Inorganic particle reinforced alloy material

A technology of inorganic particles and alloy materials, applied in the field of inorganic particles reinforced PC/PET alloys, can solve problems such as poor strength, affecting mechanical properties, etc., and achieve the effects of low cost, excellent electrical properties and processing properties, and good application prospects.

Inactive Publication Date: 2018-06-12
青岛绿谷生物科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since PET is a crystalline polymer and PC is an amorphous polymer, the PC / PET alloy is a typical amorphous / crystalline blend system, and the PC / PET alloys on the market still have poor strength and the blending of the two affects the mechanical properties. performance issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An inorganic particle reinforced PC / PET alloy, the components of which are proportioned by mass percentage: 56% PC, 25% PET, 10% heavy calcium carbonate with a particle size between 10nm and 20μm, 5% compatibilizer, Light stabilizer 2%, titanate coupling agent 0.5%, antioxidant 10100.2%, antioxidant 1680.1%, pentaerythritol stearate (PETS) 1.2%. Wherein, the PC is bisphenol A type aromatic polycarbonate, the weight average molecular weight is 20000-40000g / mol; the PET is polyethylene terephthalate, and its characteristic viscosity is 0.6-1.0dL / g; the compatibilizer is a terpolymer of glycidyl methacrylate (GMA), styrene (St) and acrylonitrile (AN), and the weight percent content of GMA contained in it is 1%~ 5%, and the weight percent content of AN is 25% to 50%; the light stabilizer is a compound of hindered amine high molecular weight light stabilizers GW-944Z and GW-622 with a mass ratio of 1:1.

[0023] Preparation method: (1), dry PC at 110°C-130°C for 3-4 hours ...

Embodiment 2

[0025] An inorganic particle reinforced PC / PET alloy, the composition of which is: 46% PC, 28% PET, 20% talcum powder with a particle size between 10nm and 20μm, 3% compatibilizer, and light-stabilizing Agent 1%, aluminum-titanium composite coupling agent 1%, antioxidant 10760.1%, antioxidant 1680.1%, ethylene bis stearamide (EBS) 0.8%. Wherein, the PC is bisphenol A type aromatic polycarbonate, the weight average molecular weight is 20000-40000g / mol; the PET is polyethylene terephthalate, and its characteristic viscosity is 0.6-1.0dL / g; the compatibilizer is a terpolymer of glycidyl methacrylate (GMA), styrene (St) and acrylonitrile (AN), and the weight percent content of GMA contained in it is 1%~ 5%, and the weight percent content of AN is 25% to 50%; the light stabilizer is a compound of hindered amine high molecular weight light stabilizers GW-944Z and GW-622 with a mass ratio of 1:1.

[0026] Preparation method: (1), dry PC at 110°C-130°C for 3-4 hours in a blower drye...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an inorganic particle reinforced PC / PET alloy. The alloy comprises the following components in percentages by weight: 40% to 60% of PC, 5% to 30% of PET, 10% to 20% of inorganic particles, 2% to 5% of a compatilizer, 0.5% to 2% of a light stabilizer, 0.5% to 1% of a coupling agent, 0.1% to 0.5% of a main antioxidant, 0.1% to 0.5% of an auxiliary antioxidant and 0.5% to 2% of a lubricating agent. The inorganic particle reinforced PC / PET alloy has the beneficial effects that, compared with the prior art, the alloy has advantages of PC and PET, the defects of a single component on the performance are compensated, the alloy also has the characteristics of high strength, high rigidity, high heat resistance, high corrosion resistance, high weather resistance, excellent electrical performance and processability and the like, and the cost is also relatively low, so that the alloy has excellent application prospects in the fields of automobile industry, electric products, mechanical parts and buildings.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an inorganic particle reinforced PC / PET alloy. Background technique [0002] Polycarbonate (PC) is an engineering plastic with excellent performance. It has the advantages of high impact strength, creep resistance, good dimensional stability, heat resistance, transparency, and excellent dielectric properties. However, PC has high melt viscosity and poor fluidity. Poor solvent resistance, especially poor resistance to organic solvents and alkaline drugs, prone to stress cracking and swelling in solvents and alkaline environments, and sensitive to notches. Polyethylene terephthalate (PET) is a translucent crystalline thermoplastic polyester with high heat resistance, toughness, fatigue resistance, self-lubrication, low coefficient of friction, weather resistance, and is still Maintain various physical properties (including electrical properties), resist hot water, alkali...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08K13/06C08K9/04C08K3/26C08K3/34
CPCC08L69/00C08K2201/003C08L2201/08C08L2205/03C08L67/02C08K13/06C08K9/04C08K2003/265C08K3/34
Inventor 丁磊
Owner 青岛绿谷生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products