Efficient denitration catalyst and preparation method thereof

A denitrification catalyst and high-efficiency technology, applied in the field of catalysis, can solve the problems of narrow reaction temperature window and poor low-temperature activity, and achieve the effects of uniform dispersion of acid sites, inhibition of sulfation, and improvement of anti-poisoning performance

Active Publication Date: 2018-09-04
ZHEJIANG ZHIYUAN ENVIRONMENTAL TECH CO LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently commercially available V 2 o 5 -WO 3 (MoO 3 )/TiO 2 Although the catalyst is very mature, it still has a narrow reaction temperature window, poor ac

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1) Preparation of Sn-modified MCM-48 molecular sieve carrier:

[0026] The template agent used in the preparation process is CTAB; SnCl 4 As the Sn source, TEOS as the Si source; according to the molar ratio n SiO2 :n SnCl4 :n KOH :n CTAB :n H2O :n 乙醇 =1.0:0.1:0.24:0.1:30:30, weigh a certain amount of TEOS and dissolve it in aqueous ethanol, and mix it with CTAB and SnCl 4 The aqueous solution was mixed and stirred, and potassium hydroxide was added after 30 minutes to continue stirring for 20 minutes, and finally the mixture was packed into a hydrothermal reaction kettle at 150 o C crystallization treatment 36h, take out and cool, then place it in 30%H 2 o 2 Stand in the middle for 12h, then filter with suction, wash until neutral, and then put o C treatment for 12h, finally at 550 o C roasting treatment 5h obtains the MCM-48 molecular sieve carrier of Sn modification;

[0027] 2) Preparation of PO 4 3- -SO 4 2- / Sn-MCM-48

[0028]Weigh 5g of Sn-modifie...

Embodiment 2

[0032] 1) Preparation of Sn-modified MCM-48 molecular sieve carrier:

[0033] The template agent used in the preparation process is CTAB; SnCl 4 As the Sn source, TEOS as the Si source; according to the molar ratio n SiO2 :n SnCl4 :n KOH :n CTAB :n H2O :n 乙醇 =1.0:0.3:0.24:0.2:30:30, weigh a certain amount of TEOS and dissolve it in aqueous ethanol, and mix it with CTAB and SnCl 4 The aqueous solution was mixed and stirred, and potassium hydroxide was added after 30 minutes to continue stirring for 20 minutes, and finally the mixture was put into a hydrothermal reaction kettle at 180 o C crystallization treatment for 24 hours, take it out and cool it, then place it in 30% H 2 o 2 Stand in the middle for 12h, then filter with suction, wash until neutral, and then put o C treatment for 12h, finally at 550 o C roasting treatment 5h obtains the MCM-48 molecular sieve carrier of Sn modification;

[0034] 2) Preparation of PO 4 3- -SO 4 2- / Sn-MCM-48

[0035] Weigh 5g...

Embodiment 3

[0039] 1) Preparation of Sn-modified MCM-48 molecular sieve carrier:

[0040] The template agent used in the preparation process is CTAB; SnCl 4 As the Sn source, TEOS as the Si source; according to the molar ratio n SiO2 :n SnCl4 :n KOH :n CTAB :n H2O :n 乙醇 =1.0:0.2:0.24:0.15:30:30, weigh a certain amount of TEOS and dissolve it in aqueous ethanol, and mix it with CTAB and SnCl 4 The aqueous solution was mixed and stirred, and potassium hydroxide was added after 30 minutes to continue stirring for 20 minutes, and finally the mixture was put into a hydrothermal reaction kettle at 165 o C crystallization treatment 30h, take out and cool, then place it in 30%H 2 o 2 Stand in the middle for 12h, then filter with suction, wash until neutral, and then put o C treatment for 12h, finally at 550 o C roasting treatment 5h obtains the MCM-48 molecular sieve carrier of Sn modification;

[0041] 2) Preparation of PO 4 3- -SO 4 2- / Sn-MCM-48

[0042] Weigh 5g of Sn-modified...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an efficient denitration catalyst and a preparation method thereof. A hydrothermal method and a sol impregnation method are adopted for combined treatment; an Sn-containing MCM-48 molecular sieve in a skeleton serves as a carrier; the Sn-containing MCM-48 molecular sieve is subjected to SO4<2-> and PO4<3-> modification by a mixed solution which is obtained by mixing deionized water, sulfuric acid with the mass concentration of 98 percent and phosphoric acid with the mass concentration of 85 percent by weight, thereby obtaining the novel denitration catalyst taking Fe asan active component. The denitration catalyst prepared with the preparation method has relatively high specific surface area, and can have high catalytic activity and SO2 poisoning resistance withinthe range of 200 to 450 DEG C.

Description

technical field [0001] The technical field of catalysis of the present invention relates to a denitration catalyst, in particular to a high-efficiency denitration catalyst and a preparation method thereof. Background technique [0002] In recent years, with the continuous advancement of my country's industrialization and urbanization process, the use of fossil energy and resource consumption have continued to increase, the situation of air pollution has further deteriorated, regional air pollution continues to intensify, and the emission of multiple pollutants ranks among the top in the world. Among many pollutants, nitrogen oxides (NO x ) is one of the typical air pollutants in my country, and a large amount of NO is emitted into the atmosphere x It will lead to a series of air pollution problems, such as acid rain formed by gas phase reaction, greenhouse effect caused by hydrocarbons, photochemical smog and smog caused by light; at the same time, it also endangers human h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J29/03B01J33/00B01J37/02B01J37/10B01D53/86B01D53/56
CPCB01D53/8628B01D2255/2094B01D2255/50B01J29/0333B01J33/00B01J35/0073B01J37/0201B01J37/10B01J2229/18B01J2229/183
Inventor 李俊霞
Owner ZHEJIANG ZHIYUAN ENVIRONMENTAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap