Method of preparing semi-chemical pulp with broadleaf wood slab
A semi-chemical pulp and wood board technology, applied in pulp beating method, fiber dispersant addition, paper and other directions, can solve the problems of strict requirements on reaction conditions, increase the difficulty of wastewater treatment, unfavorable clean production, etc., achieve rich raw materials, reagents Clean and free from contamination, lax specifications and quality requirements
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0030] The method that present embodiment provides is that raw material prepares semi-chemical pulp with hardwood bark, comprises the steps:
[0031] (1) Pretreatment step: take the hardwood veneer as raw material, add ethanol aqueous solution and hydrolysis aid to form a cooking liquid; the cooking liquid is heated up to 160°C and kept for 120 minutes; the weight of the hydrolysis aid accounts for 3% by weight, the hydrolysis aid consists of NaOH and H 2 o 2 Composition, NaOH and H in the hydrolysis aid 2 o 2 The mass ratio of is 1.2:1; The volume fraction that ethanol accounts for in the ethanol aqueous solution is 40% in the pretreatment step; The weight of described ethanol aqueous solution is 6 times of hardwood bark weight;
[0032] (2) Refining step: the hardwood boards through the pretreatment step are directly refined without washing; in the refining step, a high-consistency refiner is used to perform two-stage refining operations, and the first stage refining gap ...
Embodiment 2
[0035] The difference between this embodiment and Example 1 is that the hydrolysis aid weight accounts for 3% of the hardwood board skin weight, and the hydrolysis aid consists of NaOH and H 2 o 2 It is composed according to the mass ratio of 1.2:1, the liquid ratio is 1:8, the volume concentration of ethanol in the ethanol aqueous solution is 60%, the cooking temperature is 160°C, and the heat preservation is 120 minutes. In the beating step, beating to beating degree is 28 o Sr.
Embodiment 3
[0037] The difference between this embodiment and Example 1 is that in the pretreatment step: the weight of the hydrolysis aid accounts for 5% of the weight of the hardwood board bark, and the aid is composed of NaOH and H 2 o 2 The composition is based on a weight ratio of 1.2:1, a liquid ratio of 1:6, a volume concentration of ethanol in an ethanol aqueous solution of 40%, a maximum cooking temperature of 160°C, and a heat preservation time of 180 minutes.
[0038] In the refining step, the refining concentration is 25%, and beating to a degree of beating in the beating step is 30% o Sr.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com