Soft ceramic wall surface composite material and preparation method thereof

A composite material and wall technology, applied in the field of building wall materials, can solve the problem of high energy consumption, and achieve the effects of simple preparation process, guaranteed source and good compatibility

Inactive Publication Date: 2018-10-16
广东福莱特建筑材料有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although soft tiles have the above advantages, they still need to be improved in terms of waterproof performance and aging resistance, and most of the existing soft porcelain preparation processes require high-temperature sintering and high energy consumption.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A soft porcelain wall composite material, comprising the following raw materials in parts by mass: 10 parts of polymer emulsion, 25 parts of inorganic filler, 0.1 part of wetting agent, 0.2 part of defoamer, 0.1 part of cellulose, 10 parts of deionized water, 0.1 part of polyvinyl alcohol fiber.

[0026] The inorganic filler adopts heavy calcium carbonate.

[0027] The wetting agent adopts sulfonated oil.

[0028] Described defoamer adopts emulsified silicone oil.

[0029] The cellulose is hydroxyethyl cellulose.

[0030] The polymer emulsion adopts acrylic acid emulsion.

[0031] The solid content in the polymer emulsion was 35%.

[0032] The preparation method of the above-mentioned soft porcelain wall composite material specifically comprises the following steps:

[0033] 1) Weigh each component of the formulation amount, add the required polymer emulsion, cellulose, and deionized water into the reaction kettle under normal temperature and pressure, and stir at ...

Embodiment 2

[0037] A soft porcelain wall composite material, comprising the following raw materials in parts by mass: 20 parts of polymer emulsion, 45 parts of inorganic filler, 0.15 part of wetting agent, 0.3 part of defoamer, 0.2 part of cellulose, 12 parts of deionized water, 0.2 parts of polyvinyl alcohol fiber.

[0038] The inorganic filler is quartz sand.

[0039] The wetting agent adopts mercaptan compound.

[0040] The defoamer uses a high-carbon alcohol fatty acid ester compound.

[0041] The cellulose is ethyl-2-hydroxyethyl cellulose.

[0042] The polymer emulsion adopts acrylic acid emulsion.

[0043] The solid content in the polymer emulsion was 45%.

[0044] The preparation method of the above-mentioned soft porcelain wall composite material specifically comprises the following steps:

[0045] 1) Weigh each component of the formulation amount, add the required polymer emulsion, cellulose, and deionized water into the reaction kettle under normal temperature and pressure...

Embodiment 3

[0049] A soft porcelain wall composite material, comprising the following raw materials in parts by mass: 35 parts of polymer emulsion, 65 parts of inorganic filler, 0.2 part of wetting agent, 0.4 part of defoamer, 0.3 part of cellulose, 15 parts of deionized water, 0.3 parts of polyvinyl alcohol fiber.

[0050] The inorganic filler is quartz sand.

[0051] The wetting agent is a hydrazide compound.

[0052] Described defoamer adopts polydimethylsiloxane.

[0053] The cellulose is mixed with hydroxyethyl cellulose and ethyl-2-hydroxyethyl cellulose at a ratio of 1:1.

[0054] The polymer emulsion adopts acrylic acid emulsion.

[0055] The solids content in the polymer emulsion was 55%.

[0056] The preparation method of the above-mentioned soft porcelain wall composite material specifically comprises the following steps:

[0057] 1) Weigh each component of the formulation amount, add the required polymer emulsion, cellulose, and deionized water into the reaction kettle at...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of building walls and discloses a soft ceramic wall surface composite material. The soft ceramic wall surface composite material is prepared from, by mass,10-35 parts of polymer emulsion, 25-65 parts of inorganic filler, 0.1-0.2 part of a wetting agent, 0.2-0.4 part of an antifoaming agent, 0.1-0.3 part of cellulose, 10-15 parts of deionized water and0.1-0.3 part of polyvinyl alcohol fibers. The soft ceramic wall surface composite material has advantages of high water-repellency breathability, light weight, flexibility, acid-base resistance, freeze thawing resistance, aging resistance, quake resistance, crack resistance and high exterior wall external insulation system compatibility. The soft ceramic wall surface composite material overcomes potential safety hazards including proneness to falling to hurt people and the like of traditional ceramic tiles, mosaics and the like and is especially suitable for serving as an exterior wall facingmaterial for high-rise buildings and exterior wall external insulation systems. Especially, the soft ceramic material can be adhered directly to an old wall without knocking off old ceramic tiles andmosaics in old wall renovation or space renovation.

Description

technical field [0001] The invention relates to a soft porcelain wall surface composite material and a preparation method thereof, belonging to the technical field of building wall materials. Background technique [0002] Soft porcelain is not real porcelain, nor tiles, it is a new type of building decoration material. According to the "Technical Regulations for Soft Porcelain Architectural Decoration Engineering" formulated by the state, it is a kind of flexible porcelain made of modified clay powder (MCM) as the main raw material, formed by a special temperature-controlled molding system, baked, and irradiated. architectural decorative surface materials. It has the appearance of ceramic tiles, so it is commonly known as soft porcelain. With the development of technology, it can be developed to imitate stone, imitate leather, imitate wood, etc. Anything that can be imagined, soft porcelain can be realized. Soft porcelain building decoration materials can be pasted on a va...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/00C08L1/28C08L29/04C08K3/26C08K3/36
CPCC08K2003/265C08L33/00C08L2205/025C08L2205/03C08L2205/035C08L2205/16C08L1/284C08L29/04C08K3/26C08K3/36
Inventor 李远华覃现勇
Owner 广东福莱特建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com