A kind of preparation method of core-shell type porous silica/iron oxide nano catalyst

A porous silica and iron oxide nanotechnology, which is applied in the fields of chemistry and nanomaterials, can solve the problems of sintering and growing of iron oxide grains, uncontrollable morphology and size, and achieve the effects of short production cycle and low cost.

Active Publication Date: 2020-11-17
XIAN UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for preparing a core-shell porous silica / iron oxide nanocatalyst, which solves the problem that the iron oxide crystal grains are sintered and grown and the shape and size are uncontrollable in the heat treatment process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of core-shell type porous silica/iron oxide nano catalyst
  • A kind of preparation method of core-shell type porous silica/iron oxide nano catalyst
  • A kind of preparation method of core-shell type porous silica/iron oxide nano catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A preparation method of a core-shell type porous silica / iron oxide nanocatalyst, specifically implemented according to the following steps:

[0045] Step 1, the synthesis of allyl malonate:

[0046] Add allylmalonic acid and benzyl alcohol to the anhydrous toluene solvent in sequence, add concentrated sulfuric acid with a concentration of 98wt% dropwise during the stirring process to carry out the catalytic shrinkage reaction, reflux at 120°C for 8 hours, and then use Dean- The Stark device removes the generated water, and the collected product is sequentially washed with saturated sodium bicarbonate, saturated saline and distilled water, and finally the product is purified by column chromatography;

[0047] Wherein, the mass ratio of allyl malonic acid and anhydrous toluene solvent is 0.166:1; The mass ratio of benzyl alcohol and anhydrous toluene solvent is 0.26:1; The mass ratio of allyl malonic acid and the concentrated sulfuric acid of 98wt% The ratio is 120:1; th...

Embodiment 2

[0058] A preparation method of a core-shell type porous silica / iron oxide nanocatalyst, specifically implemented according to the following steps:

[0059] Step 1, the synthesis of allyl malonate:

[0060] Add allylmalonic acid and benzyl alcohol to the anhydrous toluene solvent in sequence, add concentrated sulfuric acid with a concentration of 98wt% dropwise during the stirring process to carry out the catalytic shrinkage reaction, reflux reaction at 122°C for 7h, and then use Dean- The Stark device removes the generated water, and the collected product is sequentially washed with saturated sodium bicarbonate, saturated saline and distilled water, and finally the product is purified by column chromatography;

[0061] Wherein, the mass ratio of allyl malonic acid and anhydrous toluene solvent is 0.168:1; The mass ratio of benzyl alcohol and anhydrous toluene solvent is 0.323:1; The mass ratio of allyl malonic acid and the concentrated sulfuric acid of 98wt% The ratio is 118:...

Embodiment 3

[0073] A preparation method of a core-shell type porous silica / iron oxide nanocatalyst, specifically implemented according to the following steps:

[0074] Step 1, the synthesis of allyl malonate:

[0075] Add allylmalonic acid and benzyl alcohol to the anhydrous toluene solvent in sequence, add concentrated sulfuric acid with a concentration of 98wt% dropwise during the stirring process to carry out the catalytic shrinkage reaction, reflux reaction at 130°C for 9h, and then use Dean- The Stark device removes the generated water, and the collected product is sequentially washed with saturated sodium bicarbonate, saturated saline and distilled water, and finally the product is purified by column chromatography;

[0076] Wherein, the mass ratio of allyl malonic acid and anhydrous toluene solvent is 0.16:1; The mass ratio of benzyl alcohol and anhydrous toluene solvent is 0.35:1; The mass ratio of allyl malonic acid and the concentrated sulfuric acid of 98wt% The ratio is 119:1;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a core-shell porous silica / iron oxide nanocatalyst, which is specifically implemented according to the following steps: Step 1, synthesis of allyl malonate: Step 2, hydrosilylation reaction: Step 3. Hydrogenation reduction reaction: Step 4, synthesis of silica / iron oxide nanocatalyst. Compared with the existing synthesis route, this preparation method is practical, simple, has a short production cycle and low cost, and can simultaneously control the morphological structure of iron oxide and the pore size of the silica carrier. The preparation method is achieved by using a carbonyl precursor containing POSS-carboxyl groups and iron for coordination reaction. By controlling the molar ratio of different groups in the reaction, calcination temperature, calcination time, etc., the influence of relevant synthesis parameters on the morphology and structure of the prepared silica / iron oxide nanocatalyst can be determined.

Description

technical field [0001] The invention belongs to the technical field of chemistry and nanometer materials, and in particular relates to a preparation method of a core-shell porous silica / iron oxide nanocatalyst. Background technique [0002] Iron oxide is a very important inorganic non-metallic material, it is non-toxic, non-polluting, and can be used as magnetic material, polishing agent and pigment. Nanoscale iron oxide usually has significant surface effect, volume effect and small size effect, and it has good absorption and shielding effects on ultraviolet rays, and can be widely used in plastics, leather, coatings, inks, electronics, absorbing materials and Catalytic applications and other fields. At present, there are many preparation methods for the synthesis of nanostructured iron oxides with different morphologies, the main methods are template method, hydrothermal method, solid-phase chemical method and chemical vapor deposition method. Among them, the hydrotherma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/745B01J35/00B01J37/08
CPCB01J23/745B01J37/086B01J35/397B01J35/393B01J35/23
Inventor 王珍姚顺侯先亮方长青潘少菲
Owner XIAN UNIV OF TECH