Novel aluminum profile solid wood veneer gluing process

A technology of aluminum profiles and solid wood, which is applied in the field of new aluminum profile solid wood veneer technology, can solve the problems of reduced selectivity, reduced service life and corrosion resistance of aluminum profiles, single style of aluminum profiles, etc., and achieves increased selectivity, improvement and beauty , Design novel effects

Inactive Publication Date: 2018-05-11
浙江丽尚建材科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, most of the existing aluminum profiles are not veneered with solid wood, so that the style of the aluminum profiles is relatively simple, and the life and corrosion resistance of the aluminum profiles are greatly reduced, which reduces the selectivity of people when using it. Therefore, we invented A new type of solid wood veneering process for aluminum profiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] A new aluminum profile solid wood veneer process, comprising the following steps:

[0017] Step 1: Put the material used to make aluminum profiles into the corresponding embossing machine, and adjust the corresponding embossing style and interval size through the set knife edge, so that the aluminum profile can be pressed with the aluminum profile when it is continuously heated. The flower machine is used to express the corresponding pattern,

[0018] Step 2: After embossing the aluminum material, the next step is to place the embossed strip to cut off the heat, and then heat the aluminum profile after it is cut off.

[0019] Step 3: In the state of high pressure, use the extrusion knife to remove the air between the two, so that they can be tightly connected,

[0020] Step 4: Place the finished aluminum profile in the electroplating tank to galvanize the aluminum profile with electricity, place it in the spraying machine after completion, and spray the anti-rust fluor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel aluminum profile solid wood veneer gluing process. A material used for manufacturing an aluminum profile is put into a corresponding knurling machine, an arranged knifeedge is used for adjusting out a corresponding knurling type and the interval size, and under the condition that the aluminum profile is constantly heated, the knurling machine is used for showing and pressing out corresponding patterns; and after knurling of the aluminum profile is completed, a knurling strip is placed for heat cutoff, and after heat cutoff of the knurling strip, heating of thealuminum profile is carried out. The novel aluminum profile solid wood veneer gluing process is simple in manufacturing and novel in design, the type and appearance of the aluminum profile can be greatly changed, selectivity of people is greatly improved, practicality and attractiveness can be improved, and the service life of the aluminum profile can be greatly prolonged; and after solid wood glued veneer is damaged, rust prevention of the aluminum profile can be greatly improved, the service life of the aluminum profile is prolonged, the application range is wide, and spreading and popularization are facilitated .

Description

technical field [0001] The invention relates to a novel aluminum profile solid wood veneering process. Background technique [0002] Aluminum profile is a common metal product in daily life, which has many advantages. For example, the density of corrosion-resistant aluminum profile is only 2.7g / cm3, which is about the density of steel, copper or brass (respectively 7.83g / cm3, 8.93g / cm3), 1 / 3 of that, under most environmental conditions, including in air, water (or salt water), petrochemical and many chemical systems, aluminum can show excellent corrosion resistance. Conductivity Aluminum profiles are often chosen due to their excellent conductivity. On the basis of equal weight, the electrical conductivity of aluminum is nearly twice that of copper, and the thermal conductivity of aluminum alloy is about 50-60% of that of copper, which is very important for the manufacture of heat exchangers, evaporators, and heating appliances. , cooking utensils, and automobile cylinder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/00B27D5/00B44C1/24B05D1/02
Inventor 蔡凌雲沈正华陆佳洁殷振超宋一平胡滨宋佳军
Owner 浙江丽尚建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products