Diatomite wallpaper with long-acting heat preservation and temperature adjustment and preparation method

A diatomite and wallpaper technology, applied in chemical instruments and methods, household appliances, other household appliances, etc., can solve the problems of easy leakage of phase change materials, poor debugging and thermal insulation effect, and weak bonding, etc., to improve the moisturizing effect. Temperature effect, low production cost, good product performance

Inactive Publication Date: 2018-07-10
CHENDU NEW KELI CHEM SCI CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Aiming at the problems of poor dispersibility, easy agglomeration, weak bonding, easy leakage of phase change materials, and poor thermal insulation effect of debugging in diatomite temperature-regulating wallpapers that are widely used at present, the present invention proposes a long-term thermal insulation and temperature-regulating wallpaper. The diatomite wallpaper and its preparation method effectively improve the moisturizing and temperature-regulating effect of the diatomite temperature-regulating wallpaper. At the same time, the diatomite is evenly dispersed, and the product performance is good and the effect is long-lasting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The preparation process is:

[0037] (1) Add dry diatomaceous earth and phase change material into the mixer, heat and stir, so that the phase change material turns into a liquid, wets and covers the surface of diatomite; the mixer is a ribbon type stirring device;

[0038] (2) Stop stirring, and slowly increase the pressure in the agitator under the ultrasonic environment, so that the liquid phase change material is poured into the micropores of diatomite, and the material is discharged after slow cooling to obtain the diatomite phase change material; The ultrasonic environment is generated by an ultrasonic generator with a power of 200W, and the ultrasonic frequency is 60kHz; the pressure increase rate in the stirrer is 70kPa / min, the final pressure is 9MPa, and the maintenance time is 4min; ammonia refrigerant is used for cooling, and the cooling rate is 4°C / min;

[0039] (3) Add the diatomite phase change material prepared in step (2) into methyl methacrylate, th...

Embodiment 2

[0043] The preparation process is:

[0044](1) Add dry diatomite and phase-change material into the mixer, heat and stir, so that the phase-change material turns into a liquid, wets and covers the surface of diatomite; the mixer is a screw-type mixer ;

[0045] (2) Stop stirring, and slowly increase the pressure in the agitator under the ultrasonic environment, so that the liquid phase change material is poured into the micropores of diatomite, and the material is discharged after slow cooling to obtain the diatomite phase change material; The ultrasonic environment is generated by an ultrasonic generator with a power of 100W, and the ultrasonic frequency is 40kHz; the pressure increase rate in the stirrer is 50kPa / min, the final pressure is 8MPa, and the maintenance time is 5min; methylamine refrigerant is used for cooling, and the cooling rate is 3°C / min;

[0046] (3) Add the diatomite phase change material prepared in step (2) into methyl methacrylate, then add foaming ag...

Embodiment 3

[0049] The preparation process is:

[0050] (1) Add dry diatomite and phase-change material into the mixer, heat and stir, so that the phase-change material turns into a liquid, wets and covers the surface of diatomite; the mixer is a propulsion mixer ;

[0051] (2) Stop stirring, and slowly increase the pressure in the agitator under the ultrasonic environment, so that the liquid phase change material is poured into the micropores of diatomite, and the material is discharged after slow cooling to obtain the diatomite phase change material; The ultrasonic environment is generated by an ultrasonic generator with a power of 300W, and the ultrasonic frequency is 80kHz; the pressure increase rate in the stirrer is 100kPa / min, the final pressure is 10MPa, and the maintenance time is 3min; sulfur dioxide refrigerant is used for cooling, and the cooling rate is 6°C / min;

[0052] (3) Add the diatomite phase change material prepared in step (2) into methyl methacrylate, then add foa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides diatomite wallpaper with long-acting heat preservation and temperature adjustment and a preparation method. Diatomite and a phase-change material are heated and stirred to moisten the phase-change material, and the diatomite is coated with the phase-change material; pressure is increased in the ultrasonic environment, the diatomite phase-change material is obtained after cooling and discharging, and the diatomite phase-change material is added into methyl methacrylate; a microporous composite phase-change material is prepared by radiation under the action of an initiatorand a blowing agent, and coated between two layers of polyvinyl chloride films, and diatomite composite wallpaper is prepared after hot-pressing. The composite phase-change material is coated by polymer, and is subjected to the hot-pressing to be firmly fixed on a base material, so that the problem of leakage of the phase-change material is solved, and the diatomite has good dispersity, good ability of temperature adjustment and humidity adjustment and long-acting heat preservation effect; and the whole preparation process is simple, easy operation is achieved, a raw material is easy to obtain, the production cost is low, and the diatomite wallpaper with the long-acting heat preservation and temperature adjustment can be industrialized and popularized.

Description

technical field [0001] The invention relates to the field of wallpaper preparation, in particular to a wallpaper with thermal insulation and temperature regulation functions, in particular to a diatomite wallpaper with long-term thermal insulation and temperature regulation and a preparation method. Background technique [0002] With the popularization of home decoration, people's requirements for wall decoration are not limited to paint products, but more and more wallpaper products with various patterns and exquisite patterns are used. As the name implies, wallpaper is a wall decoration material made of paper material as the base material, polyvinyl chloride, fiber and paper material as the surface coating, and a series of processes. It has various colors, rich patterns, and luxurious style. , Safety and environmental protection, convenient construction, affordable price and many other incomparable characteristics of other interior decoration materials, the application is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/00B32B37/06B32B37/10C08F120/14C08F2/44C08K3/34
CPCE04F13/002B32B37/06B32B37/10B32B2037/243B32B2255/10B32B2307/304B32B2607/02C08F2/44C08F120/14C08K3/346
Inventor 陈庆曾军堂
Owner CHENDU NEW KELI CHEM SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com