Wear-resistant and anti-ageing automotive rubber damping piece material

A kind of rubber shock absorption and anti-aging technology, which is applied in the field of automobile processing to achieve the effect of improving interface affinity, good compatibility and strong heat resistance

Inactive Publication Date: 2018-12-25
ANHUI WEIWEI RUBBER PARTS GRP
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The metal and rubber shock-absorbing bushing has certain performance requirements for rubber, and there is still a lot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A wear-resistant and anti-aging automotive rubber shock absorber material, comprising the following raw materials in parts by weight:

[0027] 20 parts of natural rubber, 20 parts of butyl rubber, 10 parts of butadiene rubber, 20 parts of wear-resistant polyvinyl chloride masterbatch, 4 parts of talcum powder, 2 parts of toughening agent, 2 parts of antioxidant, 1 part of anti-aging agent, 1 part of joint agent, 3 parts of mineral oil, 3 parts of maleic anhydride compatibilizer, 3 parts of paraffin, 5 parts of nano-barium sulfate, 2 parts of modified nano-silicon nitride, 1 part of potassium stearate, 2 parts of accelerator , 2 parts of crosslinking agent, 1 part of zinc borate, 3 parts of sulfur;

[0028] The wear-resistant polyvinyl chloride masterbatch comprises the following components in proportion by weight: 50 parts of polyvinyl chloride masterbatch, 5 parts of glass fiber, 2 parts of long carbon fiber, 3 parts of graphene, 1 part of low molecular weight chitosan...

Embodiment 2

[0034] A wear-resistant and anti-aging automotive rubber shock absorber material, comprising the following raw materials in parts by weight:

[0035] 30 parts of natural rubber, 25 parts of butyl rubber, 15 parts of butadiene rubber, 25 parts of wear-resistant polyvinyl chloride masterbatch, 7 parts of talcum powder, 5 parts of toughening agent, 4 parts of antioxidant, 4 parts of anti-aging agent, 3 parts of joint agent, 9 parts of mineral oil, 6 parts of maleic anhydride compatibilizer, 7 parts of paraffin, 8 parts of nano-barium sulfate, 5 parts of modified nano-silicon nitride, 3 parts of potassium stearate, 5 parts of accelerator , 4 parts of crosslinking agent, 2 parts of zinc borate, 7 parts of sulfur;

[0036] The wear-resistant polyvinyl chloride masterbatch comprises the following components in proportion by weight: 50 parts of polyvinyl chloride masterbatch, 9 parts of glass fiber, 5 parts of long carbon fiber, 5 parts of graphene, 5 parts of low molecular weight chi...

Embodiment 3

[0042] A wear-resistant and anti-aging automotive rubber shock absorber material, comprising the following raw materials in parts by weight:

[0043] 25 parts of natural rubber, 23 parts of butyl rubber, 12 parts of butadiene rubber, 23 parts of wear-resistant polyvinyl chloride masterbatch, 5 parts of talcum powder, 4 parts of toughening agent, 3 parts of antioxidant, 3 parts of anti-aging agent, 2 parts of joint agent, 6 parts of mineral oil, 4 parts of maleic anhydride compatibilizer, 5 parts of paraffin, 7 parts of nano-barium sulfate, 4 parts of modified nano-silicon nitride, 2 parts of potassium stearate, 4 parts of accelerator , 3 parts of crosslinking agent, 1.5 parts of zinc borate, 5 parts of sulfur.

[0044]The wear-resistant polyvinyl chloride masterbatch comprises the following components in proportion by weight: 50 parts of polyvinyl chloride masterbatch, 7 parts of glass fiber, 3.5 parts of long carbon fiber, 4 parts of graphene, 3 parts of low molecular weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear-resistant and anti-ageing automotive rubber damping piece material. The wear-resistant and anti-ageing automotive rubber damping piece material comprises the following raw materials in parts by weight: 20-30 parts of natural rubber, 20-25 parts of butyl rubber, 10-15 parts of butadiene rubber, 20-25 parts of wear-resistant polyvinyl chloride masterbatches, 4-7 partsof talcum powder, 2-5 parts of a toughener, 2-4 parts of an antioxidant, 1-4 parts of an anti-ageing agent, 1-3 parts of a coupling agent, 3-9 parts of mineral oil, 3-6 parts of a maleic anhydride compatilizer, 3-7 parts of paraffin, 5-8 parts of nano barium sulfate, 2-5 parts of modified nano silicon nitride, 1-3 parts of potassium stearate, 2-5 parts of a promotor, 2-4 parts of a crosslinking agent, 1-2 parts of zinc borate and 3-7 parts of sulphur. The wear-resistant and anti-ageing automotive rubber damping piece material is reasonable in formula, the compatibility of various components isgood, and the prepared damping material has the advantages of high damping coefficient, high resilience force, damping ability, high temperature resistance, ageing resistance, creep resistance, wearresistance, good flame retardant and the like, and is suitable for automotive damping products.

Description

technical field [0001] The invention relates to the field of automobile processing, in particular to a wear-resistant and anti-aging automobile rubber shock absorber material. Background technique [0002] With the rapid development of modern industry, vibration and noise have become serious problems in various fields. It will reduce the operating accuracy, affect product quality, shorten product life, make high-precision instruments not work normally, and endanger safety. [0003] In the processing and manufacturing of automobiles, the shock absorber is one of the essential parts. It is mainly used to suppress the shock when the spring rebounds after absorbing the shock and the impact from the road surface, which plays a role in the comfort and handling stability of the vehicle. important role. The principle of the existing shock absorber bushing is to convert the mechanical energy of vibration into thermal energy through the elastic support and dissipate it to the surroun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L23/22C08L9/00C08L27/06C08L5/08C08K13/06C08K9/06C08K3/34C08K7/14C08K7/06C08K3/30C08J3/22
CPCC08L7/00C08J3/226C08J2307/00C08J2323/22C08J2427/06C08K2003/3045C08K2201/011C08L23/22C08L2201/02C08L2201/08C08L2205/035C08L9/00C08L27/06C08L5/08C08K13/06C08K9/06C08K3/34C08K7/14C08K7/06C08K3/30
Inventor 李俊毛旺龙张文强李斌商赵旭袁良鹏
Owner ANHUI WEIWEI RUBBER PARTS GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap