Building external wall heat preservation coating and preparation method thereof

A technology for thermal insulation coatings and building exterior walls, applied in anti-corrosion coatings, anti-fouling/underwater coatings, coatings, etc., can solve problems such as poor thermal insulation performance, and achieve low cost, low thermal conductivity, and good stain resistance.

Inactive Publication Date: 2018-11-27
李晟隆
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to save energy and improve the quality of living, thermal insulation coatings, as an important part of building energy conservation, have become a hot topic in current research. However, the thermal insulation performance of building exterior wall coatings is poor at present and cannot meet people's needs. Further research on thermal insulation coatings is required. Improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A thermal insulation coating for building exterior walls, comprising the following raw materials in parts by weight: 40 parts of silicon acrylic emulsion, 45 parts of expanded perlite, 1 part of tripolyethylene glycol monodecyl ether, 1 part of potassium ricinoleate, dimethyl dimethicone 4 parts of copper thiocarbamate, 5 parts of aluminum starch octenyl succinate.

[0020] A preparation method for building exterior wall thermal insulation coating, comprising the following steps:

[0021] (1) Send expanded perlite, aluminum octenyl succinate starch and copper dimethyl dithiocarbamate into ultrafine containers respectively for ultrafine pulverization, and add the pulverized raw materials into the stirring tank successively and heat to Stir at 60°C for 20 minutes, with a stirring speed of 400 rpm, and cool down for later use after stirring;

[0022] (2) After mixing triethylene glycol monodecyl ether and potassium ricinoleate in proportion, add 50 parts of deionized wate...

Embodiment 2

[0025] A thermal insulation coating for building exterior walls, comprising the following raw materials in parts by weight: 45 parts of silicon acrylic emulsion, 48 parts of expanded perlite, 2 parts of tripolyethylene glycol monodecyl ether, 2 parts of potassium ricinoleate, dimethyl dimethicone 5 parts of copper thiocarbamate, 6 parts of aluminum starch octenyl succinate.

[0026] A preparation method for building exterior wall thermal insulation coating, comprising the following steps:

[0027] (1) Send expanded perlite, aluminum octenyl succinate starch and copper dimethyl dithiocarbamate into ultrafine containers respectively for ultrafine pulverization, and add the pulverized raw materials into the stirring tank successively and heat to Stir at 62°C for 23 minutes, with a stirring speed of 450 rpm, and cool down for later use after stirring;

[0028] (2) After mixing triethylene glycol monodecyl ether and potassium ricinoleate in proportion, add 50 parts of deionized wa...

Embodiment 3

[0031] A thermal insulation coating for building exterior walls, comprising the following raw materials in parts by weight: 50 parts of silicone acrylic emulsion, 50 parts of expanded perlite, 3 parts of tripolyethylene glycol monodecyl ether, ricinoleic acid 3 parts of potassium, 6 parts of copper dimethyl dithiocarbamate, 7 parts of aluminum starch octenyl succinate.

[0032] A preparation method for building exterior wall thermal insulation coating, comprising the following steps:

[0033] (1) Send expanded perlite, aluminum octenyl succinate starch and copper dimethyl dithiocarbamate into ultrafine containers respectively for ultrafine pulverization, and add the pulverized raw materials into the stirring tank successively and heat to Stir at 65°C for 25 minutes, with a stirring speed of 500 rpm, and cool down for later use after stirring;

[0034] (2) After mixing triethylene glycol monodecyl ether and potassium ricinoleate in proportion, add 50 parts of deionized water t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a building external wall heat preservation coating and a preparation method thereof. The coating is prepared from, by weight, 40-60 parts of silicone acrylic emulsion, 45-55 parts of expanded perlite, 1-5 parts of triethylene glycol monodecyl ether, 1-5 parts of potassium ricinoleate, 4-8 parts of copper(II) dimethyldithiocarbamate and 5-10 parts of starch aluminium octenylsuccinate. The thermal conductivity coefficient of the heat preservation coating is low, the heat preservation performance of the coating is obviously improved, the water resistance, acid and alkali resistance and washing resistance are good, the raw materials are wide in source, and the coating is low in cost, good in pollution resistance, environmentally friendly and free of pollution.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a thermal insulation coating for building exterior walls and a preparation method thereof. Background technique [0002] Coating is a material that can be coated on the surface of an object by different construction techniques to form a solid film with strong adhesion, certain strength and continuity. The film formed in this way is commonly called a coating film, also known as a paint film or a coating. Architectural coatings are a class of coating products mainly used for house decoration. With the development of urbanization and real estate, the application market of architectural coatings is gradually increasing. [0003] In order to save energy and improve the quality of living, thermal insulation coatings, as an important part of building energy conservation, have become a hot topic in current research. However, the thermal insulation performance of building exterior wall ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/08C09D5/16C09D7/61
CPCC09D5/08C09D5/1687C09D143/04C08L3/06C08L3/04C08K5/098C08K7/26C08K5/06C08K5/39C08K13/04
Inventor 李晟隆
Owner 李晟隆
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap