A kind of epoxy resin/cement mortar composite concrete material and preparation method thereof

A technology of epoxy resin and cement mortar, which is applied in the field of road material preparation, can solve the problems of poor durability, poor comprehensive performance of semi-flexible pavement, thermal construction period, etc., and achieve reasonable gravel gradation, excellent mechanical properties and process performance , Improve the effect of impact resistance and crack resistance

Active Publication Date: 2021-03-16
山西交通科学研究院集团有限公司 +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the shortcomings of semi-flexible pavement, the present invention provides an epoxy resin / cement mortar composite concrete material and its preparation method to overcome the poor comprehensive performance and poor durability of the existing semi-flexible pavement, which requires partial thermal construction and construction period Short and other deficiencies provide a new idea and new material for the development of high-performance pavement materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of epoxy resin/cement mortar composite concrete material and preparation method thereof
  • A kind of epoxy resin/cement mortar composite concrete material and preparation method thereof
  • A kind of epoxy resin/cement mortar composite concrete material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Epoxy resin / cement mortar composite concrete material is composed of high porosity epoxy resin crushed stone mixture and high fluidity polymer modified cement mortar. Porosity The internal pores of the epoxy resin crushed stone mixture form a dense composite structure after the two are consolidated and formed.

[0038] The high-porosity epoxy resin crushed stone mixture is composed of a single-component epoxy resin adhesive and crushed stones, the porosity is 20%, and the mass ratio of crushed stones to adhesive is 100:6. Crushed stone is a mixture of basalt rock with a particle size of 3-5mm and basalt rock with a particle size of 5-10mm, and the mass ratio of the two is 2:1.

[0039] The one-component epoxy resin adhesive is a water-activated one-component epoxy resin adhesive, and the formula composition in parts by mass is as follows:

[0040]

[0041] The preparation method of described one-component epoxy resin adhesive, its concrete steps are:

[0042] 1) We...

Embodiment 2

[0055] Epoxy resin / cement mortar composite concrete material is composed of high porosity epoxy resin crushed stone mixture and high fluidity polymer modified cement mortar. Porosity The internal pores of the epoxy resin crushed stone mixture form a dense composite structure after the two are consolidated and formed.

[0056] The high-porosity epoxy resin crushed stone mixture is composed of a single-component epoxy resin adhesive and crushed stones, the porosity is 30%, and the mass ratio of crushed stones to adhesive is 100:3. Crushed stone is a mixture of basalt rock with a particle size of 3-5mm and basalt rock with a particle size of 5-10mm, and the mass ratio of the two is 1:1.

[0057] The one-component epoxy resin adhesive is a water-activated one-component epoxy resin adhesive, and the formula composition in parts by mass is as follows:

[0058]

[0059] The preparation method of described one-component epoxy resin adhesive, its concrete steps are:

[0060] 1) We...

Embodiment 3

[0073] Epoxy resin / cement mortar composite concrete material is composed of high porosity epoxy resin crushed stone mixture and high fluidity polymer modified cement mortar. Porosity The internal pores of the epoxy resin crushed stone mixture form a dense composite structure after the two are consolidated and formed.

[0074] The high-porosity epoxy resin crushed stone mixture is composed of a single-component epoxy resin adhesive and crushed stone, its porosity is 25%, and the mass ratio of crushed stone to adhesive is 100:4.5. Crushed stone is a mixture of basalt rock with a particle size of 3-5mm and basalt rock with a particle size of 5-10mm, and the mass ratio of the two is 1.5:1.

[0075] The one-component epoxy resin adhesive is a water-activated one-component epoxy resin adhesive, and the formula composition in parts by mass is as follows:

[0076]

[0077] The preparation method of described one-component epoxy resin adhesive, its concrete steps are:

[0078] 1) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of preparation of road materials and discloses an epoxy resin / cement mortar compound concrete material and a preparation method therefor. The epoxy resin / cement mortar compound concrete material is prepared through compounding a high-porosity epoxy resin gravel mixture and high-fluidity polymer modified cement mortar in a specific compounding manner that internal pores of the high-porosity epoxy resin gravel mixture are filled with the high-fluidity polymer modified cement mortar, and a dense compound structure is formed after the high-porosity epoxy resin gravel mixture and the high-fluidity polymer modified cement mortar are subjected to consolidation molding. The preparation method comprises the following steps: 1) preparing the high-porosityepoxy resin gravel mixture; 2) pouring the high-fluidity polymer modified cement mortar; and 3) performing concrete curing. Compared with the prior art, the epoxy resin / cement mortar compound concrete material has the advantages of high comprehensive performance, good stability and durability, high cost performance, convenience in construction, long construction cycle, and the like and is relatively applicable to the paving construction of semi-flexible pavements.

Description

technical field [0001] The invention belongs to the technical field of road material preparation, and in particular relates to an epoxy resin / cement mortar composite concrete material and a preparation method thereof. Background technique [0002] Asphalt concrete material and cement concrete material are two typical pavement materials for expressway construction in my country, each with its own advantages and disadvantages. Asphalt pavement is a flexible pavement with smooth road surface and comfortable driving, but its strength is low, its service life is short, and it is prone to high-temperature rutting and low-temperature cracking. The strength and rheological properties are greatly affected by temperature changes. When the temperature is high in summer, the asphalt material will weaken the cohesion between the aggregate particles due to the decrease in viscosity, which will reduce the strength and deformation resistance of the pavement, and it is easy to appear Waves,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C08L63/00C08K13/06C08K3/34C08K7/26C08K7/08
CPCC04B28/00C04B2201/50C08L63/00C08L2205/025C04B24/281C04B14/14C04B2103/50C04B2103/408C04B14/06C04B18/08C04B14/383C04B14/104C04B24/023C04B24/32C04B24/38C04B24/121C04B2103/302C08K13/06C08K3/346C08K7/26C08K7/08
Inventor 舒兴旺程飞申力涛张影李登华刘哲崔东霞林浩毛敏
Owner 山西交通科学研究院集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products