Steel slag-diatomite composite rubber filling material with reinforcing and flame-retarding synergistic performance

A technology of composite rubber and diatomite, which is applied in the field of recycling of solid waste resources, can solve the problems of single function, poor compatibility, high price of filler carbon black and white carbon black, etc., so as to promote efficiency, improve mechanical properties and resistance Combustibility performance, realize the effect of recycling

Active Publication Date: 2018-08-31
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the high price and single function of the main filler carbon black and silica in the existing rubber industry, steel slag and diatomite are easily agglomerated when directly added to rubber, and the interaction between the steel slag-diatomite inorganic interface and the rubber organic interface To solve the problem of poor capacity, the present invention provides a steel slag-diatomite composite rubber filler with synergistic properties of reinforcement and flame retardancy, in order to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel slag-diatomite composite rubber filling material with reinforcing and flame-retarding synergistic performance
  • Steel slag-diatomite composite rubber filling material with reinforcing and flame-retarding synergistic performance
  • Steel slag-diatomite composite rubber filling material with reinforcing and flame-retarding synergistic performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Taking the preparation of product 100g of the present invention as an example, the components used and their mass proportions are:

[0022]

[0023] The water is deionized water; the silane coupling agent is industrially pure; the steel slag is hot metal desulfurization tailings, and its particle size is 5.6 μm to 110.4 μm; the diatomite, its particle size is 7.8 μm ~38.2 μm.

[0024] First, mix water and silane coupling agent, and use an ultrasonic disperser to disperse it for 10 minutes to obtain a silane coupling agent solution; then mix steel slag and diatomaceous earth, and use a constant temperature magnetic stirrer to dry it under airtight conditions at room temperature Stir for 10 hours to obtain a steel slag-diatomite mixture; finally mix the steel slag-diatomite mixture with the silane coupling agent solution, and use a constant temperature magnetic stirrer to stir for 4 hours at a stirring temperature of 60°C to obtain a steel slag-diatomite composite Rub...

Embodiment 2

[0026] Taking the preparation of product 100g of the present invention as an example, the components used and their mass proportions are:

[0027]

[0028] The water is deionized water; the silane coupling agent is industrially pure; the steel slag is casting slag with a particle size of 5.4 μm to 104.5 μm; the diatomite has a particle size of 5.9 μm to 40.2 μm μm.

[0029] First, mix water and silane coupling agent, and use an ultrasonic disperser to disperse it for 30 minutes to obtain a silane coupling agent solution; then mix steel slag and diatomaceous earth, and use a constant temperature magnetic stirrer to process it under airtight conditions at room temperature Stir for 6 hours to obtain a steel slag-diatomite mixture; finally mix the steel slag-diatomite mixture with the silane coupling agent solution, and use a constant temperature magnetic stirrer to stir for 2 hours at a stirring temperature of 80°C to obtain a steel slag-diatomite composite Rubber filler.

Embodiment 3

[0031] Taking the preparation of product 100g of the present invention as an example, the components used and their mass proportions are:

[0032]

[0033]

[0034] The water is deionized water; the silane coupling agent is industrially pure; the steel slag is converter hot slag with a particle size of 2.9 μm to 92.4 μm; the diatomite has a particle size of 6.3 μm to 41.5 μm.

[0035] First, mix water and silane coupling agent, and use an ultrasonic disperser to disperse it for 20 minutes to obtain a silane coupling agent solution; then mix steel slag and diatomaceous earth, and use a constant temperature magnetic stirrer to process it under airtight conditions at room temperature Stir for 12 hours to obtain a steel slag-diatomite mixture; finally mix the steel slag-diatomite mixture with the silane coupling agent solution, and use a constant temperature magnetic stirrer to stir for 3 hours at a stirring temperature of 50°C to obtain a steel slag-diatomite composite Rub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a steel slag-diatomite composite rubber filling material with reinforcing and flame-retarding synergistic performance, belonging to the field of cyclic utilization of solid waste resources. The filling material comprises water, a silane coupling agent, steel slag, and diatomite. The preparation method for the filling material comprises the following concrete steps: mixing the water and the silane coupling agent, and carrying out dispersing so as to obtain a silane coupling agent solution; then mixing the steel slag and the diatomite, and carrying out stirring so as to obtain a steel slag-diatomite mixture; mixing the steel slag-diatomite mixture and the silane coupling agent solution, and carrying out stirring so as to obtain the steel slag-diatomite composite rubber filling material. The steel slag-diatomite composite rubber filling material provided by the invention solves the problems of high price and single function of main filling materials of carbon blackand white carbon black in the rubber industry, improves mechanical properties and flame retardancy of rubber, realizes cyclic utilization of industrial wastes, promotes efficiency of metallurgical enterprises, reduces the cost of the rubber product industry, and meets the requirements of current industrial development for energy conservation, environmental protection and cyclic economy.

Description

technical field [0001] The invention belongs to the field of recycling of solid waste resources, and in particular relates to a steel slag-diatomite composite rubber filler with reinforcing-flame-retardant synergistic performance and a preparation method thereof. Background technique [0002] Steel slag is solid waste produced in the steelmaking process, accounting for about 15% to 20% of steelmaking output. Steel slag is mainly composed of oxides of calcium, iron, silicon, magnesium and a small amount of aluminum, manganese, phosphorus, etc., that is, SiO 2 , Fe 2 o 3 、Al 2 o 3 , ZnO, CaO, MgO, P 2 o 5 , MnO, SO 3 etc., also contains free calcium oxide and metallic iron. Diatomaceous earth is a siliceous rock whose main chemical composition is SiO 2 , due to the high impurity content, it cannot be used directly and requires deep processing. At present, a large amount of steel slag and diatomite are stockpiled, which not only takes up valuable land, but also pollut...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08K7/26C08K11/00C08K5/54C08L9/06C08K13/08
CPCC08K5/54C08K7/26C08K11/005C08K13/08C08K2201/003C08L2201/02C08L9/06Y02P20/10
Inventor 张浩王凯祥龙红明张欣雨唐刚刘秀玉
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap