Gas diffusion electrode, preparation method thereof and application thereof in electrochemical reduction of carbon dioxide

A gas diffusion electrode, carbon dioxide technology, applied in the field of electrochemical catalysis, can solve the problems of easy deactivation of catalysts, low energy utilization rate of electrochemical reduction of carbon dioxide, poor product selectivity, etc., so as to suppress hydrogen evolution reaction and increase electrochemical reduction catalysis. Active, the effect of increasing the contact area

Active Publication Date: 2018-11-16
ZHEJIANG UNIV
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the low energy utilization rate of electrochemical reduction of carbon dioxide, poor product selectivity, and easy deactivation of catalysts are the main factors that limit its application. The key to solving this problem is to develop electrode materials with specific selectivity and high catalytic activity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gas diffusion electrode, preparation method thereof and application thereof in electrochemical reduction of carbon dioxide
  • Gas diffusion electrode, preparation method thereof and application thereof in electrochemical reduction of carbon dioxide
  • Gas diffusion electrode, preparation method thereof and application thereof in electrochemical reduction of carbon dioxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: catalyst preparation

[0045] Weigh 10g of urea and 1g of anhydrous copper acetate, mix urea and anhydrous copper acetate evenly and physically to obtain a catalyst precursor, place the catalyst precursor in a 30mL crucible with a lid, and place it in a muffle furnace for pyrolysis Reaction, the reaction temperature is 400°C, the heating rate is 5°C / min, and the reaction time is 2h. The obtained solid is ground to obtain graphite-phase carbon nitride-supported nano-copper oxide, which is the carbon dioxide electrochemical reduction catalyst, called Cu x O@C 3 N 4 -400°C catalyst.

Embodiment 2

[0046] Embodiment 2: catalyst preparation

[0047] The specific preparation process is as shown in Example 1. Only by changing the reaction temperature to 450°C, the graphite-phase carbon nitride-supported nano-copper oxide can also be obtained, which is called Cu x O@C 3 N 4 -450°C catalyst. For Cu in Example 2 x O@C 3 N 4 XRD characterization of the catalyst at -450°C, such as figure 1 As shown, it can be seen that the catalyst includes graphite phase carbon nitride and nano-copper oxides in two crystal forms of cupolite and cuprite.

Embodiment 3

[0048] Embodiment 3: catalyst preparation

[0049] The specific preparation process is as shown in Example 1. Only by changing the reaction temperature to 500 ° C, can also obtain graphite-phase carbon nitride-supported nano-copper oxide, called Cu x O@C 3 N 4 -500°C catalyst. For Cu in Example 3 x O@C 3 N 4 XRD characterization of the catalyst at -500°C, such as figure 1 As shown, it can be seen that the catalyst includes graphite phase carbon nitride and nano-copper oxides in two crystal forms of cupolite and cuprite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a gas diffusion electrode, a preparation method of the gas diffusion electrode, and the application of the gas diffusion electrode in electrochemical reduction of carbon dioxide. The gas diffusion electrode comprises a gas diffusion electrode body and carbon dioxide electrochemical reduction catalysts loaded on the gas diffusion electrode body. Nano copper oxide supportedon graphite phase carbon nitride serves as the carbon dioxide electrochemical reduction catalysts and has two crystal forms of tenorite and cuprit. The gas diffusion electrode can improve the Faradayefficiency of carbon dioxide electrochemical reduction products such as methane, ethylene and other hydrocarbons, and also can effectively inhibit hydrogen evolution reaction.

Description

technical field [0001] The invention relates to the field of electrochemical catalysis, in particular to a gas diffusion electrode, its preparation method and its application in the electrochemical reduction of carbon dioxide. Background technique [0002] Carbon dioxide electrochemical reduction is an important direction of carbon dioxide resource utilization technology, which can convert carbon dioxide into gaseous carbon monoxide, methane, ethylene, ethane, propylene, propane and liquid formic acid, methanol, formaldehyde, acetic acid, ethanol, ethane Aldehyde, ethylene glycol, oxalic acid and other substances produce economically valuable chemicals while slowing down the greenhouse effect brought by carbon dioxide. They have dual benefits of environment and economy, and have received extensive attention in recent years. [0003] Carbon dioxide is the product of the highest oxidation stage of carbon. From the perspective of chemical change, it is in a stable state, close ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25B3/04C25B11/06C25B11/12B01J23/72C25B3/25
CPCB01J23/72B01J35/0033C25B3/25C25B11/051C25B11/091
Inventor 傅杰黎梓浩吕秀阳欧阳平凯
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap