Formaldehyde-free plywood preparation process

A preparation process and technology of plywood, applied in the field of plywood manufacturing, can solve the problems of easy cracking of plywood, uneven bonding strength, poor quality of the board, etc., and achieve the effect of stable pressure, sufficient and uniform pressure, and good stability

Active Publication Date: 2018-08-10
广西协力合板有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the improvement of people's living standards, people's awareness of health and environmental protection is becoming stronger and stronger, and the desire for formaldehyde-free decorative materials in interior decoration is also more urgent. At present, the decorative panels on the market are mainly E1 and E0 grades. Mainly, it has been unable to meet people's needs for high-quality life, and the appearance of formaldehyde-free plywood provides protection for people's health
However, based on the formaldehyde-free plywood, especially when water-based polyurethane is used as the adhesive, the quality of the board obtained by using the traditional processing technology is poor, mainly reflected in defects such as uneven bonding strength, easy cracking and deformation of the plywood, and poor stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0029] Formaldehyde-free plywood preparation process, its process steps include:

[0030] (1) Single board manufacturing

[0031] The processing requires the surface of the veneer to be smooth, without large burrs, basically without dead joints, and uniform in thickness; the veneer is assembled into a 4x8 feet format by a veneer. Then enter the veneer atomization and water addition step; the veneer atomization and water addition step is to spread the veneer on the conveyor belt, atomize the water and spray the veneer, and adjust the amount of spraying or the speed of the conveyor belt to ensure After standing still, the moisture content inside and outside of the veneer is between 19-20%.

[0032] (2) Compounding

[0033] The water-based polyurethane mixture is prepared by mixing the water-based polyurethane and the curing agent at a ratio of 8:1. Of course, this embodiment can also be obtained by mixing the water-based polyurethane and the curing agent at a ratio of 9:1.5. ...

specific Embodiment 2

[0055] Formaldehyde-free plywood preparation process, its process steps include:

[0056] (1) Single board manufacturing

[0057] The processing requires the surface of the veneer to be smooth, without large burrs, basically without dead joints, and uniform in thickness; the veneer is assembled into a 4x8 feet format by a veneer. Then enter the veneer atomization and water addition step; the veneer atomization and water addition step is to spread the veneer on the conveyor belt, atomize the water and spray the veneer, and adjust the amount of spraying or the speed of the conveyor belt to ensure After standing still, the moisture content inside and outside of the veneer is between 18-22%.

[0058] (2) Compounding

[0059]Prepare water-based polyurethane mixture by mixing water-based polyurethane and curing agent in a ratio of 8:2.

[0060] (three) sizing, tissue embryo

[0061] Apply double-sided glue to the veneer that needs to be glued, and the total amount of double-side...

specific Embodiment 3

[0081] Formaldehyde-free plywood preparation process, its process steps include:

[0082] (1) Single board manufacturing

[0083] The processing requires the surface of the veneer to be smooth, without large burrs, basically without dead joints, and uniform in thickness; the veneer is assembled into a 4x8 feet format by a veneer. Then enter the veneer atomization and water addition step; the veneer atomization and water addition step is to spread the veneer on the conveyor belt, atomize the water and spray the veneer, and adjust the amount of spraying or the speed of the conveyor belt to ensure After standing still, the moisture content inside and outside of the veneer is between 20-22%.

[0084] (three) with glue

[0085] Prepare water-based polyurethane mixture by mixing water-based polyurethane and curing agent at a ratio of 9:1. Of course, this embodiment can also be obtained by mixing water-based polyurethane and curing agent at a ratio of 9:2, and the effect is better....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formaldehyde-free plywood preparation process. The formaldehyde-free plywood preparation process comprises single-plate manufacturing, glue preparation, sizing, assembling, cold pressing and aftertreatment. After the cold pressing procedure is carried out, the step of a hot pressing procedure is further needed, and a waterborne polyurethane mixing agent is adopted as an adhesive composition in the sizing procedure. The formaldehyde-free plywood preparation process is suitable for adopting waterborne polyurethane, and plywood is good in bonding strength, even in plateblank thickness, not likely to deform and good in stability.

Description

technical field [0001] The invention relates to the technical field of plywood manufacture, in particular to a preparation process of formaldehyde-free plywood. Background technique [0002] The adhesives currently used in plywood production mainly include urea-formaldehyde resin adhesives, phenolic resin adhesives and melamine-modified urea-formaldehyde resin adhesives. These kinds of adhesives are all aldehyde adhesives, and the most prominent problem is that the released formaldehyde is harmful to the human body. With the improvement of people's living standards, people's awareness of health and environmental protection is becoming stronger and stronger, and the desire for formaldehyde-free decorative materials in interior decoration is also more urgent. At present, the decorative panels on the market are mainly E1 and E0 grades. Mainly, it has been unable to meet people's needs for high-quality life, and the appearance of formaldehyde-free plywood provides protection fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/04B27D1/08B27G11/00C09J175/04
CPCB27D1/04B27D1/08B27G11/00C09J175/04
Inventor 黄文煜宋磊
Owner 广西协力合板有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap