Composite material for manufacturing glass crafts

A composite material and handicraft technology, applied in the field of glass handicraft materials, can solve the problems of high quality glass handicrafts, not easy to transport and store, not corrosion-resistant, etc. Effect

Inactive Publication Date: 2018-10-16
盐城克莱斯曼工艺品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glass handicrafts are generally divided into three categories: molten glass handicrafts, lampwork glass handicrafts, and glazed handicrafts. They are often used as decorative materials or high-end gifts and artworks. After repeated mould-turning and pouring, such as lampwork glass crafts, colorful glass rods are used as the main material. Oxygen and liquefied gas are used to heat the glass rods to melt the heated rods quickly, and then the operator uses pliers, Blades and other small tools carry out the whole process of shaping various products. With the continuous development of society, people's tastes gradually improve, and they pay more and more attention to spiritual life. Compared with glass crafts, they are favored by people, which can enhance the taste and quality of home decoration. Artistic sense, the existing composite materials used to make glass handicrafts are almost the same as the raw materials of ordinary glass, and the prepared glass handicrafts are of high quality, fragile, and not resistant to corrosion, which makes it difficult to transport and store. Composite materials for manufacturing glass crafts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1) Put 25 parts of silica sand, 22 parts of kaolin and 20 parts of limestone into the jaw crusher for crushing;

[0018] 2) Add the preparation in step 1), 17 parts of sodium carbonate, 12 parts of sodium sulfate and 3 parts of glass colorant into the mixer, and then add water into the mixer, the amount of water added is the material in the mixer 5% of the total weight, start the mixer, and mix the material evenly;

[0019] 3) Put the preparation in step 2) into a melting furnace for melting, the melting temperature is 1200°C, and the melting time is 25 minutes;

[0020] 4) Cool down the preparation in step 3) to 300°C, and the cooling time is 60 minutes;

[0021] 5) Add 8 parts of phthalic acid, 1 part of polystyrene, 1 part of polyvinyl acetate and 1 part of vinyl resin to the preparation in step 4), and use a vacuum defoaming mixer to stir the mixture evenly.

Embodiment 2

[0023] 1) Put 27 parts of silica sand, 22 parts of kaolin and 21 parts of limestone into the jaw crusher for crushing;

[0024] 2) Add the preparation in step 1), 18 parts of sodium carbonate, 13 parts of sodium sulfate and 3 parts of glass colorant into the mixer, and then add water into the mixer, the amount of water added is the material in the mixer 6% of the total weight, start the mixer, and mix the material evenly;

[0025] 3) Put the preparation in step 2) into a melting furnace for melting, the melting temperature is 1220°C, and the melting time is 27 minutes;

[0026] 4) Cool down the preparation in step 3) to 305°C, and the cooling time is 60 minutes;

[0027] 5) Add 9 parts of phthalic acid, 2 parts of polystyrene, 2 parts of polyvinyl acetate and 1 part of vinyl resin to the preparation in step 4), and use a vacuum defoaming mixer to stir the mixture evenly.

Embodiment 3

[0029] 1) Put 29 parts of silica sand, 23 parts of kaolin and 22 parts of limestone into the jaw crusher for crushing;

[0030] 2) Add the preparation in step 1), 19 parts of sodium carbonate, 14 parts of sodium sulfate and 4 parts of glass colorant into the mixer, and then add water into the mixer, the amount of water added is the material in the mixer 6% of the total weight, start the mixer, and mix the material evenly;

[0031] 3) Put the preparation in step 2) into a melting furnace for melting, the melting temperature is 1240°C, and the melting time is 29 minutes;

[0032] 4) Cool down the preparation in step 3) to 310°C, and the cooling time is 60 minutes;

[0033] 5) Add 10 parts of phthalic acid, 2 parts of polystyrene, 2 parts of polyvinyl acetate and 1 part of vinyl resin to the preparation in step 4), and use a vacuum defoaming mixer to stir the mixture evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of glass craft materials, in particular to a composite material for manufacturing glass crafts. The composite material is composed of silica sand, kaolin,limestone, sodium carbonate, sodium sulfate, phthalic acid, glass colorant, polystyrene, polyethyl acetate and vinyl resin. The phthalic acid is unsaturated polyester resin, thereby having the advantages of light weight and high strength, so that the glass crafts have the advantages of light weight and high strength; polystyrene and polyethyl acetate are mixed in phthalic acid and form a low shrinkage agent to enable multiple micropores to be formed after the phthalic acid is solidified, so that shrinkage rate in the process of solidifying and shrinking of the phthalic acid is lowered effectively, and size accuracy and surface smoothness of the glass crafts are ensured; the vinyl resin is corrosion-resistant resin, so that corrosion resistance of the glass crafts is improved and preservation time of the same is prolonged after the vinyl resin is added.

Description

technical field [0001] The invention relates to the technical field of glass handicraft materials, and the specific field is a composite material used for manufacturing glass handicrafts. Background technique [0002] Glass handicrafts are generally divided into three categories: molten glass handicrafts, lampwork glass handicrafts, and glazed handicrafts. They are often used as decorative materials or high-end gifts and artworks. After repeated mould-turning and pouring, such as lampwork glass crafts, colorful glass rods are used as the main material. Oxygen and liquefied gas are used to heat the glass rods to melt the heated rods quickly, and then the operator uses pliers, Blades and other small tools carry out the whole process of shaping various products. With the continuous development of society, people's tastes gradually improve, and they pay more and more attention to spiritual life. Compared with glass crafts, they are favored by people, which can enhance the taste ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/04C03C4/20
CPCC03C1/00C03C4/20C03C2201/60
Inventor 郭建军
Owner 盐城克莱斯曼工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com