A technology of elastic latex paint and high adhesion, applied in the field of coatings, can solve the problems of insufficient adhesion of latex paint, affecting the strength of adhesion, and bulging of the film layer, so as to enhance anti-spot and stain resistance, improve elastic performance, and avoid Shedding effect

Inactive Publication Date: 2018-12-25
HEFEI FENGTENG ENERGY SAVING TECH CO LTD
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adhesion of the latex paint of this technical solution is still insufficient, and the high and lo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly-adhesive elastic emulsion paint
  • Highly-adhesive elastic emulsion paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A high-adhesion elastic latex paint. According to the mass parts, the components of the latex paint include: 85 parts of pure acrylic emulsion, 15 parts of styrene-acrylic emulsion, 70 parts of inorganic filler, 5 parts of composite tackifier, polytetrafluoroethylene - 4 parts of polyurethane copolymer, 1 part of polyacrylamide, 1 part of nano-titanium dioxide, 0.2 part of preservative, 0.2 part of defoamer, 0.1 part of leveling agent, 20 parts of deionized water.

[0035] Wherein, the inorganic filler is a mixture of titanium dioxide, talc and light calcium carbonate in a mass ratio of 5:3:1.

[0036] The preservative is selected from 1,2-benzisothiazol-3-one.

[0037] The defoamer is a silicone defoamer; the leveling agent is a silicone polyether acrylate copolymer.

[0038] The preparation method of the latex paint provided in this example is: according to the mass parts, the tackifier and polytetrafluoroethylene-polyurethane copolymer are added to the mixture of pu...

Embodiment 2

[0040] A high-adhesion elastic latex paint. According to the mass parts, the components of the latex paint include: 100 parts of pure acrylic emulsion, 20 parts of styrene-acrylic emulsion, 80 parts of inorganic filler, 8 parts of composite tackifier, polytetrafluoroethylene - 7 parts of polyurethane copolymer, 2.5 parts of polyacrylamide, 1.6 parts of nano titanium dioxide, 0.7 parts of preservative, 0.4 parts of defoamer, 0.3 parts of leveling agent, 25 parts of deionized water.

[0041] Wherein, the inorganic filler is a mixture of titanium dioxide, talc and light calcium carbonate in a mass ratio of 5:3:1.

[0042] The preservative is selected from methylisothiazolinone.

[0043] The defoamer is a silicone defoamer; the leveling agent is a polysiloxane-polyether copolymer.

[0044] The preparation method of the latex paint provided in this example is: according to the mass parts, the tackifier and the polytetrafluoroethylene-polyurethane copolymer are added to the mixture...

Embodiment 3

[0046] A high-adhesion elastic latex paint. According to the mass parts, the components of the latex paint include: 94 parts of pure acrylic emulsion, 17 parts of styrene-acrylic emulsion, 76 parts of inorganic filler, 7 parts of composite tackifier, polytetrafluoroethylene - 5.5 parts of polyurethane copolymer, 2.1 parts of polyacrylamide, 1.4 parts of nano titanium dioxide, 0.5 parts of preservative, 0.3 parts of defoamer, 0.2 parts of leveling agent, 23 parts of deionized water.

[0047] Wherein, the inorganic filler is a mixture of titanium dioxide, talc and light calcium carbonate in a mass ratio of 5:3:1.

[0048] The preservative is 5-chloro-2-methyl-4-isothiazolin-3-one.

[0049] The defoamer is a silicone defoamer; the leveling agent is a silicone polyether acrylate copolymer.

[0050] The preparation method of the latex paint provided in this example is: according to the mass parts, the tackifier and the polytetrafluoroethylene-polyurethane copolymer are added to th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of painting, particularly to a highly-adhesive elastic emulsion paint. The highly-adhesive elastic emulsion paint is composed of pure acrylic emulsion, styrene-acrylic emulsion, inorganic filler, compound thickening agent, polytetrafluoroethylene-polyurethane copolymer, polyacrylamide, nanometer titanium dioxide, preservative, defoamer, leveling agent and deionized water, wherein the compound thickening agent is a special combination prepared by compounding materials such as mucopolysaccharides, modified cellulose and modified starch; the organic filler is a mixture of titanium dioxide, talcum powder and light calcium carbonate; the preservative is 1, 2-benzisothiazolin-3-one, methylisothiazolinone or 5-chloro-2-methyl-4-isothiazolinone-3-one. The highly-adhesive elastic emulsion paint is high in adhesiveness and easy to dry and cure and can form coating high in elasticity, strength and washing resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an elastic latex paint with high adhesion. Background technique [0002] Emulsion paint (Emulsion Paint.), also known as synthetic resin emulsion paint, is a kind of organic paint. It is a kind of water-based paint formulated with synthetic resin emulsion as the base material and added with pigments, fillers and various additives. According to different production raw materials, latex paint mainly includes polyvinyl acetate latex paint, ethylene-propylene latex paint, pure acrylic latex paint, styrene-acrylic latex paint and other varieties. According to the different application environment of the product, it is divided into two types: interior wall latex paint and exterior wall latex paint. According to the gloss effect of the decoration, it can be divided into dull, matte, semi-gloss, mercerized and glossy. Latex paint has many advantages that are different from traditional...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D125/14C09D5/02C09D5/16C09D5/08C09D7/61C09D7/63C09D7/65C09D7/44
CPCC09D133/04C08K2003/2241C08K2003/265C08K2201/011C08L2205/035C09D5/024C09D5/08C09D5/14C09D5/1687C09D7/44C08L25/14C08L87/00C08L33/26C08L5/00C08L3/02C08L1/02C08K13/02C08K3/22C08K3/34C08K3/26
Inventor 吴旭
Owner HEFEI FENGTENG ENERGY SAVING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap