Flower-shaped multistage structure molybdenum trioxide material induce by nickel-titanium alloy and preparation method and application thereof

A technology of nickel-titanium alloy and molybdenum trioxide, which is applied in the direction of structural parts, electrochemical generators, electrical components, etc., can solve the problem of poor cycle performance and magnification of negative electrode materials, and cannot meet the requirements of the structural integrity of negative electrode materials with volume changes. Unfavorable application and production problems, to achieve the effect of easy operation, improved cycle stability, and enhanced conductivity

Active Publication Date: 2019-01-18
SOUTH CHINA UNIV OF TECH
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method usually needs to remove the template after the reaction, and the added surfactants are all polymer insulating materials, which need to be further compounded with conductive materials, which is not conducive to practical application and production
[0007] In summary, neither of the above approaches alone is a good solution to MoO 3 The problem of poor cycle performance and rate performance of negative electrode materials
The reason is that using the above method alone can only improve its performance to a certain extent, and cannot meet the huge volume change and the structural integrity of the electrode during the long-term cycle of the negative electrode material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flower-shaped multistage structure molybdenum trioxide material induce by nickel-titanium alloy and preparation method and application thereof
  • Flower-shaped multistage structure molybdenum trioxide material induce by nickel-titanium alloy and preparation method and application thereof
  • Flower-shaped multistage structure molybdenum trioxide material induce by nickel-titanium alloy and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] (1) Analytical pure (NH 4 ) 6 Mo 7 o 24 4H 2 O (1.52g) was dissolved in deionized water (50mL), and stirred magnetically at 200 rpm for 15 minutes to obtain solution A;

[0043] (2) Under magnetic stirring, 9.1 mL of HNO with a solubility of 65% was added dropwise to solution A obtained in step (1). 3 , to obtain solution B;

[0044] (3) under magnetic stirring, add 0.228g, 60nm spherical NiTi alloy (the mass percent of Ni in the alloy composition is 55%) powder to the solution B obtained in step (2), to obtain solution C;

[0045] (4) The solution C obtained in step (3) was transferred to a tetrafluoroethylene-lined autoclave, and reacted at 180° C. for 24 hours.

[0046] (5) After the reaction is completed and cooled to room temperature, the reaction product obtained in step (4) is collected by centrifugation, washed with water and ethanol three times respectively, and then the reaction product is vacuum-dried at 60°C for 24 hours under a vacuum of 1000 Pa to ob...

Embodiment 2

[0050] (1) Analytical pure (NH 4 ) 6 Mo 7 o 24 4H 2 O (1.52g) was dissolved in deionized water (50mL), and magnetically stirred at 400 rpm for 12 minutes to obtain solution A;

[0051] (2) Under magnetic stirring, 9.1 mL of HNO with a solubility of 50% was added dropwise to the solution A obtained in step (1). 3 , to obtain solution B;

[0052] (3) under magnetic stirring, add 0.456g, 100nm near-spherical NiTi alloy (the mass percentage of Ni in the alloy composition is 56%) powder to the solution B obtained in step (2), to obtain solution C;

[0053] (4) The solution C obtained in step (3) was transferred to a tetrafluoroethylene-lined autoclave, and reacted at 210° C. for 3 hours.

[0054] (5) After the reaction is completed and cooled to room temperature, the reaction product obtained in step (4) is collected by centrifugation, washed 5 times with water and ethanol respectively, and then the reaction product is vacuum-dried at 80°C for 12 hours under a vacuum of 4000P...

Embodiment 3

[0058] (1) Analytical pure (NH 4 ) 6 Mo 7 o 24 4H 2 O (1.52g) was dissolved in deionized water (50mL), and magnetically stirred at 100 rpm for 18 minutes to obtain solution A;

[0059] (2) Under magnetic stirring, 9.1 mL of HNO with a solubility of 30% was added dropwise to the solution A obtained in step (1). 3 , to obtain solution B;

[0060] (3) under magnetic stirring, add 0.2g, 120nm spherical NiTi alloy (the mass percentage of Ni in the alloy composition is 54%) powder to the solution B obtained in step (2), to obtain solution C;

[0061](4) The solution C obtained in step (3) was transferred to a tetrafluoroethylene-lined autoclave, and reacted at 150° C. for 16 hours.

[0062] (5) After the reaction is completed and cooled to room temperature, the reaction product obtained in step (4) is collected by centrifugation, washed with water and ethanol for 4 times, and then the reaction product is vacuum-dried at 70°C for 18 hours under a vacuum of 2000Pa to obtain a fl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flower-shaped multistage structure molybdenum trioxide material induced by a nickel-titanium alloy and a preparation method and application thereof. At first, (NH4) 6Mo7O24.4H2O aqueous solution and HNO3 are uniformly mix; Then adding 60-120 nm spherical or near-spherical nickel-titanium alloy powder into the aqueous solution, uniformly mixing, transferring the solutionto a tetrafluoroethylene-lined high-pressure reaction kettle, and reacting at 150-210 DEG C for 3-24 hours; At that end of the reaction, aft cooling to room temperature, the reaction product is collect by centrifugation, washed with water and ethanol for several times respectively, and then the product is vacuum dry to obtain flower-like multi-stage structure molybdenum trioxide material. The preparation method of the invention has strong controllability and simple operation, can be used for large-scale production of lithium ion secondary battery electrode material, and can remarkably improvethe cycle and rate performance of the electrode material.

Description

technical field [0001] The invention relates to a molybdenum trioxide (MoO 3 ) material, preparation method and application, belonging to the field of nano functional material and lithium ion secondary battery. Background technique [0002] Lithium ion batteries (Lithium ion batteries, LIBs) are composed of negative electrode (also known as anode) and positive electrode (cathode) materials, and a rechargeable energy storage is realized through the reciprocating intercalation and extraction movement of Li ions between the positive and negative electrodes. storage device. During discharge, Li ions (Li + ) transport current from the anode to the cathode through the nonaqueous electrolyte and separator; during charging, the process goes in the opposite direction. [0003] LIBs have the advantages of high energy density (high specific capacity), light weight, long life, and no memory effect. The specific capacity of lithium-ion batteries is mainly determined by the positive a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/48H01M4/62H01M10/0525
CPCH01M4/362H01M4/483H01M4/62H01M4/626H01M4/628H01M10/0525Y02E60/10
Inventor 袁斌闫钰胡仁宗杨黎春刘军朱敏
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com