Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Low smell corrosion-resistant HIPS composite material for refrigerator and preparation method thereof

A composite material, HIPS100 technology, applied in the field of low-odor and anti-corrosion HIPS composite materials for refrigerators and its preparation field, can solve the problems such as easy to escape again, and achieve easy processing and preparation, simple compounding process and processing process, and environmental friendliness Effect

Inactive Publication Date: 2019-01-11
ANHUI LIANKE WATER BASED MATERIAL TECH
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] CN107501834A and CN106751339A prepare low-odor HIPS materials by adding a kind of one-dimensional or multi-dimensional porous zeolite powder, but VOC still exists in this method, and the adsorption of small molecules is selective and balanced, and it is easy to escape again at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The preparation method in embodiment one and comparative example one, comprises the following steps:

[0045] (1) Weigh and take various raw materials according to weight percentage;

[0046] (2) Mix HIPS, polyethylene resin, toughening compatibilizer, raw gypsum powder, antioxidant, reactive castor oil, lubricant, etc. in a high-speed mixer for 3-5 minutes;

[0047] (3) Place the above-mentioned mixed materials in the main feeding port of a twin-screw extruder with a length-to-diameter ratio of 36:1, melt and extrude to granulate, and the extruded materials are cooled, air-dried, pelletized, and dried. Corrosion of HIPS composites with low-odor anti-foaming agents for refrigerators.

[0048] The temperature setting range of the twin-screw extruder is 65-185°C, the screw speed is 200-500rpm, the vacuum at the end of the extruder is -0.08-0.09MPa, and the temperature of each zone of the twin-screw extruder is:

[0049] Zone 1 temperature: 65°C, Zone 2 temperature: 70°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
impact strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low smell corrosion-resistant HIPS composite material for a refrigerator and a preparation method thereof. The composite material is prepared from the following components inparts by weight: 100 parts of HIPS, 10-40 parts of polyethylene resin, 5-15 parts of a toughening compatilizer, 10-20 parts of gypsum powder, 0.1-0.5 part of a main antioxidant, 0.1-0.5 part of an auxiliary antioxidant, 0.1-0.5 part of a lubricant and 1-5 parts of reactive castor oil. The preparation method comprises the following steps: vaporizing water in the raw material gypsum powder in a fusing processing process; vacuumizing small molecular substances capable of generating smell in the HIPS and polyethylene to take away the materials; and combining smell substances in an active functional group chelating material of the reactive castor oil to form a stable novel compound so as to prepare the low smell foaming agent corrosion-resistant HIPS high performance composite material, so that the content of VOCs is reduced effectively, and the demand of the composite material of the refrigerator on low smell is met.

Description

technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a low-odor and anti-corrosion HIPS composite material for refrigerators and a preparation method thereof. Background technique [0002] Refrigerators are one of the most frequently used home appliances in our daily life. The existing refrigerator door end cover materials are mainly ABS materials, but ABS materials are only suitable for cyclopentane foaming systems. In the multi-component foaming system, the ABS end cover Cracking occurs in batches. The patent CN105504638A solves this problem well through the formula design of the alloy, but the common preparation method usually has some odor due to the small molecules such as residual monomers. As people's requirements for home appliance materials are getting higher and higher, the requirements for indoor air quality are also increasing. At present, most of the plastic materials of household appliances contain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/04C08L23/06C08L53/02C08L71/02C08L91/00C08K13/02C08K3/30C08K5/098C08J9/04
CPCC08J9/0023C08J9/0061C08J9/0066C08J9/0095C08J9/04C08J2351/04C08J2423/06C08J2453/02C08J2471/02C08J2491/00
Inventor 刘伯林
Owner ANHUI LIANKE WATER BASED MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com