High-strength antibacterial sealing piece and preparation method thereof
A seal, high-strength technology, applied in household components, other household appliances, applications, etc., can solve the problems of high antibacterial performance and mechanical strength, and achieve the effect of simple method, excellent antibacterial ability, and easy-to-obtain raw materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0014] The present invention provides a method for preparing a high-strength antibacterial seal, which includes:
[0015] (1) Add fluorine rubber, phthalate ester, reinforcing filler, antibacterial agent, carbon black and activated magnesium oxide to the mixer in sequence, and obtain the pre-mixed powder M after mixing;
[0016] (2) Mix the premixed powder M and the raw rubber, and add it to the internal mixer, and obtain the antibacterial masterbatch after mixing;
[0017] (3) The antibacterial masterbatch is formed and vulcanized to obtain a high-strength antibacterial seal; the forming process includes the first hot pressing treatment and the second hot pressing treatment sequentially, wherein the first hot pressing treatment The conditions include: a temperature of 70-80°C and a pressure of 5.5-7.2Mpa; the conditions of the second hot pressing treatment include: a temperature of 110-120°C and a pressure of 8.1-9.5Mpa.
[0018] In a preferred embodiment of the present invention, in...
Example Embodiment
[0027] Example 1
[0028] Add 100g of fluororubber, 4g of phthalate, 4g of pyrophyllite, 5g of zinc oxide, 5g of carbon black and 14g of activated magnesia into the blender in sequence, and obtain premixed powder M after mixing; premix 100g Powder M is mixed with 340g of raw rubber, and added to the internal mixer. After mixing (mixing temperature is 80℃, mixing time is 10min), antibacterial masterbatch is obtained; the antibacterial masterbatch is formed and cured , A high-strength antibacterial seal A1 is obtained. Wherein, the forming process includes a first hot pressing treatment and a second hot pressing treatment in sequence, wherein the conditions of the first hot pressing treatment include: a temperature of 70°C, a pressure of 5.5Mpa; The conditions of the pressure treatment include: a temperature of 110°C and a pressure of 8.1Mpa.
Example Embodiment
[0029] Example 2
[0030] Add 100g of fluororubber, 6g of phthalate, 5g of sepiolite, 7g of copper oxide, 6g of carbon black and 16g of activated magnesia into the blender in turn, and obtain premixed powder M after mixing; premix 100g Powder M is mixed with 380g of raw rubber, and added to the internal mixer. After mixing (mixing temperature is 120℃, mixing time is 20min), antibacterial masterbatch is obtained; the antibacterial masterbatch is formed and cured , A high-strength antibacterial seal A2 is obtained. Wherein, the forming process includes a first hot pressing treatment and a second hot pressing treatment in sequence, wherein the conditions of the first hot pressing treatment include: a temperature of 80°C, a pressure of 7.2Mpa; The conditions of the pressure treatment include: a temperature of 120°C and a pressure of 9.5Mpa.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap