A lithium chromium rechargeable battery and its manufacturing method

A technology for rechargeable batteries and positive poles of batteries, which is applied in the field of lithium chromium rechargeable batteries and its manufacturing, can solve the problems of short service life and low capacity, and achieve the effects of improving cycle life, capacity and high current characteristics

Active Publication Date: 2020-06-02
潘素娇
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] This kind of battery has the characteristics of low cost and long cycle life, but its capacity is too low, only about 100-300mAh / g, and its service life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A lithium chromium rechargeable battery and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] Embodiments of the present invention are described in detail below, examples of which are shown in the drawings, wherein the same or similar reference numerals designate the same or similar elements or elements having the same or similar functions throughout. The embodiments described below by referring to the figures are exemplary and are intended to explain the present invention and should not be construed as limiting the present invention.

[0028] Attached below figure 1 The lithium chromium rechargeable battery according to the embodiment of the present invention is specifically described, including a battery positive electrode 1 , a battery negative electrode 2 and an electrolyte 3 .

[0029] Specifically, the material of the battery positive electrode 1 is lithium chromium oxide; the material of the battery negative electrode 2 is boron oxide or aluminum-nickel alloy; the electrolyte 3 is used to soak the battery positive electrode 1 and the battery negative elec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lithium-chromium rechargeable battery and a manufacturing method thereof. The lithium-chromium rechargeable battery comprises a battery positive electrode made of lithium chromium oxide, a battery negative electrode made of boron oxide or an aluminum-nickel alloy, and fluorine is injected into an electrolytic solution. Thiamine organic solution, on the basis of traditional storage of electrons, also through the synergistic reaction of lithium chromium oxide and boron oxide or aluminum nickel alloy in the electrolyte, lithium chromium oxide performs reversible electrochemical reaction on the surface of boron oxide or aluminum nickel alloy The reaction further stores electrons, thereby greatly increasing the capacity of the battery, and improving the high-current characteristics of the battery, thereby improving the cycle life of the battery.

Description

technical field [0001] The invention relates to the field of batteries, in particular to a lithium-chromium rechargeable battery with high energy density, low self-discharge rate and long cycle life and a manufacturing method thereof. Background technique [0002] At present, energy conservation and emission reduction have become an inevitable requirement for my country's economic and social development. At the same time, future social development still requires high-capacity and long-life rechargeable batteries to support it. For example, consumer electronics, electric vehicles, aerospace and other fields all require high-capacity batteries. [0003] The existing rechargeable nickel ion battery is a rechargeable battery using manganese oxide material as the positive electrode active material, nickel as the negative electrode active material, and an aqueous solution containing nickel ions as the electrolyte. Common rechargeable nickel-ion batteries use manganese dioxide as t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/48H01M4/46H01M4/62H01M10/0566H01M10/052H01M10/058
CPCH01M4/366H01M4/463H01M4/483H01M4/625H01M10/052H01M10/0566H01M10/058Y02E60/10Y02P70/50
Inventor 苏蕊李炳全张增梅
Owner 潘素娇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com