Method for preparing super absorbent antibacterial blended cotton cloth

A technology of cotton gauze and high water absorption, which is applied in textiles, textiles and papermaking, biochemical fiber treatment, etc. It can solve the problems of unable to provide a moist environment for wounds, limited water absorption capacity of fibers, and unfavorable wound healing, etc., and achieve good overall easy removal , high hygroscopicity, gelation, and excellent biodegradable absorption

Inactive Publication Date: 2018-10-30
湖南科力嘉纺织股份有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The fibers in the existing medical absorbent cotton gauze generally have limited water absorption capacity and cannot provide a moist environment for t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1:

[0022] A preparation method of high water absorption and antibacterial blended cotton gauze includes the following steps:

[0023] (1) Carry out swelling treatment on cotton gauze, the cotton gauze is made by blending seaweed fiber and cotton fiber, the weight ratio of seaweed fiber and cotton fiber is 1:2; the swelling treatment includes 20wt.% hydrogen Sodium oxide solution is a swelling agent, and the cotton gauze is soaked in the swelling agent for 10 minutes at 26°C.

[0024] (2) Carry out carboxymethylation modification treatment on the cotton gauze after swelling treatment, the carboxymethylation rate is 5%.

[0025] (3) Use 37℃ warm water to wash cotton gauze;

[0026] (4) Use 1wt.% dilute hydrochloric acid to pickle cotton gauze to neutralize residual caustic soda;

[0027] (5) Wash the cotton gauze with cold water for many times until the pH of the cotton gauze is neutral;

[0028] (6) Put the cotton gauze treated in step (5) soaked in absolute ethanol for 5...

Example Embodiment

[0031] Example 2:

[0032] A preparation method of high water absorption and antibacterial blended cotton gauze includes the following steps:

[0033] (1) Carry out swelling treatment on cotton gauze, the cotton gauze is made of seaweed fiber and cotton fiber blended, the weight ratio of seaweed fiber and cotton fiber is 1:2; the swelling treatment includes 28wt.% hydrogen Sodium oxide solution is a swelling agent, and the cotton gauze is soaked in the swelling agent for 30 minutes at 29°C.

[0034] (2) Carry out carboxymethylation modification treatment on the cotton gauze after swelling treatment, the carboxymethylation rate is 30%.

[0035] (3) Wash the cotton gauze with 42℃ warm water;

[0036] (4) Use 2wt.% dilute hydrochloric acid to pickle cotton gauze to neutralize residual caustic soda;

[0037] (5) Wash the cotton gauze with cold water for many times until the pH of the cotton gauze is neutral;

[0038] (6) Put the cotton gauze treated in step (5) soaked in absolute ethanol for...

Example Embodiment

[0041] Example 3:

[0042] A preparation method of high water absorption and antibacterial blended cotton gauze includes the following steps:

[0043] (1) Carry out swelling treatment on the cotton gauze, the cotton gauze is made of seaweed fiber and cotton fiber blended, the weight ratio of seaweed fiber and cotton fiber is 1:2; the swelling treatment includes 24wt.% hydrogen Sodium oxide solution is a swelling agent, and the cotton gauze is soaked in the swelling agent for 20 minutes at 28°C.

[0044] (2) Carry out the carboxymethylation modification treatment on the cotton gauze after swelling treatment, the carboxymethylation rate is 20%.

[0045] (3) Wash the cotton gauze with warm water at 40℃;

[0046] (4) Use 1.5wt.% dilute hydrochloric acid to pickle cotton gauze to neutralize residual caustic soda;

[0047] (5) Wash the cotton gauze with cold water for many times until the pH of the cotton gauze is neutral;

[0048] (6) Put the cotton gauze treated in step (5) soaked in absolut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing super absorbent antibacterial blended cotton cloth. The method comprises the following steps: (1) swelling treatment; (2) carboxymethyl-modification treatment; (3) washing with warm water; (4) pickling and neutralizing; (5) washing with cold water; (6) sterilizing; (7) softening; (8) freeze-drying. The cotton cloth is prepared by blending alginate fibers and cotton fibers, and the alginate fibers have excellent softness, high using comfort, excellent antibacterial effect, high hygroscopic gelling property, excellent overall removable property, high oxygen permeability, excellent biocompatibility and excellent biodegradability and absorbability; the freeze-drying technology is adopted rather than the traditional drying or airing, so that air gaps of the cotton fibers in the swelling and freezing process are fully maintained, and the adsorption property of the cotton fibers is improved.

Description

technical field [0001] The invention relates to a preparation method of cotton gauze, in particular to a preparation method of highly water-absorbing and antibacterial blended cotton gauze. Background technique [0002] Medical absorbent gauze and medical absorbent cotton are the main hygienic materials used in the medical industry for wound dressing, protection, and cleaning of patients. The gauze can promote wound healing of patients, and the gauze has soft texture, low price, wide sources, simple production and processing process, and can be repeated and practical. The fibers in the existing medical absorbent cotton gauze generally have limited water absorption capacity, which cannot provide a moist environment for the wound, which is not conducive to wound healing, and it is easy to cause secondary adhesion of the wound, and in severe cases, it will cause infection. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the presen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M11/38D06M13/00D03D15/00D03D15/217D03D15/225D03D15/47D03D15/50
CPCD06M11/38D06M13/00D06M16/00D06M2101/06D10B2401/13D10B2201/02D03D15/47
Inventor 何新华
Owner 湖南科力嘉纺织股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap