A kind of imitation glaze color plastic glazed tile and preparation method thereof

A glazed tile and imitation glaze technology, applied in the field of plastic products, can solve the problems of poor impact resistance and weather resistance, affect the ecological environment, destroy cultivated land and other problems, achieve good impact resistance and weather resistance, reduce surface roughness, The effect of improving impact resistance

Active Publication Date: 2020-06-30
成都菲斯特新材料有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problem that the glazed tile made of clay in the prior art has poor impact resistance and weather resistance, needs to use clay, destroys cultivated land, and affects the ecological environment. It provides a glazed imitation colored plastic glazed tile. Using resin carrier and additives to achieve good impact resistance and weather resistance, rich colors and good appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of imitation glaze color plastic glazed tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] An imitation glazed red plastic glazed tile, including an upper layer and a lower layer, the upper layer is composed of the following raw materials by mass percentage: AS2200 67%, ASA031H 30%, transparent iron oxide red 2.25%, phthalocyanine blue 0.0092%, peach red 0.0048%, charcoal Black M430 0.2%, EBS 400A 0.49%, silane coupling agent 7007 0.05%; the lower layer includes the following raw materials in terms of mass percentage: five types of PVC 50%, nano-active calcium carbonate 40%, iron oxide 2.25%, phthalocyanine Blue 0.0092%, pink 0.0048%, carbon black M430 0.2%, AV-A 1%, EBS 0.5%, silane coupling agent 7007 1.2%, DOP 2.3%.

Embodiment 2

[0039] An imitation glazed yellow plastic glazed tile, including an upper layer and a lower layer, the upper layer is composed of the following raw materials in percentage by mass: AS resin 2200 75%, acrylate 18%, transparent iron yellow 1.9%, titanium dioxide 0.3%, pink 0.74%, EBS 0.9%, DOP 3.15%, silane coupling agent 7007 0.01%; the lower layer includes the following raw materials by mass percentage: PVC type V 60%, nano-active calcium carbonate 30%, transparent iron yellow 1.9%, titanium dioxide 0.3%, AV-A 1.5%, EBS 0.75%, DOP 2.9%, silane coupling agent 7007 0.35%.

Embodiment 3

[0041] An imitation glazed dark green plastic glazed tile, including an upper layer and a lower layer, the upper layer includes the following raw materials by mass percentage: AS resin 2200 65%, ASA031H 27%, phthalocyanine green 3.01%, carbon black 0.01%, EBS 0.95%, DOP3. 5%, silane coupling agent 7007 0.45%; the lower layer includes the following raw materials by mass percentage: PVC type five 56%, nano-active calcium carbonate 35%, phthalocyanine green 2.9%, carbon black 0.01%, EBS 1.2 %, AV-A 1.7%, silane coupling agent 7007 0.49%, DOP 2.7%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

Belonging to the technical field of plastic products, the invention discloses a glaze-imitating colored plastic glazed tile and a preparation method thereof. The glazed tile comprises an upper layer and a lower layer, the upper layer comprises the following raw materials by mass percentage: 65-75% of AS resin, 15-30% of an AS resin modifier, 2.5-3.5% of a coloring pigment I, and 0.5-5% of an assistant I; the lower layer comprises the following raw materials by mass percentage: 50-60% of PVC resin, 30-40% of nano-active CaCO3, 3.5-5% of an additive II, and 0-3.5% of a coloring pigment II; the AS resin modifier is at least one of ASA resin and acrylic ester; the coloring pigment I is a transparent pigment; and the nano-active CaCO3 crystalline form is a cubic crystal form. The glazed tile provided by the invention has good appearance effect and glaze-imitating effect, and the weatherability, impact resistance and environmental friendliness are all superior to clay glazed tiles in the prior art.

Description

technical field [0001] The invention relates to a glazed tile, in particular to an imitation glazed colored plastic glazed tile and a preparation method thereof, belonging to the technical field of plastic products. Background technique [0002] Ancient buildings are widely distributed in urban buildings, palaces, dwellings, temples, museums, and parks all over the country. Their buildings, platforms, pavilions, pavilions, pagodas, archways, and walls are all important parts of Chinese traditional culture. Glazed tiles are the "face project" of these ancient buildings, and their splendor and splendor have added splendor to Chinese ancient buildings for thousands of years. However, glazed tiles are made of clay and glazed and fired, so they are not resistant to impact and must be refurbished as they age. With the progress of human civilization, it is a basic national policy to protect the cultivated land, protect the environment, not use clay to make bricks and burn tiles, p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/30B32B27/20B32B27/18B32B27/08B32B27/06B32B9/04B32B9/00C08L27/06C08K13/02C08K3/26C08K3/22C08K3/04C08K5/14C08L25/12C08L51/04B29C48/18B29B13/06B29L31/10B29L9/00
CPCB29B13/065B29C48/22B29L2009/00B29L2031/104B32B9/00B32B9/045B32B27/06B32B27/08B32B27/18B32B27/20B32B27/302B32B27/304B32B2307/21B32B2307/304B32B2307/3065B32B2307/418B32B2307/50B32B2307/552B32B2307/558B32B2307/714B32B2307/746B32B2419/06C08K3/04C08K3/22C08K3/26C08K5/14C08K13/02C08K2003/2265C08K2003/2272C08K2003/265C08K2201/011C08L25/12C08L51/04C08L27/06
Inventor 陈旭郑凌叶邵世容
Owner 成都菲斯特新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com