Bamboo diatom board

A technology of diatom board and bamboo wood, which is applied in the field of bamboo wood board, can solve the problems of single function of bamboo board, inability to effectively use diatomite, and failure to meet the needs of use, and achieve simple preparation method, high hardness and improved function sexual effect

Inactive Publication Date: 2018-12-18
张森
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is a kind of biogenic siliceous sedimentary rock, which is mainly composed of the remains of ancient diatoms. The color of diatomite is white, off-white, gray and light taupe, etc. It is fine, loose, light, porous and water-absorbing. and strong permeability. The main component of diatomite is silicic acid. There are countless pores on the surface, which can absorb and decompose the peculiar smell in the air. It has the functions of humidity control and deodorization. Diatomaceous earth can be effectively utilized, so the bamboo boards made have single functions and cannot meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo diatom board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The present invention proposes a bamboo wood diatom board, including the following raw materials by weight: 10 parts of diatomaceous earth, 20 parts of straw, 3 parts of calcium carbonate, 4 parts of plant fiber, 5 parts of zinc stearate, 10 parts of bamboo charcoal powder, and paraffin wax 2 parts, 3 parts of silane coupling agent, 5 parts of epoxy resin, 30 parts of moso bamboo, 10 parts of wood flour;

[0025] The preparation method includes the following steps:

[0026] S1: Moso bamboo pretreatment: Choose 4 years old moso bamboo as raw material, clean the moso bamboo, dry it after cleaning, and dry it for 1 hour, so that the moisture content of moso bamboo is 1%;

[0027] S2: Cutting and slicing: cutting the pretreated moso bamboo described in S1, cutting off the bamboo joints, scraping off the green bamboo, cutting the moso bamboo, roughing and slicing the inside of the moso bamboo;

[0028] S3: Steaming: Put the flaky bamboo described in S2 into the cooking furnace, set ...

Embodiment 2

[0034] The present invention proposes a bamboo wood diatom board, which includes the following raw materials in parts by weight: 20 parts of diatomaceous earth, 25 parts of straw, 5 parts of calcium carbonate, 7 parts of plant fiber, 10 parts of zinc stearate, 12 parts of bamboo charcoal powder, and paraffin wax 5 parts, 5 parts of silane coupling agent, 7 parts of epoxy resin, 10 parts of moso bamboo, 15 parts of wood flour;

[0035] The preparation method includes the following steps:

[0036] S1: Pretreatment of Moso bamboo: Choose 5 years old Moso bamboo as raw material, clean the Moso bamboo, dry it after cleaning, and dry it for 2h, so that the moisture content of Moso bamboo is 5%;

[0037] S2: Cutting and slicing: cutting the pretreated moso bamboo described in S1, cutting off the bamboo joints, scraping off the green bamboo, cutting the moso bamboo, roughing and slicing the inside of the moso bamboo;

[0038] S3: Steaming: Put the flaky bamboo described in S2 into the cooking...

Embodiment 3

[0044] The present invention proposes a bamboo wood diatom board, which includes the following raw materials in parts by weight: 30 parts of diatomaceous earth, 30 parts of straw, 8 parts of calcium carbonate, 10 parts of plant fiber, 15 parts of zinc stearate, 15 parts of bamboo charcoal powder, and paraffin wax 7 parts, 8 parts of silane coupling agent, 10 parts of epoxy resin, 50 parts of moso bamboo, 20 parts of wood flour;

[0045] The preparation method includes the following steps:

[0046] S1: Pretreatment of moso bamboo: choose 6-year-old moso bamboo as the raw material, clean the moso bamboo, dry it after cleaning, and dry it for 3 hours to make the moso bamboo have 8% moisture content;

[0047] S2: Cutting and slicing: cutting the pretreated moso bamboo described in S1, cutting off the bamboo joints, scraping off the green bamboo, cutting the moso bamboo, roughing and slicing the inside of the moso bamboo;

[0048] S3: Steaming: Put the flaky bamboo described in S2 into the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bamboo diatom board. The bamboo diatom board comprises, by weight, 10-30 parts of kieselguhr, 20-30 parts of straw, 3-8 parts of calcium carbonate, 4-10 parts of plant fibers, 5-15 parts of zinc stearate, 10-15 parts of bamboo charcoal powder, 2-7 parts of paraffin, 3-8 parts of a silane coupling agent, 5-10 parts of epoxy resin, 30-50 parts of moso bamboo and 10-20 partsof wood flour. A preparation method of the bamboo diatom board comprises the following steps of S1, moso bamboo pretreatment, wherein moso bamboo of 4-6 years is selected as raw materials, the moso bamboo is cleaned, the moso bamboo is dried after being cleaned, the moso bamboo is dried for 1-3 h, and the water content of the moso bamboo ranges from 1% to 8%; and S2, cutoff and slicing, wherein the pretreated moso bamboo in S1 is cut, bamboo joints are cut off, and bamboo green is scraped off. According to the bamboo diatom board, peculiar smells in air can be adsorbed and decomposed throughthe added kieselguhr, the functions of humidifying and deodorization are achieved, the functionality of the bamboo board is improved, and the preparation method is simple.

Description

Technical field [0001] The invention relates to the field of bamboo wood boards, in particular to a bamboo wood diatom board. Background technique [0002] Bamboo board is a board and square lumber made of processed and processed exquisite bamboo pieces by gluing and pressing. The production of bamboo board usually requires the use of large-diameter bamboos of 4-6 years old. Dozens of processes such as high-temperature cooking, high-pressure carbonization, drying, fine planing, color separation and selection, assembly pressing, sanding, etc., have excellent physical properties, and have a small water-absorbing expansion coefficient, no cracking, and no deformation Other advantages, bamboo board, also known as bamboo board, phoebe bamboo board, moso bamboo board, bamboo furniture board, bamboo board, bamboo laminated lumber, the surface is similar to wood board, carbonized bamboo board, beautiful board surface, fresh bamboo texture, natural color , Bamboo fragrant, elegant textur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27J1/00B27K9/00B27N3/08B27D1/08
CPCB27J1/00B27D1/08B27K9/002B27N3/08
Inventor 张森
Owner 张森
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products