Crease-resistant and anti-mite fabric finishing method

A technology for fabric finishing and anti-wrinkle finishing, applied in fiber treatment, plant fiber, biochemical fiber treatment, etc., to achieve good aldehyde-free environmental protection, good anti-mite and bactericidal ability, and safe wearing effect

Inactive Publication Date: 2018-08-17
佛山慧创正元新材料科技有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Today, with the improvement of people's living standards and the development of textile culture, it has become fashionable to pursue the beauty, comfort, health care, and even functionality of textiles. However, existing fabrics, especially bed sheets and quilt covers, cannot effectively prevent the invasion of microorganisms such as mites. Breeding, which in turn affects people's normal daily life to a certain extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: a kind of anti-wrinkle and anti-mite fabric finishing method, it comprises the following steps:

[0017] (1) Preparation of anti-wrinkle finishing solution: prepare the following raw materials in parts by weight respectively, 25 parts of hydrophilic amino silicone oil, 15 parts of alkylphenol polyoxyethylene ether, 8 parts of sodium alkylbenzene sulfonate, 2 parts of sodium bicarbonate 1 part of acrylic acid, 2 parts of triethanolamine borate, 5 parts of sodium hypophosphite, 12 parts of ethanol, 115 parts of deionized water, mix the above raw materials evenly at 50-70 ° C, and after cooling, it will be an anti-wrinkle finishing solution;

[0018] (2) Preparation of anti-mite finishing solution: prepare the following raw materials in parts by weight respectively, 12 parts of thymol, 20 parts of water-soluble chitosan quaternary ammonium salt, 8 parts of sodium polyacrylate, 2 parts of sodium sulfate, methyl 3 parts of n-nonyl ketone, 100 parts of deionized...

Embodiment 2

[0022] Embodiment 2: a kind of anti-wrinkle anti-mite fabric finishing method, it comprises the following steps:

[0023] (1) Preparation of anti-wrinkle finishing solution: prepare the following raw materials in parts by weight respectively, 20 parts of hydrophilic amino silicone oil, 12 parts of alkylphenol polyoxyethylene ether, 5 parts of sodium alkylbenzene sulfonate, 1 part of sodium bicarbonate 1 part, 0.5 part of acrylic acid, 1 part of triethanolamine borate, 3 parts of sodium hypophosphite, 10 parts of ethanol, 100 parts of deionized water, mix the above raw materials at 50 ℃, and the anti-wrinkle finishing solution after cooling;

[0024] (2) Preparation of anti-mite finishing solution: prepare the following raw materials in parts by weight respectively, 10 parts of thymol, 15 parts of water-soluble chitosan quaternary ammonium salt, 5 parts of sodium polyacrylate, 1 part of sodium sulfate, methyl 2 parts of n-nonyl ketone, 80 parts of deionized water, fully mix the...

Embodiment 3

[0028] Embodiment 3: a kind of anti-wrinkle anti-mite fabric finishing method, it comprises the following steps:

[0029] (1) Preparation of anti-wrinkle finishing solution: prepare the following raw materials in parts by weight respectively, 30 parts of hydrophilic amino silicone oil, 18 parts of alkylphenol polyoxyethylene ether, 10 parts of sodium alkylbenzene sulfonate, 3 parts of sodium bicarbonate 1.5 parts of acrylic acid, 3 parts of triethanolamine borate, 6 parts of sodium hypophosphite, 15 parts of ethanol, and 130 parts of deionized water. Mix the above raw materials evenly at 70 ° C, and the anti-wrinkle finishing solution is obtained after cooling;

[0030] (2) Preparation of anti-mite finishing solution: prepare the following raw materials in parts by weight respectively, 15 parts of thymol, 25 parts of water-soluble chitosan quaternary ammonium salt, 10 parts of sodium polyacrylate, 3 parts of sodium sulfate, methyl 4 parts of n-nonyl ketone, 120 parts of deioni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a crease-resistant and anti-mite fabric finishing method. The crease-resistant and anti-mite fabric finishing method comprises the following steps: preparing crease-resistant finishing liquid; preparing anti-mite finishing liquid; taking cotton ramie fabric, immersing pure cotton fabric into the crease-resistant finishing liquid, soaking at 50 DEG C for 0.5 to 2 hours, performing twice soaking and twice rolling, and drying at 85 DEG C, wherein the rolling over rate is 65 to 85 percent; soaking the dried fabric into the anti-mite finishing liquid to perform once soakingand once rolling, and drying at 100 DEG C to obtain the finished fabric, wherein the soaking and rolling liquid level is 70 percent and the rolling over rate is 70 to 80 percent. The crease-resistantand anti-mite fabric finishing method provided by the invention has high formaldehyde-free environmental friendliness and is safe and healthy to wear; in the fabric finished by the finishing method, the dry and wet crease recovery angle is increased by 30 percent or more, and the crease recover angle is basically unchanged after the fabric is washed with soap for 40 times; and the fabric finishedby the finishing method has high anti-mite and bactericidal abilities, is safe, does not have residues and has natural plant odor, and the mite repelling rate of the fabric is up to 90 percent or more.

Description

technical field [0001] The invention relates to the field of textile material finishing methods, in particular to an anti-wrinkle and anti-mite finishing method for cotton and linen fabrics with excellent environmental protection. Background technique [0002] Traditional cotton fabric anti-wrinkle finishing agents N2 methylol amide compounds, cyclic urea methylol derivatives, etc., such finishing agents have good anti-wrinkle effects and are widely used, but they will release a large amount of free formaldehyde during fabric finishing and storage , endangering human health and safety. In the prior art, novel cotton fabric cross-linking anti-wrinkle and anti-shrinkage finishing agents are polycarboxylic acids, wherein 1,2,3,4-butanetetracarboxylic acid (BTCA) and citric acid (CA) are the most researched, and this type of finishing agent Although the treated cotton fabric did not release formaldehyde, the tear strength of the fabric decreased significantly after finishing. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/56D06M11/70D06M13/127D06M13/203D06M13/256D06M15/03D06M15/263D06M15/53D06M15/643D06M101/06
CPCD06M11/56D06M11/70D06M13/127D06M13/203D06M13/256D06M15/03D06M15/263D06M15/53D06M15/6436D06M16/00D06M2101/06D06M2200/20
Inventor 胡玲
Owner 佛山慧创正元新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap