Inorganic particle reinforced alloy material

A technology of inorganic particles and alloy materials, which is applied in the field of inorganic particle reinforced PC/PET alloys, can solve problems affecting mechanical properties and poor strength, and achieve excellent electrical properties and processing properties, low cost, and excellent heat and corrosion resistance Effect

Inactive Publication Date: 2017-05-31
格润德(青岛)新型环保建材有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since PET is a crystalline polymer and PC is an amorphous polymer, the PC / PET alloy is a typical amorphous / crystalline blend system, and the PC / PET alloys on the market still have poor strength and the blending of the two affects the mechanical properties. performance issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An inorganic particle reinforced PC / PET alloy, the components of which are proportioned by mass percentage: 56% PC, 25% PET, 10% heavy calcium carbonate with a particle size between 10nm and 20μm, 5% compatibilizer, Light stabilizer 2%, titanate coupling agent 0.5%, antioxidant 1010 0.2%, antioxidant 168 0.1%, pentaerythritol stearate (PETS) 1.2%. Wherein, the PC is bisphenol A type aromatic polycarbonate, the weight average molecular weight is 20000-40000g / mol; the PET is polyethylene terephthalate, and its characteristic viscosity is 0.6-1.0dL / g; the compatibilizer is a terpolymer of glycidyl methacrylate (GMA), styrene (St) and acrylonitrile (AN), and the weight percent content of GMA contained in it is 1%~ 5%, and the weight percent content of AN is 25% to 50%; the light stabilizer is a compound of hindered amine high molecular weight light stabilizers GW-944Z and GW-622 with a mass ratio of 1:1.

[0023] Preparation method: (1), dry PC at 110°C-130°C for 3-4 hour...

Embodiment 2

[0025] An inorganic particle reinforced PC / PET alloy, the composition of which is: 46% PC, 28% PET, 20% talcum powder with a particle size between 10nm and 20μm, 3% compatibilizer, and light-stabilizing Agent 1%, aluminum titanium composite coupling agent 1%, antioxidant 1076 0.1%, antioxidant 168 0.1%, ethylene bis stearamide (EBS) 0.8%. Wherein, the PC is bisphenol A type aromatic polycarbonate, the weight average molecular weight is 20000-40000g / mol; the PET is polyethylene terephthalate, and its characteristic viscosity is 0.6-1.0dL / g; the compatibilizer is a terpolymer of glycidyl methacrylate (GMA), styrene (St) and acrylonitrile (AN), and the weight percent content of GMA contained in it is 1%~ 5%, and the weight percent content of AN is 25% to 50%; the light stabilizer is a compound of hindered amine high molecular weight light stabilizers GW-944Z and GW-622 with a mass ratio of 1:1.

[0026] Preparation method: (1), dry PC at 110°C-130°C for 3-4 hours in a blower dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Weight average molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic particle reinforced PC / PET alloy, which comprises the following components by mass percentage: 40%-60% of PC, 5%-30% of PET, 10%-20% of inorganic particles, 2%-5% of a compatibilizer, 0.5%-2% of a light stabilizer, 0.5%-1% of a coupling agent, 0.1%-0.5% of a main antioxidant, 0.1%-0.5% of an auxiliary antioxidant, and 0.5%-2% of a lubricant. Compared with the prior art, the inorganic particle reinforced PC / PET alloy prepared by the invention not only has the respective advantages of PC and PET, makes up for the performance defects of single component, but also has the advantages of high strength, good rigidity, excellent heat resistance and corrosion resistance, good weatherability, excellent electrical properties and processability, etc., and is low in cost, thereby having very good application prospects in automobile industry, electronic appliances, mechanical parts, building and other fields.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an inorganic particle reinforced PC / PET alloy. Background technique [0002] Polycarbonate (PC) is an engineering plastic with excellent performance. It has the advantages of high impact strength, creep resistance, good dimensional stability, heat resistance, transparency, and excellent dielectric properties. However, PC has high melt viscosity and poor fluidity. Poor solvent resistance, especially poor resistance to organic solvents and alkaline drugs, prone to stress cracking and swelling in solvents and alkaline environments, and sensitive to notches. Polyethylene terephthalate (PET) is a translucent crystalline thermoplastic polyester with high heat resistance, toughness, fatigue resistance, self-lubrication, low coefficient of friction, weather resistance, and is still Maintain various physical properties (including electrical properties), resist hot water, alkali...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L67/02C08L25/14C08K13/02C08K3/36C08K3/22C08K3/34C08K3/26C08K5/134
Inventor 黄亚楠
Owner 格润德(青岛)新型环保建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap