Heating ceramic slurry and preparation method thereof

A ceramic material and main function technology, applied in the direction of heating element materials, metal processing equipment, food science, etc., can solve the problems of e-cigarette liquid coking, heating delay, affecting taste, etc., to achieve temperature control, low temperature coefficient of resistance, Rapid response to temperature rise

Inactive Publication Date: 2018-12-28
HUBEI CHINA TOBACCO IND
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because of the rapid heating rate of the heating wire and low heating delay, there will be no atomization delay during the entire 1-3 second pumping process, but at the same time, the temperature is not easy to control, and it is easy to coke the e-cigarette liquid. It affects the taste, and secondly, long-term use will cause the metal components of the heating wire to migrate, enter the smoke and be sucked, affecting health
As an environmentally friendly heating ceramic material that replaces the heating wire, in the known electronic cigarette technology field, most of the heating ceramics provided have a high temperature coefficient of resistance, so there is a serious heating delay phenomenon, which often leads to 1- During the 3-second puff, especially the first puff, no smoke is produced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A heat-generating ceramic slurry, comprising a composite functional phase, an inorganic additive and an organic carrier, the weight ratio of which is as follows: 70 parts of a composite functional phase, 20 parts of an inorganic additive, and 10 parts of an organic carrier, characterized in that the composite functional phase includes a main functional phase and the TCR adjustment phase, the main functional phase is composed of tungsten powder, manganese powder, and zinc powder in a ratio of 10:1:1, the particle size of the main functional phase is controlled at 0.5 μm, and the added amount of the TCR adjustment phase accounts for the majority 0.3% of the weight of the functional phase, the TCR adjustment phase is composed of mixed powder of palladium powder and cerium powder according to the weight ratio of 75:5, and the inorganic additive is composed of Al 2 o 3 , MgCO 3 , SiO 2 , glass powder, and its weight ratio is 60:2:17:13, and the organic carrier is composed ...

Embodiment 2

[0028] A heat-generating ceramic slurry, including a composite functional phase, an inorganic additive, and an organic carrier, the weight ratio of which is as follows: 75 parts of a composite functional phase, 16 parts of an inorganic additive, and 9 parts of an organic carrier, and is characterized in that the composite functional phase includes a main functional phase and the TCR adjustment phase, the main functional phase is composed of tungsten powder, manganese powder, and chromium powder in a ratio of 8:1:2, the particle size of the main functional phase is controlled at 1 μm, and the added amount of the TCR adjustment phase accounts for the main function 0.5% of the phase weight, the TCR adjustment phase is composed of ruthenium powder, and the inorganic additive is composed of Al 2 o 3 , MgCO 3 , SiO 2 , glass powder, and its weight ratio is 55:3:10:20, and the organic carrier is composed of turpentyl alcohol, cyclohexanone, soybean lecithin, hydrogenated castor oil...

Embodiment 3

[0034] A heat-generating ceramic slurry, including a composite functional phase, an inorganic additive, and an organic carrier, the weight ratio of which is as follows: 75 parts of a composite functional phase, 16 parts of an inorganic additive, and 9 parts of an organic carrier, and is characterized in that the composite functional phase includes a main functional phase and the TCR adjustment phase, the main functional phase is composed of tungsten powder, manganese powder, titanium powder, and zinc powder in a ratio of 8:1:2:0.5, the particle size of the main functional phase is controlled at 1 μm, and the TCR adjustment phase The amount added accounts for 0.4% of the weight of the main functional phase, the TCR adjustment phase is composed of platinum powder, ruthenium powder, and palladium powder in a ratio of 75:15:10, and the inorganic additive is composed of Al 2 o 3 , MgCO 3 , SiO 2 , glass powder, and its weight ratio is 45:0.5:6:7, and the organic carrier is compos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Temperature coefficient of resistanceaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides heating ceramic slurry, comprising a composite functional phase, an inorganic additive and an organic support. The composite functional phase includes a main functional phase and a TCR (temperature coefficient of resistance) adjusting phase. The main functional phase includes, but not limited to, one of or mixture of any of tungsten powder, molybdenum powder, manganese powder, silver powder, copper powder, nickel power, cobalt powder, titanium powder, chromium powder, and zinc powder; the TCR adjusting phase includes, but not limited to, one of or mixture of any of platinum powder, ruthenium powder, palladium powder, rhodium powder, osmium powder, iridium powder, germanium powder, and lanthanum powder or their oxides; the TCR adjusting phase accounts for 0.1-10% by weight of the main functional phase so that TCR of the heating ceramic slurry is kept to 1500 ppm / DEG C to 4000 ppm / DEG C. The heating ceramic slurry has low temperature coefficient of resistance and has delayed heating.

Description

technical field [0001] The invention relates to the technical field of novel tobacco products, in particular to a heating ceramic slurry and a preparation method thereof. Background technique [0002] Existing electronic cigarette atomizers atomize electronic cigarette liquid by winding glass fiber cotton with a heating wire, thereby generating smoke for consumers to inhale. Because of the rapid heating rate of the heating wire and low heating delay, there will be no atomization delay during the entire 1-3 second pumping process, but at the same time, the temperature is not easy to control, and it is easy to coke the e-cigarette liquid. It affects the taste, and secondly, long-term use will cause the metal components of the heating wire to migrate, enter the smoke and be inhaled, affecting health. As an environmentally friendly heating ceramic material that replaces the heating wire, in the known electronic cigarette technology field, most of the heating ceramics provided h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A24F47/00H05B3/12B22F1/00
CPCA24F47/008H05B3/12B22F1/107
Inventor 刘冰刘磊陈义坤刘华臣罗诚浩
Owner HUBEI CHINA TOBACCO IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.