Ba and Ge containing gold alloy for corrosion-resisting and deformation-resisting 10K rose red gold

A deformation-resistant, rose-red technology, applied in the field of gold alloys, to achieve great corrosion resistance, improve discoloration resistance, and improve processability

Inactive Publication Date: 2018-10-26
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But so far, there is no complete solution to prevent rose gold from fading during the 10-year service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A corrosion-resistant and deformation-resistant 10K rose red gold containing Ba and Ge gold alloy. In terms of weight percentage, the composition of the alloy is Ba:0.3wt.%, Zr:0.2wt.%, Ge:1.0wt.%, W:0.3wt.%, Ag:20.0wt.%, Au:40.0wt.% , and the balance is copper. The preparation method of the above-mentioned corrosion-resistant and deformation-resistant 10K rose gold alloy containing Ba and Ge includes the following steps: adding the raw materials in the above ratio into an induction furnace protected by argon gas, and using a graphite crucible; The flow of argon is protected to avoid severe burning of the alloy elements due to the large air flow; when smelting, it is kept at 1150 degrees for 10 minutes, and it is evenly stirred by a high-frequency induction furnace; after stirring, it is kept at 1250 degrees for 1 minute and cast out of the furnace; gold alloy Casting adopts a steel mold with a diameter of 100-200mm, and uses water cooling to cool down. Roll the obtai...

Embodiment 2

[0019]A corrosion-resistant and deformation-resistant 10K rose red gold containing Ba and Ge gold alloy. In terms of weight percentage, the composition of the alloy is Ba:0.5wt.%, Zr:0.4wt.%, Ge:1.5wt.%, W:0.5wt.%, Ag:25.0wt.%, Au:42.0wt.% , and the balance is copper. The preparation method of the above-mentioned corrosion-resistant and deformation-resistant 10K rose red gold containing Ba and Ge gold alloy includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a graphite crucible; The flow of argon is protected to avoid severe burning of the alloy elements due to the large air flow; when smelting, it is kept at 1150 degrees for 10 minutes, and it is evenly stirred by a high-frequency induction furnace; after stirring evenly, it is kept at 1250 degrees for 1 minute and cast out of the furnace; gold alloy Casting adopts a steel mold with a diameter of 100-200mm, and uses water cooling to cool down. The obtai...

Embodiment 3

[0022] A corrosion-resistant and deformation-resistant 10K rose red gold containing Ba and Ge gold alloy. In terms of weight percentage, the composition of the alloy is Ba:0.4wt.%, Zr:0.3wt.%, Ge:1.2wt.%, W:0.4wt.%, Ag:24.0wt.%, Au:41.0wt.% , and the balance is copper. The preparation method of the above-mentioned corrosion-resistant and deformation-resistant 10K rose red gold containing Ba and Ge gold alloy includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a graphite crucible; The flow of argon is protected to avoid severe burning of the alloy elements due to the large air flow; when smelting, it is kept at 1150 degrees for 10 minutes, and it is evenly stirred by a high-frequency induction furnace; after stirring evenly, it is kept at 1250 degrees for 1 minute and cast out of the furnace; gold alloy Casting adopts a steel mold with a diameter of 100-200mm, and uses water cooling to cool down. The obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Ba and Ge containing gold alloy for corrosion-resisting and deformation-resisting 10K rose red gold. According to the weight percent, the alloy comprises components including0.3 wt.%-0.5 wt.% of Ba, 0.2 wt.%-0.4 wt.% of Zr, 1.0 wt.%-1.5 wt.% of Ge, 0.3 wt.%-0.5 wt.% of W, 20.0 wt.%-25.0 wt.% of Ag, 40.0 wt.%-42.0 wt.% of Au and the balance Cu. The Ba and Ge containing gold alloy avoids the phenomenon that current 10K rose gold fades in the usage process. Through alloy component innovation and optimization, the development bottleneck of jewelry 10K rose gold materialsis broken through. It can be predicted that abundant economic gains and social benefits can be obtained due to material implementation and industrialization.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a gold alloy. Background technique [0002] Gold has a wide range of applications, and has a wide range of applications in electronics, communications, aerospace, chemical, medical and other departments and people's daily life. Jewelry gold is an important application field of gold. In addition to the reasons for gold to preserve value, clarity and pleasing colors are also an important factor. For gold alloys, except for white gold, others are called colored gold. The most common color in life is 18K gold, and K is an international symbol used to represent the purity of gold. 18K gold refers to gold with a gold content of 75%, while the remaining 25% is composed of other metals in a certain proportion. The reason for the color is due to the different proportions of the metals. Many gold alloys have these effects, such as gold-nickel alloys, gold-indium alloys, gold-copper all...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C30/02C22C1/02C22F1/14
CPCC22C30/02C22C1/02C22C5/02C22F1/14
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap