A sn-ag-cu lead-free solder containing ga and nd

A lead-free solder, mass percentage technology, used in welding/cutting media/materials, metal processing equipment, welding equipment, etc., can solve problems such as the impact of brazing joints on electronic products, improve reliability and improve shear strength , the effect of improving the wetting performance

Active Publication Date: 2020-11-13
NANJING UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the "Sn-Ag-Cu lead-free solder containing Nd and Ga" reduces the Ag content to the range of 0.01-0.5%, the content of the rare element Ga is still high at 0.003-1.5%, and when the rare earth element Nd When the upper limit of 0.001 to 0.5% is reached to 0.5%, the brazing joint is likely to produce a hidden danger that has a huge impact on electronic products - tin whiskers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A sn-ag-cu lead-free solder containing ga and nd
  • A sn-ag-cu lead-free solder containing ga and nd
  • A sn-ag-cu lead-free solder containing ga and nd

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Sn-Ag-Cu lead-free solder containing Ga and Nd, including: 0.1% Ag, 1.0% Cu, 0.125% Ga, 0.025% Nd, 0.006% Zr, 0.003% Te by mass percentage , the balance being Sn.

[0030] The liquidus temperature of the "Sn-Ag-Cu lead-free solder containing Ga and Nd" obtained by the above composition ratio is about 218°C (considering the experimental error), and the commercially available water-soluble flux (FLUX 3355-11 water-soluble Organic acid flux) has excellent wetting performance on T2 copper plate, and the mechanical properties of brazing seam can reach 85MPa±5MPa (shear strength). After aging for 6 months at 150°C, the intermetallic compound at the interface of the newly invented lead-free solder has no obvious change and no tin whiskers have sprouted, indicating that the reliability of the solder joint (solder joint) has been significantly improved.

Embodiment 2

[0032] Sn-Ag-Cu lead-free solder containing Ga and Nd, including: 0.35% Ag, 0.1% Cu, 0.5% Ga, 0.1% Nd, 0.002% Zr, 0.001% Te by mass percentage , the balance being Sn.

[0033] The liquidus temperature of "a kind of Sn-Ag-Cu lead-free solder containing Ga and Nd" obtained by the above composition ratio is about 218°C (experimental error is considered), and the commercially available water-soluble flux (FLUX 3355- 11 Water-soluble organic acid flux) It has excellent wetting performance on T2 copper plate, and the mechanical properties of brazing joint can reach 85MPa±5MPa (shear strength). After aging for 6 months at 150°C, the intermetallic compound at the interface of the newly invented lead-free solder has no obvious change and no tin whiskers have sprouted, indicating that the reliability of the solder joint (solder joint) has been significantly improved.

Embodiment 3

[0035] Sn-Ag-Cu lead-free solder containing Ga and Nd, including: 0.3% Ag, 0.7% Cu, 0.4% Ga, 0.08% Nd, 0.004% Zr, 0.002% Te by mass percentage , the balance being Sn.

[0036] The liquidus temperature of the "Sn-Ag-Cu lead-free solder containing Ga and Nd" obtained by the above composition ratio is about 218°C (considering the experimental error), and the commercially available water-soluble flux (FLUX 3355-11 water-soluble Non-toxic organic acid flux) has excellent wetting performance on T2 copper plate, and the mechanical properties of brazing seam can reach 85MPa±5MPa (shear strength). After aging for 6 months at 150°C, the intermetallic compound at the interface of the newly invented lead-free solder has no obvious change and no tin whiskers have sprouted, indicating that the reliability of the solder joint (solder joint) has been significantly improved.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Sn-Ag-Cu lead-free solder containing Ga and Nd, and belongs to metal materials and soldering materials in the field of metallurgy. The Sn-Ag-Cu lead-free solder comprises, bymass, 0.1-0.35 % of Ag, 0.1-1.0 % of Cu, 0.125-0.5% of Ga, 0.025-0.1% of Nd, 0.002-0.006% of Zr, 0.001-0.003% of Te, and the balance Sn, wherein the mass ratio of Ga to Nd is 5:1, and the mass ratioof Zr to Te is 2:1. The solder has good wetting performance, growth of tin whiskers of a soldering joint can be effectively inhibited, the reliability of the soldering joint is greatly improved, and the Sn-Ag-Cu lead-free solder can be used for reflow soldering of components in the electronic industry and can also be used for wave soldering.

Description

technical field [0001] The invention relates to a Sn-Ag-Cu lead-free solder containing Ga and Nd, belonging to metal materials and brazing materials in the field of metallurgy. Background technique [0002] At present, representative lead-free solders include Sn-Ag-Cu, Sn-Cu, Sn-Cu-Ni and other alloy systems, each with its own strengths, but compared with tin-lead solders, the cost of solder and solder There is still a certain gap in terms of melting point and so on. Sn-Zn solder melting point and raw material cost are lower than Sn-Ag-Cu, Sn-Cu, Sn-Cu-Ni solder, especially Sn-Zn solder melting point is very close to tin-lead solder, but due to Sn The wettability of -Zn solder is poor, so it is difficult to be applied to industrial production at present. [0003] In recent years, "Sn-Ag-Cu lead-free solder containing Pr, Zr, Co" (Chinese patent application, CN101579789A), "Containing Nd, Li, As, In" have been developed on the basis of Sn-Ag-Cu at home and abroad. "Sn-Ag-C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/26
CPCB23K35/262
Inventor 薛鹏梁伟良王克鸿裴夤崟孙华为
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com