Composite wallboard and production process thereof

A composite wallboard and production process technology, which is applied in the field of wallboard to achieve the effects of convenient operation, high construction civilization and less construction waste

Inactive Publication Date: 2018-12-18
四川信衡新型材料科技有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the composite wallboard of this invention has the advantages of thermal insulation, energy saving and environmental protection, low cost and light weight, as a new type of wall material, the composite wallboard is widely used in interior walls, exterior walls, roof walls, enclosure walls, etc. In life, such phenomena are often seen, such as dew on the wall, fire in the house, and the air conditioner or heating must be turned on in the house in the cold season. It is necessary to study a multifunctional composite wall panel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite wallboard and production process thereof
  • Composite wallboard and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The production process of calcium silicate board 1 is as follows:

[0036] Weigh 13kg of fly ash, 14kg of diatomite, 10kg of carbide slag, 15kg of tailings sand, 24kg of glass fiber, 6kg of high-temperature fiber and 8kg of magnesium hydroxide, and weigh the weighed fly ash, diatomite, carbide slag, Mix tailings sand, glass fiber, high-temperature fiber and magnesium hydroxide evenly to obtain a mixture; mix the mixture with water at a weight ratio of 3:1 to obtain a slurry; put the slurry into a mold and shape it to obtain silicic acid Calcium board1.

[0037] A kind of production process of composite wallboard is as follows:

[0038] Step 1: Weigh 32kg of polystyrene particles, 43kg of cement, 10kg of waterproofing agent and 10kg of setting retarder, mix them evenly, and then mix them with water in a ratio of 2:1 by weight to obtain cement slurry;

[0039] Step 2: Weigh 5kg of foaming agent, and fully foam the foaming agent to obtain foam;

[0040] Step 3: Mix the ...

Embodiment 2

[0043] The production process of calcium silicate board 1 is as follows:

[0044] Weigh 15kg of fly ash, 20kg of diatomite, 12kg of carbide slag, 14kg of tailings sand, 23kg of glass fiber, 4kg of high-temperature fiber and 12kg of magnesium hydroxide, and weigh the weighed fly ash, diatomite, carbide slag, Mix tailings sand, glass fiber, high-temperature fiber and magnesium hydroxide evenly to obtain a mixture; mix the mixture with water at a weight ratio of 4:1 to obtain a slurry; put the slurry into a mold and shape it to obtain silicic acid Calcium board1.

[0045] A kind of production process of composite wallboard is as follows:

[0046] Step 1: Weigh 53kg of polystyrene particles, 27kg of cement, 6kg of waterproofing agent and 8kg of setting retarder, mix them evenly, and then mix them with water in a ratio of 3:1 by weight to obtain cement slurry;

[0047] Step 2: Weigh 6kg of foaming agent, and fully foam the foaming agent to obtain foam;

[0048] Step 3: Mix the c...

Embodiment 3

[0051] The production process of calcium silicate board 1 is as follows:

[0052] Weigh 17kg fly ash, 18kg diatomite, 13kg carbide slag, 13kg tailings sand, 21kg glass fiber, 4kg high temperature fiber and 14kg magnesium hydroxide, and weigh the weighed fly ash, diatomite, carbide slag, Mix tailings sand, glass fiber, high-temperature fiber and magnesium hydroxide evenly to obtain a mixture; mix the mixture with water at a weight ratio of 5:1 to obtain a slurry; put the slurry into a mold and shape it to obtain silicic acid Calcium board1.

[0053] A kind of production process of composite wallboard is as follows:

[0054] Step 1: Weigh 42.5kg of polystyrene particles, 30kg of cement, 9kg of waterproofing agent and 9.5kg of retarder, mix them evenly, and then mix them with water in a ratio of 2.5:1 by weight to obtain cement slurry;

[0055] Step 2: Weigh 9kg of foaming agent, and fully foam the foaming agent to obtain foam;

[0056] Step 3: Mix the cement slurry and foam e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a composite wallboard and a production process thereof, and relates to the field of wallboards, aiming at solving the problem that in the prior art, the composite wallboard isrelatively single in function; the composite wallboard comprises two face plates and polyphenyl granular concrete filled between the two face plates, wherein the faces plates comprise calcium silicateplates or fiber cement plates. The calcium silicate plates are prepared from the following components: 27-43wt% of a siliceous material, 20-30wt% of a calcium material, 18-32wt% of reinforcing fibersand 10-20wt% of an auxiliary agent; the polyphenyl granular concrete is prepared from the following components: 32-53wt% of polyphenyl granules, 27-43wt% of cement, 10-20wt% of a modifying additive and 5-10wt% of a foaming agent. The composite wallboard has the advantages of being high in strength, firm and reliable, not easy to damage and break, energy-saving and heat-insulated, light in weightand shock-resistant, soundproof and noise reducing as well as waterproof and damp-proof, being hung by using nails or stuck, being slotted for burying wires, being easy to install and decorate, and the like.

Description

technical field [0001] The invention relates to the field of wall panels, in particular to a composite wall panel and a production process thereof. Background technique [0002] Composite wallboard is a new generation of high-performance building interior partition produced in industrialized production. It is made of various building materials and replaces traditional bricks and tiles. , The obvious advantage of fast construction. [0003] The Chinese patent with authorized notification number CN102173674A discloses a lightweight concrete composite wallboard, which is composed of cement, sand, water, light aggregate, water reducer, admixture, and fly ash. The mass parts of each component They are: 80-120 parts, 20-100 parts, 30-80 parts, 3-10 parts, 1-3 parts, 0.05-0.1 parts, 15-30 parts. Although the composite wallboard of this invention has the advantages of thermal insulation, energy saving and environmental protection, low cost and light weight, as a new type of wall m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04C2/288C04B28/00C04B28/02B28B1/50
CPCB28B1/50C04B28/00C04B28/021C04B2111/28C04B2111/52C04B2201/20C04B2201/32C04B2201/50E04C2/288C04B14/08C04B18/0427C04B18/12C04B14/42C04B16/02C04B14/38C04B16/08C04B2103/65C04B2103/22
Inventor 陈礼勇
Owner 四川信衡新型材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com