Formaldehyde-removing anti-graffiti multifunctional environmentally-friendly coating and preparation method thereof

An environmentally friendly coating and anti-graffiti technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve problems such as very harsh environmental requirements and solvents that do not meet environmental protection requirements, to avoid material waste, Good anti-graffiti performance, the effect of increasing fun

Inactive Publication Date: 2018-09-18
NINGBO INST OF TECH ZHEJIANG UNIV ZHEJIANG
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional anti-graffiti coatings are formulated with epoxy resins; epoxy resins are very demanding on the environment. Once applied, they will form a coating similar to high-gloss glass sheets, but epoxy resins are mostly two-component, It needs to be prepared on the spot during construction, and it contains a lot of solvents, which does not meet the requirements of environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] A preparation method for formaldehyde-removing anti-graffiti multifunctional environmental protection paint, comprising the following steps:

[0032] Step 1. Add water to the dispersing kettle equipped with a high-speed dispersing machine, turn on the dispersing machine, add ethylene urea, chitin, and aqueous calcium stearate to disperse for 30 minutes to 90 minutes;

[0033] Step 2. Add magnesium aluminum silicate to the dispersing kettle of step 1, and continue to disperse for 30 minutes to 90 minutes;

[0034] Step 3: Add glycerol, defoamer, and film-forming aid to the dispersing kettle in step 2 in sequence, and continue to disperse for 30 minutes to 90 minutes;

[0035] Step 4. Add formaldehyde-removing resin emulsion and anti-graffiti resin emulsion to the dispersion kettle in step 3 in sequence, and continue to disperse for 10 to 30 minutes;

[0036] Step 5. Add thickener, 2-amino-2-methyl-1-propanol and phenolphthalein to the dispersing kettle in step 4 in sequ...

Embodiment 1

[0039] A kind of formaldehyde-removing anti-graffiti multifunctional environmental protection paint, prepares raw materials according to the following weight percentages:

[0040] Formaldehyde Resin Emulsion 20%

[0041] Anti-graffiti resin emulsion 20%

[0042] Magnesium Aluminum Silicate 2.5%

[0043] Coalescent

[0044] (2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate diester) 1%

[0045] Ethylene urea 3%

[0046] 2-Amino-2-methyl-1-propanol 0.1%

[0047] Glycerol 2%

[0048] Chitin 3%

[0049] Phenolphthalein 0.01%

[0050] Defoamer 0.1%

[0051] Thickener 0.5%

[0052] Aqueous Calcium Stearate 1%

[0053] Water 46.79%.

[0054] Prepared according to the following steps:

[0055] Step 1. Add 46.79% of water into the dispersing kettle with a high-speed disperser, turn on the disperser, add 3% ethylene urea, 3% chitin, and 1% aqueous calcium stearate to disperse for 30 minutes;

[0056] Step 2. Add 2.5% magnesium aluminum silicate to the dispersing kettle of s...

Embodiment 2

[0061] A kind of formaldehyde-removing anti-graffiti multifunctional environmental protection paint, prepares raw materials according to the following weight percentages:

[0062] Formaldehyde Resin Emulsion 10%

[0063] Anti-graffiti resin emulsion 30%

[0064] Magnesium Aluminum Silicate 2%

[0065] Coalescent

[0066] (2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate diester) 3%

[0067] Ethylene urea 5%

[0068] 2-Amino-2-methyl-1-propanol 0.5%

[0069] Glycerol 3%

[0070] Chitin 5%

[0071] Phenolphthalein 0.1%

[0072] Defoamer 0.5%

[0073] Thickener 1%

[0074] Aqueous Calcium Stearate 3%

[0075] Water 36.9%.

[0076] Prepared according to the following steps:

[0077] Step 1. Add 36.9% water into the dispersing kettle with a high-speed disperser, turn on the disperser, add 5% ethylene urea, 5% chitin, and 3% aqueous calcium stearate to disperse for 40 minutes;

[0078] Step 2. Add 2% magnesium aluminum silicate to the dispersing kettle of step 1, and conti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formaldehyde-removing anti-graffiti multifunctional environmentally-friendly coating comprising the following raw materials by weight: 10% to 50% of aldehyde-removing resin emulsion, 20 to 50% of anti-graffiti resin emulsion, 1 to 5% of magnesium aluminium silicate, 1 to 10% of a membrane-formation aid, 1 to 8% of ethylene urea, 0.1 to 1% of 2-amino-2-methyl-1-propanol, 1to 6% of glycerol, 3 to 9% of chitin, 0.01 to 0.5% of phenolphthalein, 0.1 to 3% of a defoamer, 0.1 to 3% of a thickener, 1 to 8% of aqueous calcium stearate, 20 to 70% of water;the sum of the abovecomponents is 100%. The preparation method comprises the following steps: adding the water, the ethylene urea, the chitin and the calcium stearate in a dispersion kettle for dispersing, further dispersing with the magnesium aluminium silicate, further dispersing with the glycerin, the defoamer and the membrane-formation aid, then adding the aldehyde-removing resin emulsion, and the anti-graffiti resin emulsion, and finally adding the thickener, the 2-amino-2-methyl-1-propanol and the phenolphthalein.

Description

technical field [0001] The invention relates to an environmentally friendly paint, in particular to a formaldehyde-removing, graffiti-resistant, multi-functional environmentally friendly paint and a preparation method thereof. Background technique [0002] Formaldehyde has been determined by the World Health Organization as a carcinogenic and teratogenic substance, and is generally considered to be the number one indoor killer. Various decorative wood-based panels inevitably contain a certain amount of formaldehyde; in newly decorated indoor environments, the incubation period of formaldehyde is as long as several years, and it is mutagenic, carcinogenic, and reproductively toxic. At present, there are many methods and tools for removing formaldehyde in the society, but the results are not satisfactory. For example, use an air purifier to purify the air and remove formaldehyde. Most of this equipment is equipped with an activated carbon adsorption layer. After a period of u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12C09D133/14C09D5/16C09D7/61C09D7/63C09D7/65
CPCC08L2201/10C08L2205/03C09D5/1668C09D5/1687C09D127/12C09D133/14C08L33/14C08L5/08C08K13/02C08K5/3445C08K5/17C08K5/053C08K5/098C08K3/34C08L27/12
Inventor 徐金宝钟国伦胡锦平张广宇
Owner NINGBO INST OF TECH ZHEJIANG UNIV ZHEJIANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap