Fibrous acrylic resin and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An acrylic resin and fibrous technology, which is applied in the field of oil-absorbing resin, can solve the problems of poor oil-absorbing performance, and achieve the effect of high oil-absorbing efficiency and excellent oil-absorbing performance
Inactive Publication Date: 2018-05-15
CHENGDU JINHUI TECH
View PDF1 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] Existing acrylic oil-absorbing resins have poor oil-absorbing properties
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] A fibrous acrylic resin, comprising the following raw materials in parts by weight:
[0029] Tetrahydrofuryl methacrylate 25 parts
[0030] 15 parts of hydroxyethyl methacrylate
[0031] Cyclohexyl methacrylate 15 parts
[0032] 20 parts of isoamyl alcohol
[0033] 10 parts petroleum ether
[0034] 1 part lauroyl peroxide
[0035] Sodium Lauryl Sulfate 1 part
[0036] 800 parts of deionized water
[0037] Xylene 30 parts
[0038] 30 parts of dimethylacetamide.
Embodiment 2
[0040] A fibrous acrylic resin, comprising the following raw materials in parts by weight:
[0041] Tetrahydrofuryl methacrylate 30 parts
[0042] 20 parts of hydroxyethyl methacrylate
[0043] Cyclohexyl methacrylate 20 parts
[0044] 30 parts of isoamyl alcohol
[0045] 15 parts petroleum ether
[0046] 3 parts lauroyl peroxide
[0047] Sodium Lauryl Sulfate 3 parts
[0048] 1000 parts of deionized water
[0049] Xylene 40 parts
[0050] 40 parts of dimethylacetamide.
Embodiment 3
[0052] A fibrous acrylic resin, comprising the following raw materials in parts by weight:
[0053] Tetrahydrofuryl methacrylate 27 parts
[0054] 17 parts of hydroxyethyl methacrylate
[0055] Cyclohexyl methacrylate 17 parts
[0056] 25 parts of isoamyl alcohol
[0057] 12.5 parts of petroleum ether
[0058] 2 parts lauroyl peroxide
[0059] Sodium Lauryl Sulfate 2 parts
[0060] Deionized water 900 parts
[0061] Xylene 35 parts
[0062] 35 parts of dimethylacetamide.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to fibrous acrylic resin and a preparation method thereof, and belongs to the technical field of oil absorption resins. The acrylic resin comprises the following components in parts by weight: 25-30 parts of tetrahydrofurfuryl methacrylate, 15-20 parts of 2-hydroxyethyl methacrylate, 15-20 parts of cyclohexyl methacrylate, 20-30 parts of 3-methyl-1-butanol, 10-15 parts of petroleum ether, 1-3 parts of dilauroyl peroxide, 1-3 parts of sodium dodecyl sulfate, 800-1000 parts of deionized water, 30-40 parts of xylene, and 30-40 parts of dimethyl acetamide. Tetrahydrofurfurylmethacrylate, 2-hydroxyethyl methacrylate, and cyclohexyl methacrylate are used as main polymerization monomers, and copolymerization technology is used for preparing the acrylic acid oil absorption resins with a certain physical crosslinking structure. Gelation spinning technology is used for preparing the fibrous terpolymeric acrylic resin, and the resin has excellent oil absorption performanceand high oil absorption efficiency.
Description
technical field [0001] The invention relates to an acrylic resin and a preparation method thereof, more specifically, the invention relates to a fibrous acrylic resin and a preparation method thereof, belonging to the technical field of oil-absorbing resins. Background technique [0002] In recent years, there have been more and more research reports on super oil-absorbing resins at home and abroad. The main research direction is how to improve the oil absorption, oil retention rate and obtain a faster oil absorption speed of the resin. For example, some people have introduced the physical crosslinking agent polybutadiene into the copolymers of styrene and lauryl methacrylate, styrene and octyl methacrylate; and some researchers have synthesized octene and isodecyl acrylate Copolymerized oil-absorbing resins; others have studied the preparation and properties of methacrylate oil-absorbing resins, and prepared oil-absorbing fibers by using semi-interpenetrating polymer networ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more