 parts by weight of acrylic resin, 9 parts by weight of ceramic powder, acrylonitrile- 10 parts by weight of butadiene-styrene copolymer modified powder, 40 parts by weight of water, 0.3 parts by weight of emulsifier, 0.2 parts by weight of antioxidant, and 0.1 part by weight of col...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of preparation of ornamental materials, and provides a method for preparing a ceramic-imitating building and ornamental material. The method comprises thesteps of using white mica to modify acrylonitrile-butadiene-styrol copolymer to form powder, afterwards, proportioning acrylic resin and ceramic powder into a pasty material, coating the surface of building materials with the pasty material for polishing, and through polishing and heat generation, binding hot-melting acrylonitrile-butadiene-styrene copolymer powder to obtain a layer of compact andrigid acrylic acid ceramic-imitating thin film, so that the ceramic-imitating building and ornamental material is prepared. The ceramic-imitating building and ornamental material is firm in binding,does not easily shed, and has excellent waterproof and antimould effects and weather fastness.

Description

technical field [0001] The invention belongs to the technical field of preparation of decorative materials and provides a method for preparing imitation porcelain building decoration materials. Background technique [0002] With the economic development of the society and the progress of civilization, people's living standards and quality of life are improved, the requirements for housing quality are also getting higher and higher, and the aesthetics of things are becoming more and more frontier of the times, so more and more attention is paid to the quality of life. The choice of decoration materials, various new building decoration materials have been widely developed and applied, especially veneer decoration materials, with the progress of green, environmental protection, ecological, healthy and comfortable life concepts in recent years, great changes have taken place big change. [0003] Building material veneer decoration is one of the important contents of architectur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D7/61C09D7/65C09D7/63C09D5/14
CPCC09D5/14C09D133/00C08L55/02C08K3/34C08K3/00
Inventor 陈庆昝航
Owner 龙元明筑科技有限责任公司